600 ℃/NaCl-H_2O-O_2协同环境中Ti/TiAlN多层涂层的耐蚀行为
Corrosion Resistance of Alternately Multilayered Coating Ti/TiAlN on Ti-alloy Ti-6Al-4V Beneath a Solid NaCl Film in Atmosphere ofWater Vapor and Oxygen at 600 ℃
查看参考文献20篇
|
文摘
|
采用多弧离子镀技术在Ti-6Al-4V合金上沉积了单层TiAlN涂层和较厚的Ti/TiAlN多层涂层,比较了两种涂层在600 ℃/NaCl-H_2O-O_2协同环境中的腐蚀行为。结果表明:在上述环境中,单层TiAlN涂层结构存在连续的柱状晶结构,内部存在的熔滴针孔等固有缺陷成为扩散通道,腐蚀介质(O,H_2O和Cl-)沿着缺陷向内快速扩散,造成局部完全损耗,导致Ti-6Al-4V基体被腐蚀。Ti/TiAlN多层涂层由于Ti层的引入,破坏了TiAlN层连续柱状晶的结构,抑制了涂层中贯穿性固有缺陷(针孔等)的形成,有效减缓了腐蚀介质在涂层内部的扩散;而且涂层总厚度的增加明显增长了腐蚀介质到达合金基材的路径,延缓了合金被腐蚀的时间,表面形成了均匀的腐蚀产物,合金基材未受到侵蚀。Ti/TiAlN多层涂层的耐蚀性明显优于TiAlN单层涂层。 |
|
其他语种文摘
|
An alternately multilayered coating Ti/TiAlN and a coating of single layer TiAlN were respectively deposited on Ti- alloy Ti-6Al-4V by arc ion plating. Corrosion resistance of the alloy Ti-6Al-4V with the two coatings covered with a solid NaCl film was comparatively investigated in flowing atmosphere of water vapor and oxygen at 600 oC. The results show that the coating of single layer TiAlN exhibits columnar structure, which may contains some intrinsic defects such as pinholes acting as short-circuit diffusion paths for the inwards migration of corrosive species. On the other hand, the direct connection of the above mentioned short-circuit diffusion paths located in any two nearest neighbour TiN layers may be disturbed due to the intercalation of Ti layers for the Ti/TiAlN multilayer coatings, thus being beneficial to the corrosion resistance of the coating. In fact, the coating of single layer TiN showed clearly characteristics of localized corrosion induced by NaCl in flowing atmosphere of H_2O and O_2, while the coating of multilayered Ti/TiAlN kept intact. In general, the corrosion resistance of the multilayered Ti/TiAlN coating was much better than that of the single layer TiAlN coating. |
|
来源
|
中国腐蚀与防护学报
,2017,37(1):29-35 【核心库】
|
|
DOI
|
10.11902/1005.4537.2016.148
|
|
关键词
|
多弧离子镀
;
Ti/TiAlN多层涂层
;
NaCl-H_2O-O_2
;
高温腐蚀
|
|
地址
|
1.
东北大学冶金学院, 沈阳, 110819
2.
中国科学院金属研究所腐蚀与防护实验室, 沈阳, 110016
3.
东北大学材料科学与工程学院, 沈阳, 110819
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-4537 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
国家973计划
|
|
文献收藏号
|
CSCD:5945267
|
参考文献 共
20
共1页
|
|
1.
舒勇华. 固态NaCl和水蒸气协同作用下高纯铁的腐蚀行为.
金属学报,1999,35:311
|
被引
4
次
|
|
|
|
|
2.
Shu Y H. Corrosion behavior of pure Cr with a solid NaCl deposit in O_2 plus water vapor.
Oxid. Met,2000,54:457
|
被引
10
次
|
|
|
|
|
3.
舒勇华. NaCl和水蒸气对Fe—Cr合金腐蚀行为的影响.
金属学报,1999,35:1074
|
被引
4
次
|
|
|
|
|
4.
Shu Y H. Synergistic effect of NaCl and water vapor on the corrosion of 1Cr-11Ni-2W-2Mo-V steel at 500~700 ℃.
Oxid. Met,1999,51:97
|
被引
6
次
|
|
|
|
|
5.
Shu Y H. Corrosion behavior of Ti60 alloy coated with a solid NaCl deposit in O_2 plus water vapor at 500~ 700 ℃.
Oxid. Met,1999,52:463
|
被引
11
次
|
|
|
|
|
6.
Zheng D Y. The influence of TiAlN and enamel coatings on the corrosion behavior of Ti6Al4V alloy in the presence of solid NaCl deposit and water vapor at 450 ℃.
Surf. Coat. Technol,2007,201:5859
|
被引
8
次
|
|
|
|
|
7.
陈倩.
氮化物涂层对钛合金氧化腐蚀性能影响,2011
|
被引
1
次
|
|
|
|
|
8.
Aromaa J. Identification of factors affecting the aqueous corrosion properties of (Ti, Al) N-coated steel.
Surf. Coat. Technol,1991,49:353
|
被引
2
次
|
|
|
|
|
9.
Lang F Q. The corrosion resistance and wear resistance of thick TiN coatings deposited by arc ion plating.
Surf. Coat. Technol,2001,145:80
|
被引
14
次
|
|
|
|
|
10.
Jehn H A. Improvement of the corrosion resistance of PVD hard coating-substrate systems.
Surf. Coat. Technol,2000,125:212
|
被引
10
次
|
|
|
|
|
11.
王倩.
TiAlSi (Y) N涂层对钛合金高温氧化腐蚀和力学行为的影响,2012
|
被引
1
次
|
|
|
|
|
12.
Fenker M. Corrosion protection with hard coatings on steel: Past approaches and current research efforts.
Surf. Coat. Technol,2014,257:182
|
被引
6
次
|
|
|
|
|
13.
Bemporad E. High thickness Ti/TiN multilayer thin coatings for wear resistant applications.
Surf. Coat. Technol,2006,201:2155
|
被引
12
次
|
|
|
|
|
14.
Xin L. Effects of silicon and multilayer structure of TiAl (Si) N coatings on the oxidation resistance of Ti6Al4V.
Surf. Coat. Technol,2013,228:48
|
被引
6
次
|
|
|
|
|
15.
McIntyre D. Oxidation of metastable single- phase polycrystalline Ti0.5Al0.5N films: Kinetics and mechanisms.
J. Appl. Phys,1990,67:1542
|
被引
11
次
|
|
|
|
|
16.
Zhang C. Microstructure and mechanical properties of sputter deposited Ni/Ni3Al multilayer films at elevated temperature.
Appl. Surf. Sci,2016,378:408
|
被引
1
次
|
|
|
|
|
17.
Li J Z. Mono- and multiple TiN(/Ti) coating adhesion mechanism on a Ti- 13Nb- 13Zr alloy.
Appl. Surf. Sci,2015,355:502
|
被引
5
次
|
|
|
|
|
18.
Leyland A. Thick Ti/TiN multilayered coatings for abrasive and erosive wear resistance.
Surf. Coat. Technol,1994,70:19
|
被引
7
次
|
|
|
|
|
19.
Kim G S. Effects of the thickness of Ti buffer layer on the mechanical properties of TiN coatings.
Surf. Coat. Technol,2003,171:83
|
被引
10
次
|
|
|
|
|
20.
冯长杰.
电弧离子镀改性(Ti, Al) N涂层的氧化和腐蚀性能的研究,2006
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问