蠕墨铸铁激光合金化熔覆的界面组织及性能
Microstructure and mechanical properties of NiCoCrAlY coating on compacted graphite iron by laser cladding

查看参考文献14篇

文摘 针对铸铁激光熔覆涂层结合界面淬火硬化、裂纹倾向大的问题,提出激光合金化与激光熔覆相结合的工艺在蠕墨铸铁表面制备NiCoCrAlY合金涂层。通过光学显微镜、扫描电子显微镜、X射线衍射仪、维氏硬度计研究了激光合金化熔覆中熔覆层稀释率、组织、显微硬度的演化规律,通过三点弯曲试验考察了熔覆层的结合特性及力学性能。结果表明:激光合金化熔覆工艺方法将热影响区由马氏体组织转变为回火索氏体组织,降低了淬硬层深度,改善了熔覆层结合特性与塑性,抗弯强度提高到891MPa。断口显示,熔覆层与基体结合良好,断裂机制是脆性解理断裂与韧窝断裂混合机制。
其他语种文摘 Considering the problem of quench hardening and cracking at the interface of laser cladding coating on the cast iron,a method combined laser alloy and laser cladding was proposed to produce NiCoCrAlY coating on compacted graphite iron.The dilution, microstructure and microhardness of the coating were investigated by means of optical microscope,scanning electron microscopy,X-ray diffractometer,Vickers hardness tester.The bonding characteristics and mechanical properties of the layer were evaluated by three-point bending test.The results show that martensite turns to tempered sorbite in heat affected zone by the laser alloy cladding method,thus the depth of hardening layer decreases.Simultaneously,the bonding characteristics and plasticity are improved,and the bending strength is raised to 891 MPa.The fracture morphology shows a good bonding between coating and substrate,and also a combination of cleavage fracture and dimple fracture.
来源 材料热处理学报 ,2015,36(3):171-176 【核心库】
DOI 10.13289/j.issn.1009-6264.2015.03.031
关键词 蠕墨铸铁 ; 激光熔覆 ; 稀释率 ; 显微组织 ; 抗弯强度
地址

中国科学院力学研究所, 中国科学院先进制造工艺力学重点实验室, 北京, 100190

语种 中文
文献类型 研究性论文
ISSN 1009-6264
学科 金属学与金属工艺
基金 国家自然科学基金 ;  江苏高校优势学科建设工程
文献收藏号 CSCD:5407649

参考文献 共 14 共1页

1.  Ehsan Toyserkani. Laser Cladding,2005 被引 15    
2.  钟敏霖. 国际激光材料加工研究的主导领域与热点. 中国激光,2008,35(11):1653-1659 被引 43    
3.  Dubourg L. Technological and scientific landscape of laser cladding process in 2007. Sur Coat Tech,2008,202(24):5863-5869 被引 23    
4.  Bekir S Y. Laser Surface Processing and Model Studies,2013 被引 1    
5.  Dawson S. Practical applications for compacted graphite iron. AFS Transactions,2004,71(1):1211-1216 被引 1    
6.  聂树真. 强度分布整形激光束加载模拟热负荷温度场的实验研究,2011:2-14 被引 1    
7.  周振峰. 铸铁焊接冶金与工艺,2001 被引 1    
8.  董世运. 铸铁件激光熔覆NiCuFeBSi合金组织及力学性能. 中国激光,2012,39(12):67-73 被引 7    
9.  Lestan Z. Laser deposition of Metco 15E,Colmony 88 and VIM CRU 20 powders on cast iron and low carbon steel. International Journal of Advanced Manufacturing Technology,2013,66(9/12):2023-2028 被引 4    
10.  谭真. 工程合金热物性,1994 被引 84    
11.  Zhang X. Modeling of the residual stresses in plasma-spraying functionally graded ZrO2 /NiCoCrAlY coatings using finite elements method. Materials & design,2006,27(4):308-315 被引 1    
12.  乔虹. 激光熔覆工艺参数对Fe-Cr-B合金涂层组织和硬度的影响. 材料热处理学报,2014,35(2):164-168 被引 12    
13.  刘秀波. 等离子熔覆γ/Cr_7C_3复合材料涂层组织与耐磨性研究. 材料热处理学报,2006,27(6):114-117 被引 6    
14.  Li Z Y. Fatigue crack propagation in laser alloyed ductile cast iron surface. Journal of Laser Applications,2013,25(1):012003 被引 1    
引证文献 5

1 武岳 热处理工艺对RuT300蠕墨铸铁力学性能与导热性能的影响 材料热处理学报,2017,38(2):143-151
被引 5

2 张延京 FeS对复合铸铁石墨形态分布规律的影响 材料热处理学报,2016,37(8):113-118
被引 1

显示所有5篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号