Y、Gd、La和Ce对Zr(-Ti)-Cu-Ni-Al非晶形成能力和力学性能的影响
Effect of Y, Gd, La and Ce on the Glass Forming Ability and Mechanical Properties of Zr(-Ti)-Cu-Ni-Al Metallic Glasses

查看参考文献23篇

李正坤 1,2   秦鑫冬 1   刘丁铭 1   陆宏煜 1   张海峰 1 *   李扬德 2   李卫荣 2  
文摘 为了控制Zr(-Ti)-Cu-Ni-Al非晶合金中的O含量,进而改善其玻璃形成能力和力学性能,本研究基于稀土元素与O的强相互作用,向合金中添加Y、Gd、La和Ce等元素。使用铜模浇铸制备非晶合金,利用DSC、XRD和TEM对其非晶形成能力和微观结构进行分析,通过压缩试验和SEM对其力学性能及断裂方式进行表征。结果表明:Y的添加对合金的非晶形成能力具有较大的提升,在相对较低真空的气氛下,可制备出直径10 mm以上的块体非晶,抗压缩断裂强度达1950 MPa。
其他语种文摘 Y, Gd, La and Ce were added into Zr(-Ti)-Cu-Ni-Al metallic glasses based on the mechanism of strong interaction between O and rare earth elements in order to control the O content and further to improve the glass forming ability and mechanical properties of the alloys. Metallic glasses were prepared by a copper mold casting method. The glass forming ability and microstructure of the alloys were studied by differential scanning calorimetry (DSC), X-ray Diffraction (XRD) and transmission electron microscopy (TEM), and the mechanical properties and corresponding fracture modes were investigated by quasi-static compressive tests and scanning electron microscope (SEM). The results show that the addition of Y improves the glass forming ability greatly. Bulk metallic glasses with the diameter over 10 mm can be prepared under relatively low vacuum. The compressive strength is up to 1950 MPa.
来源 稀有金属材料与工程 ,2018,47(9):2755-2760 【核心库】
关键词 非晶 ; 玻璃形成能力 ; 力学性能 ; Y
地址

1. 中国科学院金属研究所, 沈阳材料科学国家(联合)实验室, 辽宁, 沈阳, 110016  

2. 东莞宜安科技股份有限公司, 广东, 东莞, 523662

语种 中文
文献类型 研究性论文
ISSN 1002-185X
学科 金属学与金属工艺
基金 国家自然科学基金 ;  广东省省级科技计划项目 ;  中国载人空间站工程 ;  江苏省创新人才计划项目
文献收藏号 CSCD:6337276

参考文献 共 23 共2页

1.  Qiao J W. Materials Science & Engineering R-Reports,2016,100:1 被引 35    
2.  Schroers J. Physics Today,2013,66(2):32 被引 19    
3.  Johnson W L. US Patent, US5288344-A,1994 被引 1    
4.  Peker A. Applied Physics Letters,1993,63(17):2342 被引 284    
5.  Inoue A. Materials Transactions Jim,1996,37(2):185 被引 60    
6.  Yokoyama Y. Materials Transactions,2007,48(12):3190 被引 6    
7.  Wang W H. Progress in Materials Science,2007,52(4):540 被引 102    
8.  Kui H W. Applied Physics Letters,1984,45(6):615 被引 40    
9.  Qiao D C. Intermetallics,2012,24:115 被引 1    
10.  Jiang F. Scripta Materialia,2005,53(5):487 被引 5    
11.  Ma D. Applied Physics Letters,2005,87(17):171914 被引 9    
12.  Zhao D Q. Materials Transactions Jim,2000,41(11):1427 被引 4    
13.  Heinrich J. Applied Physics Letters,2012,100(7):071909 被引 1    
14.  Luo J. Materials Transactions,2006,47(2):450 被引 8    
15.  Yan M. Journal of Non-Crystalline Solids,2006,352(28/29):3109 被引 7    
16.  Yan M. Acta Materialia,2006,54(13):3627 被引 7    
17.  Zhang Y. Materials Transactions Jim,2000,41(11):1410 被引 15    
18.  Hao G J. Role of yttrium in glass formation of Ti-based bulk metallic glasses. Rare Metals,2009,28(1):68 被引 4    
19.  Zhao X. Philosophical Magazine Letters,2009,89(1):11 被引 1    
20.  Xu D H. Physical Review Letters,2004,92(24):245504 被引 33    
引证文献 3

1 赵燕春 稀土元素添加对铁基非晶复合材料腐蚀行为的影响 稀有金属材料与工程,2021,50(7):2592-2598
被引 1

2 李朝岚 Gd掺杂强化(Cu_(56)Zr_(44))_(1–x)Gd_x合金非晶形成能力及摩擦学性能 表面技术,2021,50(9):254-260
被引 0 次

显示所有3篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号