铝青铜聚酯封严涂层的制备和可磨耗性能评价
Preparation and Abradability Evaluation of Aluminum Bronze Polyester Abradable Sealing Coating
查看参考文献17篇
|
文摘
|
采用机械混合的方法制备了用于可磨耗涂层的铝青铜聚酯复合粉末,并通过大气等离子喷涂制备了相应涂层。通过滑动摩擦实验,对比考察了该涂层与Metco 605NS涂层在不同温度下的可磨耗性能。结果表明:涂层组织中聚酯和孔隙分布均匀;在室温和200℃下,采用混合粉末制备的涂层与钛合金配副摩擦因数均在0.4左右,磨痕表面光滑平整,磨损体积较Metco 605NS涂层更大,表现出更优异的可磨耗性能;在400℃时,聚酯的烧蚀和涂层致密化,以及滑动摩擦实验采用的点接触产生的高接触应力,使得与两种涂层对磨的钛合金均产生黏着剥落和磨粒磨损,摩擦因数升高且存在较大波动。 |
|
其他语种文摘
|
CuAl polyester composite powders were prepared by mechanical mixing fine polyester powders and CuAl alloy powders with irregular shape. This mixed powder and a commercial CuAl polyester Metco 605NS were used for depositing abradable sealing coatings by atmosphere plasma spraying. Sliding wear tests against Ti6Al4V alloy at different temperatures were conducted on the two kinds of sealing coatings to compare their abradability. The results show that at room temperature and 200℃, the coatings obtained from the mixed powder have friction coefficients about 0.4 and smooth wear scars, as well as better abradability than the coatings deposited by the commercial powder. While at 400℃, adhesive spalling and abrasive wear are observed in Ti6Al4V, and the friction coefficients of both coatings increase and are unstable which should be attributed to the burn of polyester and the densification of the coatings, as well as the point contact mode of the wear tests which is apt to generate higher Hertzian stress. |
|
来源
|
材料工程
,2014(9):8-13 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2014.09.002
|
|
关键词
|
大气等离子喷涂
;
铝青铜
;
聚酯
;
封严
;
可磨耗
|
|
地址
|
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 兰州, 730000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
航空 |
|
基金
|
国家973计划
;
国家自然科学基金资助项目
|
|
文献收藏号
|
CSCD:5239078
|
参考文献 共
17
共1页
|
|
1.
赖师墨. 控制航空发动机运转间隙的热喷涂封严涂层.
航空制造技术,1995(增刊1):53-55
|
被引
2
次
|
|
|
|
|
2.
Stringer J. High speed wear testing of an abradable coating.
Wear,2012,294(1):257-263
|
被引
20
次
|
|
|
|
|
3.
孙杰. 高温合金/NiAl封严涂层的电偶腐蚀行为研究.
材料工程,2013(7):61-65
|
被引
2
次
|
|
|
|
|
4.
Ebert S. Failure mechanisms of magnesia alumina spinel abradable coatings under thermal cyclic loading.
Journal of the European Ceramic Society,2013,33(15/16):3335-3343
|
被引
5
次
|
|
|
|
|
5.
Dorfman M. Gas turbine use "abradable" coatings for clearance-control seals.
Sealing Technology,2002,2002(1):7-8
|
被引
10
次
|
|
|
|
|
6.
Faraoun H. Modeling route for abradable coatings.
Surface & Coatings Technology,2006,200(23):6578-6582
|
被引
16
次
|
|
|
|
|
7.
Johnston R E. Mechanical characterization of AlSi-hBN, NiCrAl-Bentonite, and NiCrAl-Bentonite-hBN freestanding abradable coatings.
Surface & Coatings Technology,2011,205(10):3268-3273
|
被引
17
次
|
|
|
|
|
8.
高忠宝. 纳米Y-PSZ基材料高温封严涂层的研制.
航空材料学报,2008,28(4):56-59
|
被引
7
次
|
|
|
|
|
9.
Ma X. Evaluation of abradable seal coating mechanical properties.
Wear,2009,267(9/10):1501-1510
|
被引
14
次
|
|
|
|
|
10.
许存官. Ni/石墨封严涂层的盐雾腐蚀研究.
航空材料学报,2010,30(4):53-57
|
被引
7
次
|
|
|
|
|
11.
曲选辉. 粉末冶金技术在航空发动机中的应用.
航空材料学报,2014,34(1):1-10
|
被引
27
次
|
|
|
|
|
12.
高俊国. 氧燃充枪比对爆炸喷涂CoCrAlYTa涂层组织和性能的影响.
航空材料学报,2013,33(2):29-34
|
被引
9
次
|
|
|
|
|
13.
朱佳. 封严涂层材料及应用.
材料开发与应用,2008,23(4):78-84
|
被引
7
次
|
|
|
|
|
14.
刘夙伟. 封严涂层材料及其可刮削性的评价.
中国表面工程,2009,22(1):12-18
|
被引
21
次
|
|
|
|
|
15.
陈恩强. 聚苯酯的性能及应用.
工程塑料应用,2002,30(8):57-60
|
被引
3
次
|
|
|
|
|
16.
Davis J R.
Handbook of Thermal Spray Technology,2004:47-53
|
被引
1
次
|
|
|
|
|
17.
王智平. 高铝青铜Cu14Alx摩擦磨损特性的研究.
铸造,2003,52(3):185-188
|
被引
15
次
|
|
|
|
|
了解气象卫星更多信息，请访问