Sequential deposition method fabricating carbonbased fully-inorganic perovskite solar cells
连续沉积法制备碳电极无机钙钛矿太阳电池
查看参考文献27篇
文摘
|
Hybrid organic-inorganic halide perovskite material has been considered as a potential candidate for various optoelectronic applications. However, their high sensitivity to the environment hampers the actual application. Hence the technology replacing the organic part of the hybrid solar cells needs to be developed. Herein, we fabricated fullyinorganic carbon-based perovskite CsPbBr_3 solar cells via a sequential deposition method with a power conversion efficiency of 2.53% and long-time stability over 20 d under ambient air conditions without any encapsulation. An evolution process from tetragonal CsPb_2Br_5 to CsPb_2Br_5-CsPbBr_3 composites to quasi-cubic CsPbBr_3 was found, which was investigated by scanning electron microscopy, X-ray diffraction spectra, UV-vis absorption spectra and Fourier transform infrared spectroscopy. Detailed evolution process was studied to learn more information about the formation process before 10 min. Our results are helpful to the development of inorganic perovskite solar cells and the CsPb_2Br_5 based optoelectronic devices. |
其他语种文摘
|
有机无机杂化钙钛矿是一种有潜力的光伏材料. 然而, 对于环境的高度敏感性限制了它的实际应用. 因此我们需要发展全无机钙钛矿材料. 本文通过连续沉积法制备了效率达到2.53%的碳电极CsPbBr_3太阳电池, 并且它能够在无封装的情况下稳定20天. 在制备CsPbBr_3薄膜的过程中, 我们首次发现从CsPb_2Br_5到CsPb_2Br_5-CsPbBr_3混合物到CsPbBr_3的转变. 该研究结果对于无机钙钛矿太阳电池的发展和CsPb_2Br_5基光电器件具有帮助作用. |
来源
|
Science China. Materials
,2018,61(1):73-79 【核心库】
|
DOI
|
10.1007/s40843-017-9117-4
|
关键词
|
perovskite solar cell
;
phase transition
;
carbon cathode
|
地址
|
1.
North China Electric Power University (Beijing), Beijing Key Laboratory of Novel Thin-Film Solar Cells, Beijing, 102206
2.
Hefei Institutes of Physical Science, Chinese Academy of Sciences, Key Laboratory of Photovoltaic and Energy Conservation Materials, Chinese Academy of Sciences, Hefei, 230031
3.
Academy of Opto-Electronic Technology, Hefei University of Technology, Key Lab of Special Display Technology, Ministry of Education;;National Engineering Lab of Special Display Technology;;State Key Lab of Advanced Display Technolo, Hefei, 230009
4.
NAAM Research Group, Department of Mathematics, Faculty of Science, King Abdulaziz University, Saudi Arabia, Jeddah, 21589
5.
Department of Mathematics, Quaid-I-Azam University, Pakistan, Islamabad, 44000
|
语种
|
英文 |
文献类型
|
研究性论文 |
ISSN
|
2095-8226 |
学科
|
电工技术 |
基金
|
国家973计划
;
国家自然科学基金
;
Distinguished Youth Foundation of Anhui Province
;
the Fundamental Research Funds for the Central Universities
;
the Major/Innovative Program of Development Foundation of Hefei Center for Physical Science and Technology
|
文献收藏号
|
CSCD:6190388
|
参考文献 共
27
共2页
|
1.
Kojima A. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells.
J Am Chem Soc,2009,131:6050-6051
|
被引
1055
次
|
|
|
|
2.
.
http://www.nrel.gov/ncpv/images/efficiency_chart.pn,2017
|
被引
1
次
|
|
|
|
3.
Dong Q. Electron-hole diffusion lengths>175 μm in solution-grown CH_3NH_3PbI_3 single crystals.
Science,2015,347:967-970
|
被引
173
次
|
|
|
|
4.
Ren Y. New insight into solvent engineering technology from evolution of intermediates via one-step spincoating approach.
Sci China Mater,2017,60:392-398
|
被引
13
次
|
|
|
|
5.
Lee J W. Lewis acid-base adduct approach for high efficiency perovskite solar cells.
Acc Chem Res,2016,49:311-319
|
被引
55
次
|
|
|
|
6.
Tan Z K. Bright light-emitting diodes based on organometal halide perovskite.
Nat Nanotech,2014,9:687-692
|
被引
216
次
|
|
|
|
7.
Wang Z. Morphology engineering for high-performance and multicolored perovskite light-emitting diodes with simple device structures.
Small,2016,12:4412-4420
|
被引
3
次
|
|
|
|
8.
Xing G. Low-temperature solutionprocessed wavelength-tunable perovskites for lasing.
Nat Mater,2014,13:476-480
|
被引
88
次
|
|
|
|
9.
Seo J. Rational strategies for efficient perovskite solar cells.
Acc Chem Res,2016,49:562-572
|
被引
14
次
|
|
|
|
10.
Li Z Q. One-pot synthesis of mesoporous TiO_2 micropheres and its application for high-efficiency dye-sensitized solar cells.
ACS Appl Mater Interfaces,2015,7:10928-10934
|
被引
6
次
|
|
|
|
11.
Li Z Q. Mesoporous TiO_2 yolk-shell microspheres for dye-sensitized solar cells with a high efficiency exceeding 11%.
Sci Rep,2015,5:14178
|
被引
6
次
|
|
|
|
12.
Leijtens T. Overcoming ultraviolet light instability of sensitized TiO_2 with meso-superstructured organometal tri-halide perovskite solar cells.
Nat Commun,2013,4:2885
|
被引
104
次
|
|
|
|
13.
Conings B. Intrinsic thermal instability of methylammonium lead trihalide perovskite.
Adv Energ Mater,2015,5:1500477
|
被引
87
次
|
|
|
|
14.
Manser J S. Making and breaking of lead halide perovskites.
Acc Chem Res,2016,49:330-338
|
被引
19
次
|
|
|
|
15.
Liu X. Tetraphenylmethane-arylamine hole-transporting materials for perovskite solar cells.
Chem-SusChem,2017,10:968-975
|
被引
1
次
|
|
|
|
16.
Stoumpos C C. Crystal growth of the perovskite semiconductor CsPbBr3:a new material for high-energy radiation detection.
Cryst Growth Des,2013,13:2722-2727
|
被引
49
次
|
|
|
|
17.
Kulbak M. How important is the organic part of lead halide perovskite photovoltaic cells? Efficient CsPbBr3 cells.
J Phys Chem Lett,2015,6:2452-2456
|
被引
55
次
|
|
|
|
18.
Liao J F. Inorganic cesium lead halide CsPbX_3 nanowires for long-term stable solar cells.
Sci China Mater,2017,60:285-294
|
被引
9
次
|
|
|
|
19.
Liang J. All-inorganic perovskite solar cells.
J Am Chem Soc,2016,138:15829-15832
|
被引
57
次
|
|
|
|
20.
Ripolles T S. Efficiency enhancement by changing perovskite crystal phase and adding a charge extraction interlayer in organic amine free-perovskite solar cells based on cesium.
Sol Energ Mater Sol Cells,2016,144:532-536
|
被引
7
次
|
|
|
|
|