微结构和应力比对Ti-6A1-4V高周和超高周疲劳行为的影响
EFFECTS OF MICROSTRUCTURE AND STRESS RATIO ON HIGH-CYCLE AND VERY-HIGH-CYCLE FATIGUE BEHAVIOR OF Ti-6A1-4V ALLOY
查看参考文献25篇
|
文摘
|
采用旋转弯曲和超声疲劳实验分别测试了全等轴和等轴双态组织Ti-6A1-4V合金的高周和超高周疲劳性能,并用SEM观察了疲劳断口特征.结果表明:2种组织T1-6A1-4V合金的高周和超高周疲劳行为相似,不同应力比下,其S-N曲线均表现出单线形或双线形的形式;存在滑移机制和解理机制2种疲劳破坏机制.随应力比增加,2种组织Ti-6A1-4V合金的高周和超高周疲劳破坏机制均从滑移机制向解理机制转变.基于疲劳寿命和疲劳强度建立模型分析了应力比对2种机制之间竞争行为的影响,模型预测结果与实验结果趋势吻合. |
|
其他语种文摘
|
Titanium alloys have been widely used as superior engineering materials because of their high specific strength, high temperature resistance and high corrosion resistance. In their engineering applications such as used in aircraft engines, titanium alloys may experience even 10~(10) fatigue cycles. Recently, faceted crack initiation was observed in high-cycle fatigue (HCF) and very-high-cycle fatigue (VHCF) regimes of titanium alloys, which resulted in a sharp decrease in fatigue strength. Therefore, the HCF and VHCF of titanium alloys have both scientific significance and engineering requirement. In this work, the effects of microstructure and stress ratio (R) on HCF and VHCF of a Ti-6A1-4V alloy have been investigated. Fatigue tests were conducted on a rotating-bending fatigue machine and an ultrasonic fatigue machine. All the fatigue fracture surfaces were observed by SEM. The results show that the HCF and VHCF behaviors of the fully-equiaxed and the bimodal Ti-6A1-4V alloy are similar. The observations of fracture surface indicate that two crack initiation mechanisms prevail, i.e. slip mechanism and cleavage mechanism. With the increase of stress ratio, the crack initiation mechanism switches from slip to cleavage. The S-N curves present the single-line type or the bilinear type. For the cases of rotating-bending and ultrasonic axial cycling with R= -1.0, -0.5 and 0.5, the S-N curves are single-line type corresponding to the slip mechanism or cleavage mechanism. For the cases of R= -0.1 and 0.1,the S-N curves are bilinear type corresponding to both slip and cleavage mechanisms. A model based on fatigue life and fatigue limit is proposed to describe the competition between the two mechanisms, which is in agreement with the experimental results. |
|
来源
|
金属学报
,2016,52(8):923-930 【核心库】
|
|
DOI
|
10.11900/0412.1961.2015.00581
|
|
关键词
|
Ti-6A1-4V合金
;
超高周疲劳
;
微结构
;
应力比
;
滑移机制
;
解理机制
|
|
地址
|
1.
中国科学院力学研究所, 非线性力学国家重点实验室, 北京, 100190
2.
瓦房店轴承股份有限公司热处理分厂, 大连, 116300
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金项目
|
|
文献收藏号
|
CSCD:5761349
|
参考文献 共
25
共2页
|
|
1.
Li S X.
Int Mater Rev,2012,57:92
|
被引
14
次
|
|
|
|
|
2.
洪友士. 合金材料超高周疲劳行为的基本特征和影响因素.
金属学报,2009,45:769
|
被引
27
次
|
|
|
|
|
3.
Liu X L.
Mater Sci Eng,A,2015,622:228
|
被引
12
次
|
|
|
|
|
4.
Leopold G.
Fatigue Fract Eng Mater Struct,2015,38:1026
|
被引
1
次
|
|
|
|
|
5.
丁宏升. 冷坩埚定向凝固Ti-47Al-2Cr-2Nb合金的拉伸与高周疲劳性能研究.
金属学报,2015,51:569
|
被引
1
次
|
|
|
|
|
6.
Neal F D.
Acta Metall,1976,24:59
|
被引
1
次
|
|
|
|
|
7.
Szczepanski C J.
Metall Mater Trans,A,2008,39:2841
|
被引
10
次
|
|
|
|
|
8.
Chandran K S.
Acta Mater,2005,53:1867
|
被引
1
次
|
|
|
|
|
9.
Chandran K S.
Int J Fatigue,2010,32:482
|
被引
1
次
|
|
|
|
|
10.
Oguma H.
Int J Fatigue,2013,50:89
|
被引
10
次
|
|
|
|
|
11.
Oguma H.
Scr Mater,2010,63:32
|
被引
10
次
|
|
|
|
|
12.
Chandran K S.
Nat Mater,2005,4:303
|
被引
1
次
|
|
|
|
|
13.
Shanyavskiy A A.
Sci China-Phys Mech Astron,2014,57:19
|
被引
4
次
|
|
|
|
|
14.
Lei Z Q.
Sci China-Phys Mech Astron,2014,57:74
|
被引
2
次
|
|
|
|
|
15.
Matsunaga H.
Fatigue Fract Eng Mater Struct,2015,38:1274
|
被引
3
次
|
|
|
|
|
16.
Goodman J.
Mechanics Applied Engineering,1899:30
|
被引
1
次
|
|
|
|
|
17.
Gerber W.
Z Bayer Archit Ing Ver,1874,6:101
|
被引
1
次
|
|
|
|
|
18.
Zuo J H.
Mater Sci Eng,A,2008,473:147
|
被引
24
次
|
|
|
|
|
19.
竹内悦男.
鉄と鋼,2010,96:36
|
被引
1
次
|
|
|
|
|
20.
Takeuchi E.
Fatigue Fract Eng Mater Struct,2008,31:599
|
被引
10
次
|
|
|
|
|
了解气象卫星更多信息，请访问