利用盐泥制取轻质氧化镁
Preparation of Light Magnesium Oxide from Salt Mud
查看参考文献14篇
|
文摘
|
采用二氧化碳法提取盐泥中的镁,研究了使之转化为轻质氧化镁的影响因素以及主要反应的动力学性质。实验确定的最佳条件为固液比1∶15、二氧化碳通入时间90 min、水解温度90℃、水解时间25 min,在此条件下,盐泥中镁的总提取率为75%;采用微分法求得氢氧化镁与二氧化碳反应的反应级数和活化能分别为1.7和68.1 kJ/mol。 |
|
其他语种文摘
|
Magnesium in salt mud was extracted by carbon dioxide method. The factors affecting its transformation into light magnesium oxide and the main reaction kinetics were studied. The optimum conditions are as follows:solid-liquid ratio 1∶15,carbon dioxide aeration time 90 min,hydrolysis temperature 90 ℃,hydrolysis time 25 min. Under these conditions,the total magnesium extraction rate is 75%. The reaction order and activation energy of the reaction between magnesium hydroxide and carbon dioxide are obtained by differentiation method,which are 1.7 and 68.12 kJ/mol respectively. |
|
来源
|
化工环保
,2013,33(2):144-148 【扩展库】
|
|
关键词
|
盐泥
;
轻质氧化镁
;
二氧化碳
;
综合利用
|
|
地址
|
1.
中国科学院新疆理化技术研究所, 新疆, 乌鲁木齐, 830011
2.
天辰化工有限公司, 新疆, 石河子, 832000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1006-1878 |
|
学科
|
化学工业 |
|
基金
|
中国科学院院地合作专项基金资助项目
|
|
文献收藏号
|
CSCD:4817935
|
参考文献 共
14
共1页
|
|
1.
文震. 废盐泥去除卤水中硫酸根新工艺的研究.
海湖盐与化工,2002,31(6):12-14
|
被引
2
次
|
|
|
|
|
2.
王敏. 利用盐泥制取七水硫酸镁.
苏盐科技,2003(2):1
|
被引
3
次
|
|
|
|
|
3.
于明. 盐泥中硫酸钡提取利用.
上海氯碱化工,2003(6):18-19
|
被引
2
次
|
|
|
|
|
4.
胡云霞. 制碱废渣盐泥的综合开发利用.
化工进展,1997(6):64-66
|
被引
1
次
|
|
|
|
|
5.
Ouyang Chenxin. VC and Cr_3C_2 doped WC-MgO compacts prepared by hot-pressing sintering.
Mater Design,2012,40:550-555
|
被引
3
次
|
|
|
|
|
6.
郝福兰. 原位改性纳米氧化镁/顺丁橡胶复合材料的制备与性能.
合成橡胶工业,2012,35(1):22-25
|
被引
1
次
|
|
|
|
|
7.
Tai C Y. Synthesis of magnesium hydroxide and oxide nanoparticles using spinning disc reactor.
Ind Eng Chem Res,2007,46:5536-5541
|
被引
10
次
|
|
|
|
|
8.
天津化工研究设计院.
HG/T 2573-2006工业轻质氧化镁,2007
|
被引
1
次
|
|
|
|
|
9.
刘宝树. 碳酸氢镁溶液增浓的研究.
无机盐工业,2010,42(1):25-26
|
被引
2
次
|
|
|
|
|
10.
Schaef H T. Brucite[Mg(OH)_2] carbonation in wet supercritical CO_2: An in situ high pressure X-ray diffraction study.
Geochim Cosmochim Acta,2011,75(23):7458-7471
|
被引
2
次
|
|
|
|
|
11.
Hopkinson L. Phase transitions in the system MgO-CO_2-H_2O during CO_2 degassing of Mg-bearing solutions.
Geochim Cosmochim Acta,2012,76:1-13
|
被引
3
次
|
|
|
|
|
12.
吕瑞东.
物理化学.(4版),1999:301-304
|
被引
1
次
|
|
|
|
|
13.
Gunawidjaja P N. Quantifying apatite formation and cation leaching from mesoporous bioactive glasses in vitro:A SEM, solid-state NMR and powder XRD study.
J Mater Chem,2012,22:7214-7223
|
被引
1
次
|
|
|
|
|
14.
Zhang Yi. Quantitative XRD analysis of hydrothermally-derived leucite content in dental procelain ceramics.
J Ceram Soc Jap,2007,114(5):329-332
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问