Process Parameter Optimizing and Studies on Microstructure and Properties of AZ31 Alloy Prepared by Semisolid Rolling Process
查看参考文献20篇
|
文摘
|
A novel continuous semisolid rolling process for producing AZ31 alloy strip was developed. The process parameters were optimized, and microstructure and properties of AZ31 alloy prepared by the process were studied. The results reveal that primary grains of the strip become coarse, and the grain structure transforms from round shape to dendrite with the increment of casting temperature gradually. Eutectic phase fraction and primary grain size increase with the increment of roll speed. The primary grain size decreases firstly and then increases with the increment of the vibration frequency correspondingly. When the casting temperature is from 650 °C to 690 °C, the roll speed is 0.069 m·s~(-1), and the vibration frequency is about 80 Hz, AZ31 alloy strip with a cross section size of 4 mm×160 mm was prepared by the proposed process. The ultimate tensile strength and elongation are improved 1% and 57%, respectively. |
|
来源
|
Acta Metallurgica Sinica(English Letters)
,2013,26(3):293-298 【核心库】
|
|
DOI
|
10.1007/s40195-012-0190-5
|
|
关键词
|
Semisolid
;
Sloping plate
;
Rolling
;
AZ31 alloy
;
Microstructure
;
Property
|
|
地址
|
School of Materials and Metallurgy, Northeastern University, Shengyang, 110189
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1006-7191 |
|
学科
|
金属学与金属工艺 |
|
基金
|
supported by the National Natural Science Foundation for Outstanding Young Scholars of China
;
国家自然科学基金
;
国家教育部霍英东教育基金
;
国家973计划
|
|
文献收藏号
|
CSCD:4842670
|
参考文献 共
20
共1页
|
|
1.
Yu K.
Chin. J. Nonferr. Met. (in Chinese),2003,13:277
|
被引
13
次
|
|
|
|
|
2.
Wu S S.
Foundry. (in Chinese),2002,51:583
|
被引
1
次
|
|
|
|
|
3.
Flemings M C.
Mater. Sci. Eng. A,1976,25:103
|
被引
45
次
|
|
|
|
|
4.
Giraud E.
Metall. Mater. Trans. A,2011,42:3370
|
被引
2
次
|
|
|
|
|
5.
Moeller H.
Int. J. Cast. Met. Res,2009,22:417
|
被引
2
次
|
|
|
|
|
6.
Haghayeghia R.
J. Alloys Compd,2010,502:382
|
被引
2
次
|
|
|
|
|
7.
Zhang X L.
Rare Met. Mater. Eng. (in Chinese),2009,38:1495
|
被引
1
次
|
|
|
|
|
8.
Motegi T.
Int. J. Mater. Prod. Technol,2001,2:468
|
被引
5
次
|
|
|
|
|
9.
Kapranos P.
J. Mater. Process. Technol,2003,135:271
|
被引
23
次
|
|
|
|
|
10.
Grimmig T.
Diffus. Defect Data Part B,2006,116/117:484
|
被引
6
次
|
|
|
|
|
11.
Haga T.
J. Mater. Process. Technol,2004,153/154:42
|
被引
42
次
|
|
|
|
|
12.
Guan R G.
Mater. Sci. Forum,2007,561/565:865
|
被引
4
次
|
|
|
|
|
13.
Canyook R. Evolution of microstructure in semi-solid slurries of rheocast aluminum alloy.
Trans. Nonferr. Met. Soc. Chin,2010,20:1649
|
被引
10
次
|
|
|
|
|
14.
Mehrara H.
Diffus. Defect Data Part B,2008,141/143:785
|
被引
2
次
|
|
|
|
|
15.
Guan R G.
J. Mater. Process. Technol,2012,212:1430
|
被引
13
次
|
|
|
|
|
16.
Guan R G.
J. Mater. Process. Technol,2009,209:2592
|
被引
28
次
|
|
|
|
|
17.
Ye H Z.
J. Alloys Compd,2006,419:54
|
被引
8
次
|
|
|
|
|
18.
Zhao H.
J. Mater. Process. Technol,2012,212:1670
|
被引
5
次
|
|
|
|
|
19.
Tan X F.
Chin. Mech. Eng. (in Chinese),2010,21:2865
|
被引
1
次
|
|
|
|
|
20.
Masoumi M.
Mater. Sci. Eng. A,2011,528:1268
|
被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问