抗静电耐腐蚀涂层的制备及性能研究
Preparation and Properties of Antistatic and Anitcorrosion Coatings
查看参考文献26篇
|
文摘
|
用导电云母替代富锌涂料中的部分锌粉,制备了含不同含量导电云母的抗静电耐腐蚀涂料,涂料经固化形成抗静电耐腐蚀涂层,测试了涂层的力学性能和抗静电性,采用盐雾、浸泡以及电化学等测试方法对涂层耐腐蚀性能进行了评价,并对涂层进行了防腐蚀机理的分析。结果表明:盐雾实验对涂层的抗静电性能影响不大。导电云母添加量为3%时,涂层阴极保护作用提高,并具有最佳的防静电性和防腐蚀性。 |
|
其他语种文摘
|
By replacing partially, the quantity of zinc powder in zinc-rich coatings with conductive mica, zinc-rich coatings with different amount of conductive mica were prepared, then of which the antistatic-, mechanical-and anticorrosion-properties were assessed by means of measurements of surface-and volume-resistivity, pencil-hardness, impact resistance and adhesion etc. as well as immersion test, salt spray test and electrochemical impedance spectroscopy. Results show that the antistatic properties of the coatings are only slightly affected after the salt spray test. Among others, the coating with addition of 3% conductive mica shows the best performance in antistatic and anticorrosion, while the cathodic protection effectiveness of the coating is improved. |
|
来源
|
腐蚀科学与防护技术
,2018,30(5):459-466 【核心库】
|
|
DOI
|
10.11903/1002.6495.2017.289
|
|
关键词
|
防腐涂料
;
导电云母
;
抗静电性
;
阴极保护
;
电力设备
|
|
地址
|
1.
国网浙江省电力公司电力科学研究院, 杭州, 310014
2.
中国科学院金属研究所, 中国科学院核用材料与安全评价重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国网浙江省电力公司重点科技项目
|
|
文献收藏号
|
CSCD:6334684
|
参考文献 共
26
共2页
|
|
1.
陈中华. 一种环保水性抗静电防腐蚀涂料的性能研究.
中国腐蚀与防护学报,2009,29:113
|
被引
1
次
|
|
|
|
|
2.
Azim S S. Studies on graphite based conductive paint coatings.
Prog. Org. Coat,2006,55:1
|
被引
31
次
|
|
|
|
|
3.
Zhang S. Surface resistivity of carbonaceous fiber/PTFE antistatic coatings.
J. Cent. South Univ,2014,21:1689
|
被引
1
次
|
|
|
|
|
4.
吴连锋. 抗静电涂料研究概述.
涂料工业,2016,46(8):75
|
被引
7
次
|
|
|
|
|
5.
Johnson J A. Dispersion and film properties of carbon nanofiber pigmented conductive coatings.
Prog. Org. Coat,2003,47:198
|
被引
5
次
|
|
|
|
|
6.
吴宗汉. 高性能防腐涂料的进展及应用.
涂料工业,2007,37(1):45
|
被引
5
次
|
|
|
|
|
7.
张贤慧. 海洋工程用环氧富锌涂料的研究.
涂料技术与文摘,2016,37(9):33
|
被引
3
次
|
|
|
|
|
8.
杨红波. 铁路钢桥用环氧富锌防锈底漆的研制.
上海涂料,2016,54(4):10
|
被引
1
次
|
|
|
|
|
9.
谢德明. 富锌漆研究进展.
中国腐蚀与防护学报,2004,24:314
|
被引
16
次
|
|
|
|
|
10.
赵振涌. 石墨粉对低锌含量水性环氧富锌漆阴极保护性能的影响.
电镀与涂饰,2014,33:774
|
被引
6
次
|
|
|
|
|
11.
Shreepathi S. Electrochemical impedance spectroscopy investigations of epoxy zinc rich coatings: Role of Zn content on corrosion protection mechanism.
Electrochim. Acta,2010,55:5129
|
被引
32
次
|
|
|
|
|
12.
Pereira D. The application of electrochemical measurements to the study and behaviour of Zinc-rich coating.
Corros. Sci,1990,30:1135
|
被引
6
次
|
|
|
|
|
13.
Knudsen O O. Zinc-rich primers-Test performance and electrochemical properties.
Prog. Org. Coat,2005,54:224
|
被引
12
次
|
|
|
|
|
14.
官青松. 磷铁粉替代环氧富锌底漆中部分锌粉的耐腐蚀性能影响研究.
化学研究与应用,2012,24:1130
|
被引
6
次
|
|
|
|
|
15.
马少妹. 磷酸盐替代环氧富锌涂料中的锌粉制备环氧锌粉底漆.
表面技术,2011,40(3):98
|
被引
4
次
|
|
|
|
|
16.
王清海. 石墨烯在环氧富锌底漆中的应用.
涂料工业,2016,46(12):42
|
被引
16
次
|
|
|
|
|
17.
奚祥. 空心玻璃微球在环氧富锌底漆中的应用探讨.
中国涂料,2014,29(2):66
|
被引
1
次
|
|
|
|
|
18.
胡涛. 气相二氧化硅对环氧富锌涂料性能的改性研究.
广东化工,2009,36(5):11
|
被引
2
次
|
|
|
|
|
19.
Marchebois H. Characterization of zincrich powder coatings by EIS and Raman spectroscopy.
Surf. Coat. Technol,2002,157:151
|
被引
24
次
|
|
|
|
|
20.
张鉴清. 富锌涂层的电化学阻抗谱特性.
中国腐蚀与防护学报,1996,16:175
|
被引
28
次
|
|
|
|
|
了解气象卫星更多信息，请访问