氩气/空气辉光放电对聚乙烯薄膜的表面改性研究
Surface Modification of Polythene Membranes by Glow Discharge in Argon/Air Plasma
查看参考文献31篇
|
文摘
|
利用氩气/空气混合气体辉光放电对聚乙烯(PE)材料表面改性。主要研究了单一气体等离子体和混合气体等离子体对 PE 膜表面改性的影响,通过蒸馏水的接触角测量和二碘甲烷的接触角测量对处理前后的 PE 膜表面性质进行表征,对PE膜表面能的变化进行了分析。实验结果表明,经辉光放电等离子体处理过的 PE 膜表面的液体接触角显著下降,固体表面能有明显提高,在固定的电压和气压下,PE 膜表面水接触角随着氩气/空气混合比例的增大而先减小后增大,说明辉光放电比丝状放电在提高聚乙烯材料润湿性方面效果要好。处理后的样品放置在空气当中后,样品表面水接触角有所增大,但始终小于处理前的接触角。 |
|
其他语种文摘
|
The surfaces of polythene(PE)membranes were modified by glow discharge in argon/air plasma.The effects of the glow discharge conditions,including but not limited to the ratio of argon/air flow rates,pressure,discharge voltage and discharge time,on the wettability of PE membranes were investigated. The results show that depending on the ratio of Ar/air flow rates,the glow discharge considerably improved the wettability of PE membranes. For example,as the ratio increased,the water contact angle of PE membranes changed in a decrease-increase mode,accompanied by an increase of surface energy. When it comes to the transition of PE membrane from hydrophobility to hydrophilicity by surface modification,the glow discharge outperforms filament discharge. Decreased with storage time,the hydrophilicity of the modified PE membrane remains to be higher than that of the control sample. |
|
来源
|
真空科学与技术学报
,2014,34(12):1315-1320 【扩展库】
|
|
关键词
|
氩气/空气
;
辉光放电
;
聚乙烯薄膜
;
表面改性
|
|
地址
|
1.
山东青年政治学院信息工程学院, 山东省高校信息安全与智能控制重点实验室, 济南, 250103
2.
山东青年政治学院信息工程学院, 济南, 250103
3.
中国科学院等离子体物理研究所, 山东省高校信息安全与智能控制重点实验室, 合肥, 230031
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1672-7126 |
|
学科
|
化学工业 |
|
基金
|
山东省自然科学基金
;
山东青年政治学院重点研究基金项目
|
|
文献收藏号
|
CSCD:5320109
|
参考文献 共
31
共2页
|
|
1.
马兰. 塑料薄膜材料的性能简介.
中国印刷物资商情,2005(3):39-41
|
被引
1
次
|
|
|
|
|
2.
郑丽霞. 低温等离子体法制备超亲水PE薄膜及其性能研究究.
浙江理工大学学报,2013,30(4):19-23
|
被引
1
次
|
|
|
|
|
3.
欧军飞. 聚合物表面改性方法概述.
塑料工业,2007,35(11):5-10
|
被引
14
次
|
|
|
|
|
4.
Broseta D. Molecular Weight and Polydispersity Effects at Polymer-Polymer Interfaces.
Macromolecules,1990,23(1):132-139
|
被引
4
次
|
|
|
|
|
5.
Yang W T. Photoinitiation Performance of some Ketones in the LDPE-Acrylic Acid Surface Photografting System.
European Polymer Journal,1999,35(8):1557-1568
|
被引
15
次
|
|
|
|
|
6.
Zhu S Q. Improving the Wettability of Deep-Groove Polypropylene Fibers by Photografting.
Textile Research Journal,2009,79(6):534-547
|
被引
2
次
|
|
|
|
|
7.
孟月东. 低温等离子体技术应用研究进展.
物理,2006,35(2):140-146
|
被引
25
次
|
|
|
|
|
8.
李洪霞. 大气压等离子体射流改性船体钢表面亲水性研究.
真空科学与技术学报,2012,32(4):269-273
|
被引
8
次
|
|
|
|
|
9.
方志. 空气中大气压下低温等离子体对聚四氟乙烯进行表面改性的研究.
真空科学与技术学报,2003,23(6):408-412
|
被引
10
次
|
|
|
|
|
10.
Hendricks S K. Plasma-Deposited Membranes for Controlled Release of Antibiotic to Prevent Bacterial Adhesion and Biofilm formation.
Journal of Biomedical Materials Research,2000,50(21):60-170
|
被引
2
次
|
|
|
|
|
11.
Wang J. The Analysis of Armos Fibers Reinforced Poly (Phthalazinone Ether Sulfone Ketone) Composite Surfaces after Oxygen Plasma Treatment.
Surface and Coatings Technology,2008,202(20):4986-4991
|
被引
7
次
|
|
|
|
|
12.
郭玉海. 空气电晕放电处理涤纶织物表面结构性能表征.
中国纺织大学学报(自然科学版),2000,26(1):102-105
|
被引
1
次
|
|
|
|
|
13.
马丕波. 电晕处理对涤纶纱线上浆性能的影响.
纺织学报,2009,30(4):74-79
|
被引
1
次
|
|
|
|
|
14.
马丕波. 电晕处理对棉织物表面性能的影响.
天津工业大学学报,2009,28(1):53-56
|
被引
3
次
|
|
|
|
|
15.
解艳凤. 直流脉冲偏压协同射频等离子体对PET膜的表面改性.
真空科学与技术学报,2013,33(9):893-897
|
被引
5
次
|
|
|
|
|
16.
Gerenser L J. Esca Studies of Corona-Discharge-Treated Polyethylene Surfaces by Use of Gas-Phase Derivatization.
Polymer,1985,26(8):1162-1166
|
被引
2
次
|
|
|
|
|
17.
Brandenburg R. The Hairline Plasma:an Intermittent Negative Dc-Corona Discharge at Atmospheric Pressure for Plasma Medical Applications.
Applied Physics Letters,2010,96(14):143701-1-143701-3
|
被引
11
次
|
|
|
|
|
18.
Chang J S. Corona Discharge Processes.
IEEE Transactions on Plasma Sciences,1991,19(6):1152-1166
|
被引
60
次
|
|
|
|
|
19.
解林坤. RF-Ar等离子体对聚乙烯薄膜的表面改性.
真空科学与技术学报,2012,32(7):545-549
|
被引
5
次
|
|
|
|
|
20.
李成榕. 大气压下的辉光放电.
高电压技术,2002,120(28):41-43
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问