流变相法制备NiMn_2O_4热敏陶瓷材料及电学性能研究
Fabrication and electrical properties of NiMn_2O_4 thermistor ceramic materials by rheological phase method
查看参考文献19篇
|
文摘
|
采用流变相法制备了NiMn_2O_4负温度系数热敏电阻材料,重点研究了不同煅烧温度和烧结温度对NiMn_2O_4热敏电阻材料微观形貌和电学性能的影响,并且借助XRD、SEM以及电学测试等手段对其进行了表征。研究结果表明,煅烧温度为850 ℃时,粉体主要由立方尖晶石相和少量的NiO相组成;当烧结温度为1 150 ℃时,陶瓷样品具有最低的室温电阻率、最高的材料常数B值以及最低的电阻漂移率(ΔR/R),分别为2 679 Ω?cm、3 878 K和0.75%~0.86%。而且不同烧结温度下的陶瓷样品电导激活能都在0.33 eV左右。因此,流变相法制备的NiMn_2O_4陶瓷材料具有良好的热稳定性以及热敏性能,满足市场发展的需要。 |
|
其他语种文摘
|
NiMn_2O_4 negative temperature coeifficient (NTC) thermistor materials were prepared by the rheological phase method. The effect of calcination temperature and sintering temperature on the microstructure and electrical properties of NiMn_2O_4 ceramic materilas was systemically investigated and characterized by XRD, SEM, and electrical mearsurement. The results indicate that the NiMn_2O_4 powders are mainly composed of cubic spinel phase and a small amount of NiO phase at the calcination temperature of 850 ℃. At the sintering temperature of 1 150 ℃, the values of ceramic samples with the lowest resistivity at room temperature (ρ_(25)), the maximum value of the material constant B and the lowest resistivity drift rate (ΔR/R), are 2 679 Ω?cm, 3 878 K and 0.75%-0.86%, respectively. The activation energy of NiMn_2O_4 ceramic samples sintered at different temperatures is about 0.33 eV. Therefore, NiMn_2O_4 ceramic materials prepared by the rheological phase have well thermal stability and thermal performance and meet the demands of market development. |
|
来源
|
功能材料
,2016,47(8):8248-8252 【扩展库】
|
|
DOI
|
10.3969/j.issn.1001-9731.2016.08.045
|
|
关键词
|
流变相
;
热敏电阻
;
电阻率
;
稳定性
|
|
地址
|
1.
昌吉学院昌吉学院物理系, 中国科学院特殊环境功能材料与器件重点实验室;;新疆电子信息材料与器件重点实验室, 新疆, 昌吉, 831100
2.
中国科学院新疆理化技术研究所, 中国科学院特殊环境功能材料与器件重点实验室;;新疆电子信息材料与器件重点实验室, 乌鲁木齐, 830011
3.
昌吉学院昌吉学院物理系, 新疆, 昌吉, 831100
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-9731 |
|
学科
|
化学工业 |
|
基金
|
中国科学院西部之光人才培养计划
;
中国科学院特殊环境功能材料与器件重点实验室开放课题基金资助项目
;
国家863计划
|
|
文献收藏号
|
CSCD:5790860
|
参考文献 共
19
共1页
|
|
1.
Feteira A. Negative temperature coetticient resistance(NTCR) ceramic thermistors: an industrial perspective.
J Am Ceram Soc,2009,92(5):967-983
|
被引
31
次
|
|
|
|
|
2.
Zhang B. Spark plasma sintering of MgAl_2O_4-YCr_(0.5)Mn_(0.5)O_3 composite NTC ceramics.
J Eur Ceram Soc,2014,34(12):2989-2995
|
被引
2
次
|
|
|
|
|
3.
Diez A. Structure and physical properties of nickel manganite NiMn_2O_4 obtained from nickel permanganate precursor.
J Eur Ceram Soc,2010,30(12):2617-2624
|
被引
2
次
|
|
|
|
|
4.
Ashcroft G. Study of the preparation conditions for NiMn_2O_4 grown from hydroxide precursors.
J Eur Ceram Soc,2006,26(6):901-908
|
被引
8
次
|
|
|
|
|
5.
Yao J C. Effect of La_2O_3 addition on copper-nickel manganese thermistors for low-temperature applications.
INT J Appl Ceram Tec,2013,10(S1):E106-E122
|
被引
2
次
|
|
|
|
|
6.
Zhuang J W. The effects of pH value on the characterization of CoMnNiO NTC thermistor nanopowders.
Ceram Int,2004,30(7):1661-1663
|
被引
3
次
|
|
|
|
|
7.
Zhang H M. The optimal synthesis condition by sol-gel method and electrical properties of Mn_(1.5-x)Co_(1.5)Ni_xO_4 ceramics.
Ceram Int,2014,40(6):7865-7872
|
被引
2
次
|
|
|
|
|
8.
Huang J S. Organic phosphoric sources for syntheses of Li_3V_2(PO_4)_3/C via improved rheological phase reaction.
Mater Lett,2012,66(1):196-198
|
被引
1
次
|
|
|
|
|
9.
Yao J C. Preparation of Ni_(0.9)Mn_(2.1-x)Mg_xO_4(0 ≤x≤ 0.3) negative temperature coefficient ceramic materials by a rheological phase reaction method.
Mater Lett,2013,112:69-71
|
被引
2
次
|
|
|
|
|
10.
黄艳华. 草酸盐共沉淀前驱体的热分解过程.
冶金粉末材料科学与工程,2007,1(12):35-38
|
被引
1
次
|
|
|
|
|
11.
Fang D L. Aging of nickel manganite NTC ceramics.
J Electroceram,2009,22(4):421-427
|
被引
3
次
|
|
|
|
|
12.
Fang D L. Preparation of ultra-fine nickel manganite powders and ceramics by a solid state coordination reaction.
J Am Ceram Soc,2006,89(1):230-235
|
被引
8
次
|
|
|
|
|
13.
Csete De Gyorgyfalva G D C. Decomposition of NiMn_2O_4 spinels.
J Mater Res,2003,18(6):1301-1308
|
被引
1
次
|
|
|
|
|
14.
Feltz A. Spinel forming ceramics of the system Fe_xNi_yMn_(3-x-y)O_4 for high temperature NTC thermistor applications.
J Eur Ceram Soc,2000,20(14/15):2353-2356
|
被引
10
次
|
|
|
|
|
15.
马仁君. 固相球磨-水热法制备Mn_(1.5)6Co_(0.9)6Ni_(0.48)O_4纳米粉体及其NTC性能.
功能材料,2014,45(20):20146-20149
|
被引
1
次
|
|
|
|
|
16.
张惠敏. NTC陶瓷材料Co_(1.5)Mn_(1.5-x)Ni_xO_4中阳离子分布与导电性间的关系.
无机化学学报,2010,5(26):781-786
|
被引
1
次
|
|
|
|
|
17.
Park K. Structural and electrical properties of MgO-doped Mn_(1.4)Ni_(1.2)Co_(0.4-x)Mg_xO_4(0≤x≤0.25)NTC thermistors.
J Eur Ceram Soc,2007,27(4):2009-2016
|
被引
10
次
|
|
|
|
|
18.
Gao H. Preparation and characterization of NiMn_2O_4 negative temperature coefficient ceramics by solid-state coordination reaction.
J Mater Sci: Mater Electron,2014,25(9):3990-3995
|
被引
3
次
|
|
|
|
|
19.
Ma C J. Preparation and characterization of Ni_(0.6)Mn_(2.4)O_4 NTC ceramics by solid-state coordination reaction.
J Mater Sci: Mater Electron,2013,24(12):5183-5188
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问