激光离散处理车轮钢- 钢轨钢摩擦副的摩擦学性能研究
Tribological Properties of Laser Dispersed Treated Wheel Steel - Rail Steel Tribopairs

查看参考文献22篇

曾东方 1   鲁连涛 1 *   李正阳 2   张继旺 1   朱旻昊 1   金学松 1  
文摘 将激光离散处理前后的车轮试样分别与钢轨试样匹配,利用滚动接触摩擦磨损试验机测试各摩擦副的摩擦系数和磨损率,研究激光离散处理对轮轨摩擦副滚动接触摩擦磨损性能的影响. 结果表明:车轮试样经过激光离散处理后,其抗磨损性能大幅增加,对应的轮轨试样摩擦副的摩擦系数小幅增加,其对摩钢轨试样的磨损加剧. 未处理车轮试样主要发生剥层磨损并伴随轻微的疲劳磨损;处理后的车轮试样主要发生疲劳磨损并伴随轻微的剥层磨损. 这是由于激光离散处理提高了车轮试样表层材料的抗塑性变形能力,从而抑制了材料的剥层磨损. 各钢轨试样均发生剥层磨损,但是车轮试样经激光离散处理后,对应钢轨试样的剥层磨损加剧.
其他语种文摘 Laser dispersed treatment (LDT) was performed on wheel steel. The treated and untreated wheel steels were mated with rail steel and the friction coefficient and wear rate of these frictional pairs were measured on a rolling sliding test machine. The effect of LDT on the rolling contact friction and wear behavior of these frictional pairs was investigated. The results show that the wear resistance of treated wheel steel was improved obviously,while the friction coefficient of the frictional pair was increased and the wear of the corresponding rail steel is deteriorated. The dominant wear mechanism in the untreated wheel steel was delamination wear accompanied by mild fatigue wear. The dominant wear mechanism in the treated wheel steel was fatigue wear accompanied by mild delamination wear. LDT improved the plastic deformation resistance of wheel steel and inhibited the treated wheel steel from delamination wear. The delamination was the dominant wear mechanism for both rail steels against treated and untreated wheel steels. However,the delamination wear of rail steel was deteriorated after LDT was performed on the corresponding wheel steel.
来源 摩擦学学报 ,2014,34(1):79-86 【核心库】
关键词 激光离散处理 ; 摩擦磨损 ; 车轮钢 ; 钢轨钢 ; 剥层磨损
地址

1. 西南交通大学, 牵引动力国家重点实验室, 四川, 成都, 610031  

2. 中国科学院力学研究所, 北京, 100190

语种 中文
文献类型 研究性论文
ISSN 1004-0595
学科 机械、仪表工业
基金 国家科技支撑计划项目 ;  国家铁道部科技研究开发计划项目 ;  国家自然科学基金高铁联合基金 ;  2014年西南交通大学博士研究生创新基金 ;  中央高校基本科研业务费专项资金
文献收藏号 CSCD:5059985

参考文献 共 22 共2页

1.  崔银会. 铬对高速车轮钢显微组织和力学性能的影响. 钢铁研究学报,2006,18(8):39-42 被引 5    
2.  曾东方. 合金含量对高速车轮材料滚动接触磨损性能的影响. 摩擦学学报,2012(6):599-605 被引 5    
3.  Fletcher D I. Image analysis to reveal crack development using a computer simulation of wear and rolling contact fatigue. Fatigue & Fracture of Engineering Materials & Structures,2003,26(10):957-967 被引 2    
4.  Franklin F J. Computer simulation of wear and rolling contact fatigue. Wear,2001,251:949-955 被引 15    
5.  Lonsdale C. Some possible alternatives for longer - life locomotive wheels. Proceedings of 2002 ASME International Mechanical Engineering Congress & Exposition,2002:239-244 被引 1    
6.  Taleff E M. Pearlite in ultrahigh carbon steels: Heat treatments and mechanical properties. Metallurgical and Materials Transactions A,1996,27(1):111-118 被引 17    
7.  王文健. 轮轨材料硬度匹配性能试验研究. 摩擦学学报,2013,33(1):65-69 被引 23    
8.  季怀忠. 碳含量对高速车轮用钢综合性能的影响. 钢铁,2005,40(2):62-65 被引 8    
9.  Singh U. Influence of microalloying on mechanical and metallurgical properties of wear resistant coach and wagon wheel steel. Journal of materials engineering and performance,2003,12(5):573-580 被引 12    
10.  Franklin F. Rolling contact fatigue and wear behaviour of the infrastar two - material rail. Wear,2005,258(7):1048-1054 被引 8    
11.  DiMelfi R. Mitigation of subsurface crack propagation in railroad rails by laser surface modification. Surface and Coatings Technology,1998,106(1):30-43 被引 2    
12.  Aldajah S. Investigation of top of rail lubrication and laser glazing for improved railroad energy efficiency. Journal of tribology,2003,125(3):643-648 被引 3    
13.  Wang H. Rapid graphitization of a pulsed laser remelted ductile cast iron during multipass overlap melting. Metallurgical and Materials Transactions A,1995,26(4):793-800 被引 2    
14.  Iino Y. Effect of overlap pass tempering on hardness and fatigue behaviour in laser heat treatment of carbon steel. Journal of materials science letters,1987,6(10):1193-1194 被引 2    
15.  Jiang J. Discrete laser spot transformation hardening of AISI O1 tool steel using pulsed Nd: YAG laser. Surface and Coatings Technology,2011,205(21):5156-5164 被引 1    
16.  李正阳. 激光点状合金化对42CrMo钢疲劳裂纹扩展速率的影响. 应用激光,2007,27(1):1-4 被引 2    
17.  Suh N P. The delamination theory of wear. Wear,1973,25(1):111-124 被引 52    
18.  Чкалов Л А. 车轮与钢轨的激光强化. 国外机车车辆工艺,2000,2:7-12 被引 1    
19.  陈扬枝. 机车轮缘减磨研究. 内燃机车,1995(8):4-7 被引 1    
20.  周清跃. 客运专线钢轨的强度等级和材质选择. 中国铁路,2007(7):41-45 被引 7    
引证文献 6

1 曹熙 激光离散淬火对轮轨材料磨损与损伤性能的影响 中国表面工程,2016,29(5):72-79
被引 10

2 丁阳喜 铁道车辆轮轨表面激光改性技术研究综述 热加工工艺,2016,45(14):26-30
被引 0 次

显示所有6篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

ResearcherID 链接
李正阳 D-3234-2009
版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号