相界面对双相钛合金层裂孔洞形核的影响
Effects of Phase Interface on Void Nucleation of Spallation in Dual Phase Titanium Alloy

查看参考文献11篇

杨扬 1,2,3,4   蒋志 1 *   胡海波 2   汤铁钢 2   张虎生 3   付亚楠 5  
文摘 利用一级轻气炮对TC4双相钛合金进行加载,获得初期的层裂状态,在加载中采用多普勒激光干涉测速技术对样品自由面粒子速度进行测试。在软回收经过加载的样品之后,借助于金相显微镜、X射线断层扫描、纳米压痕等检测手段进行多维分析,探讨了相界面对孔洞形核位置的影响。结果表明,孔洞绝大部分都在α相内形核,而不是如准静态损伤理论预测的形核于α/β相界面。这是由于相界面的反射与透射作用,当冲击波从高阻抗α相传入到低阻抗β相时,会在α相内产生拉伸脉冲,当拉伸脉冲足够大时,导致在α相内产生孔洞。
其他语种文摘 TC4 dual phase titanium alloy was dynamically loaded by one-stage light gas gun,resulting in an initial spallation state. During the loading,the velocity of free surface particles was measured with photonie Doppler velocimetry (PDV). The effect of α /β phase interface on dynamic damage nucleation,growth,and coalescence in TC4 were investigated by multidimensional testing techniques,such as optical microscopy,X-ray computer tomography and nanoindentation. Results showed that a majority of voids were nucleated within α-phases,rather than at the α /β phase interface as prediction by the quasi-static damage theory. Because of the effects of reflection and transmission of shock wave at the phase interface,a tensile pulse would be formed within α-phase when the shock wave was transmitted from α-phase with high impedance to β-phase with low impedance. And when this tensile pulse was large enough,voids could be formed in α-phase.
来源 矿冶工程 ,2018,38(3):143-147 【扩展库】
DOI 10.3969/j.issn.0253-6099.2018.03.035
关键词 层裂 ; 相界面 ; 孔洞形核 ; TC4双相钛合金
地址

1. 中南大学材料科学与工程学院, 湖南, 长沙, 410083  

2. 中国科学院流体物理研究所, 四川, 绵阳, 621900  

3. 中国科学院力学研究所, 北京, 100190  

4. 中南大学, 有色金属材料科学与工程教育部重点实验室, 湖南, 长沙, 410083  

5. 中国科学院上海应用物理研究所, 上海, 201800

语种 中文
文献类型 研究性论文
ISSN 0253-6099
学科 金属学与金属工艺
基金 国家自然科学基金 ;  国家自然科学基金委员会-中国工程物理研究院“NSAF联合基金” ;  非线性力学国家重点实验室开放基金
文献收藏号 CSCD:6274099

参考文献 共 11 共1页

1.  Antoun T H. Spall fracture,2003 被引 10    
2.  Meyers M A. Dynamic behavior of materials,1994 被引 156    
3.  Yang Y. Spall behaviors of high purity copper under sweeping detonation. Materials Science & Engineering A,2016,651:636-645 被引 3    
4.  Yang Y. The characteristics of void distribution in spalled high purity copper cylinder under sweeping detonation. Philosophical Magazine,2017(11):1-14 被引 1    
5.  Yang Y. Multidimensional study on spall behavior of high-purity copper under sliding detonation. Metallurgical and Materials Transactions A,2015,46(9):4070-4077 被引 3    
6.  Yang Y. X-ray quantitative analysis on spallation response in high purity copper under sweeping detonation. Materials Science & Engineering A,2016,667:54-60 被引 4    
7.  Minich R W. Effect of microstructural length scales on spall behavior of copper. Metallurgical and Materials Transactions A,2004,35:2663-2673 被引 14    
8.  Fensin S J. Dynamic damage nucleation and evolution in multiphase materials. Journal of Applied Physics,2014,115(20) 被引 3    
9.  Fensin S J. Dynamic failure in twophase materials. Journal of Applied Physics,2015,118(23) 被引 3    
10.  Han W Z. Deformation and failure of shocked bulk Cu-Nb nanolaminates. Acta Materialia,2014,63:150-161 被引 4    
11.  Curran D R. Dynamic failure of solids. Physics Reports-review Section of Physics Letters,1987,147:253-388 被引 93    
引证文献 2

1 杨扬 平板冲击加载下对双相钢动态损伤演变的研究 矿冶工程,2020,40(1):143-146
被引 1

2 邓丽萍 铸态Ti-20Zr-20Al钛合金动态压缩力学性能与断裂机制研究 矿冶工程,2020,40(6):134-137
被引 2

显示所有2篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号