CL60车轮材料表面激光离散熔凝的滚动磨损形貌
Rolling Wear Properties of CL60 Steel after Pulsed Nd∶YAG Laser Surface Melting
查看参考文献17篇
|
文摘
|
针对激光离散熔凝后的CL60材料磨损后的形貌问题,使用MM-P2摩擦磨损试验机对NdYAG激光离散熔凝后的圆环试样进行磨损试验,使用micro XAM三维白光干涉表面形貌仪对磨损试验前后的试样表面进行测量。使用金相显微镜和扫描电镜研究磨损试验后的试样金相。结果表明,经过激光离散熔凝的点硬度高,在磨损过程中形成凸起;熔凝点可以有效阻止试样表面塑性变形的积累,提高材料整体的抗塑性变形能力,减小试样表面由于塑性变形而产生的层片状剥落,表现出较高的耐磨性;不同螺距点距的熔凝点分布可以形成不同的磨损后表面形貌。 |
|
其他语种文摘
|
Laser surface melting is carried out using a pulsed NdYAG laser on specimens made of CL60 steel, after that the rolling wear properties of specimens are studied using a MM-P2 rolling friction and wear test machine. The surface topography of the specimens before and after the rolling wear test is measured by a micro XAM 3D surface topography instrument. Metallographic examinations of the specimens are taken out after the rolling wear test using metallographic microscope and scanning electron microscope. It turns out that the laser melted spots stand out during the experiments due to its higher hardness. The laser melted spots are not only reducing the plastic deformation themselves, but also hindering the plastic deformation of vicinity base material on the same circle. The laser melted spots can reduce the scraps peeling off from specimens and the rolling wear resistance is improved. Different distributions of laser melted spots can form different surface topographies after wear. |
|
来源
|
中国激光
,2013,40(3):0303006-1-0303006-8 【核心库】
|
|
关键词
|
激光技术
;
CL60
;
激光离散熔凝
;
磨损
;
表面形貌
|
|
地址
|
1.
中国科学院力学研究所, 北京, 100190
2.
青岛四方机车车辆股份有限公司, 高速列车系统集成国家工程实验室, 山东, 青岛, 266111
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0258-7025 |
|
学科
|
金属学与金属工艺;电子技术、通信技术 |
|
基金
|
国家科技支撑计划项目
|
|
文献收藏号
|
CSCD:4801457
|
参考文献 共
17
共1页
|
|
1.
Xue L. Dot matrix hardening of steels using a fiber optic coupled pulsed NdYAG laser.
Materials and Manufacturing Processes,1999,14(1):53-65
|
被引
3
次
|
|
|
|
|
2.
Yilbas B S. Nano-second pulse laser treatment of Incoloy 800HT alloy-corrosion properties.
Optics and Lasers in Engineering,1999,32(2):157-172
|
被引
1
次
|
|
|
|
|
3.
钟如涛. 连续/脉冲CO_2激光熔覆高温合金K403.
中国激光,2010,37(3):852-857
|
被引
14
次
|
|
|
|
|
4.
Gadag S P. Dry sliding wear and friction: laser-treated ductile iron.
Wear,1994,173(1/2):21-29
|
被引
2
次
|
|
|
|
|
5.
Yares'ko S I. The influence of the composition of cobalt phase of hard alloys on tool wear upon laser hardening.
Russian Journal of Non-Ferrous Metals,2009,50(5):556-562
|
被引
1
次
|
|
|
|
|
6.
Kusiski J. Microstructure, chemical composition and properties of the surface layer of M2 steel after laser melting under different conditions.
Applied Surface Science,1995,86(1/4):317-322
|
被引
6
次
|
|
|
|
|
7.
Kamachi Mudali U. Effects of laser surface melting on the pitting resistance of sensitized nitrogen-bearing type 316 L stainless steel.
Materials Engineering and Performance,1996,5(1):124-128
|
被引
1
次
|
|
|
|
|
8.
黄开金. 薄板012Al模具钢脉冲NdYAG激光熔凝的研究.
中国机械工程,2006,17(S1):327-330
|
被引
1
次
|
|
|
|
|
9.
占剑. 脉冲YAG激光波形对缸套内壁激光刻蚀微坑形貌的影响.
中国激光,2011,38(6):0603032
|
被引
2
次
|
|
|
|
|
10.
李美艳. 激光熔凝处理高铬钢的高温磨损性能.
中国激光,2010,37(1):302-306
|
被引
4
次
|
|
|
|
|
11.
Shen Lian. Effect of laser melting processing on the microstructure and wear resistance of gray cast iron.
Wear,1991,147(1):195-206
|
被引
3
次
|
|
|
|
|
12.
Blau Peter J. Mechanisms for transitional friction and wear behavior of sliding metals.
Wear,1981,72(1):55-66
|
被引
5
次
|
|
|
|
|
13.
王爱琴. 表面感应淬火对45钢滚动磨损特性的影响.
材料热处理学报,2007,28(1):127-129
|
被引
11
次
|
|
|
|
|
14.
Colaco R. On the influence of retained austenite in the abrasive wear behaviour of a laser surface melted tool steel.
Wear,2005,258(1/4):225-231
|
被引
12
次
|
|
|
|
|
15.
张庆茂. 激光熔凝层组织与摩擦学特性的研究.
强激光与粒子束,2006,18(3):389-392
|
被引
11
次
|
|
|
|
|
16.
孙浩. 扫描间距对45钢激光熔凝强化组织性能的影响.
农业工程学报,2011,27(2):156-160
|
被引
11
次
|
|
|
|
|
17.
徐秉业(译).
接触力学,1992:56-59
|
被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问