应变速率对X80管线钢应力腐蚀的影响
Effect of Strain Rate on Stress Corrosion Cracking of X80 Pipeline Steel

查看参考文献19篇

程远 1   俞宏英 2   王莹 1   孟旭 1   孙冬柏 1  
文摘 利用慢应变速率拉伸试验研究了应变速率对X80管线钢在土壤模拟溶液中的应力腐蚀的影响。采用的模拟溶液以我国西北部碱性土壤的化学成分为基础,在不同应变速率条件下进行试验。样品断裂后利用扫描电镜对断口形貌以及断口侧面二次裂纹进行观察。研究结果表明:X80钢在1.0×10~(-6)s~(-1)应变速率下表现出最高的应力腐蚀敏感性。低于该应变速率下,应力腐蚀敏感性略有降低;而高于该应变速率下,应力腐蚀敏感性明显减小。不同应变速率下应力腐蚀敏感性的差异主要是由应力腐蚀过程中腐蚀和力学作用的影响程度不同造成。应变速率低于1.0×10~(-6)s~(-1)时,腐蚀作用影响更大,较长的腐蚀时间造成裂纹被腐蚀,裂纹扩展受到影响,因此应力腐蚀敏感性略有降低。当应变速率高于1.0×10~(-6)s~(-1)时,力学作用主导整个过程,形成的裂纹没有受到足够腐蚀的情况下,在力学作用下发生快速机械扩展、断裂,因此产生了明显降低的应力腐蚀行为。
其他语种文摘 Stress corrosion cracking susceptibility of X80 pipeline steel was investigated in a simulated soil solution using slow strain rate tensile (SSRT) tests. The simulated soil solution was based on the chemical compositions of alkaline Gansu soil in northwest of China. The tests were conducted at different strain rates. The fracture surfaces and secondary cracks were observed using scanning electron microscopy (SEM). The results showed that strain rates had an important role on SCC of X80 steel in simulated soil solutions. Corrosion and mechanical factors have different influences during the SCC processes at different strain rates, which results in the variety of SCC. There was the highest SCC susceptibility at the strain rate of 1.0×10~(-6)s~(-1). Combined effect of corrosion and mechanics leads to high SCC susceptibility. When the strain rates were lower than 1.0×10~(-6)s~(-1), enough long corrosion time results in the corrosion of crack in this strain rate range. The crack propagation is restrained. Thus, slight decrease of SCC susceptibilities occurs. As the strain rates were higher than 1.0×10~(-6) s~(-1), SCC susceptibilities were low obviously. In this high strain rates range, the mechanical factors have more effect on SCC than corrosion factors, which mainly lead to mechanical fracture of specimens.
来源 材料工程 ,2013(3):77-82 【核心库】
DOI 10.3969/j.issn.1001-4381.2013.03.015
关键词 X80管线钢 ; 应力腐蚀 ; 慢应变速率拉伸 ; 应变速率
地址

1. 北京科技大学, 国家材料服役安全科学中心, 北京, 100083  

2. 北京科技大学腐蚀与防护中心表面科学与技术研究所, 北京, 100083

语种 中文
文献类型 研究性论文
ISSN 1001-4381
学科 金属学与金属工艺
基金 中国石油天然气股份有限公司科技开发项目
文献收藏号 CSCD:4774837

参考文献 共 19 共1页

1.  黄志潜. 国外输气管道技术的发展现状和几点建议. 焊管,2000,23(3):1-20 被引 5 次    
2.  黄志潜. X80级管线钢在高压大流量输气管道上的应用与发展前景. 焊管,2005,28(3):1-10 被引 8 次    
3.  庄传晶. 国内X80级管线钢的发展及今后的研究方向. 焊管,2005,28(2):10-14 被引 33 次    
4.  Fang B Y. Review of stress corrosion cracking of pipeline steels in "low" and "high" pH solutions. Journal of Material Science,2003,38(1):127-132 被引 19 次    
5.  Manfredi C. Failures by SCC in buried pipelines. Engineering Failure Analysis,2002,9(5):495-509 被引 19 次    
6.  Kentish P J. Gas pipeline failures: Australian experience. Corrosion,1985,20(3):139-146 被引 6 次    
7.  Cheng Y F. Fundamentals of hydrogen evolution reaction and its implications on near-neutral pH stress corrosion cracking of pipelines. Electrochimica Acta,2007,52(7):2661-2667 被引 12 次    
8.  Gu B. Transgranular stress corrosion cracking of X-80 and X-52 pipeline steels in dilute aqueous solution with near-neutral pH. Corrosion,1999,55(3):312-318 被引 18 次    
9.  方丙炎. 埋地管道在近中性pH和高pH环境中的应力腐蚀开裂. 金属学报,2001,37(5):453-458 被引 25 次    
10.  Zhou J L. Anodic electrochemical behavior of X80 pipeline steel in NaHCO_3 solution. Acta Metallurgica Sinica,2010,46(2):251-256 被引 3 次    
11.  Gu B. Hydrogen-facilitated anodic dissolution-type stress corrosion cracking of pipeline steels in near-neutral pH solution. Corrosion,1999,55(1):96-106 被引 30 次    
12.  Wang J Q. SCC initiation for X65 pipeline steel in the high pH carbonate/bicarbonate solution. Corrosion Science,2003,45(10):2199-2217 被引 25 次    
13.  Asahi H. Role of microstructures on stress corrosion cracking of pipeline steels in carbonate-bicarbonate solution. Corrosion,1999,55(7):644-652 被引 6 次    
14.  Liang P. Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution. International Journal of Minerals, Metallurgy and Materials,2009,16(4):407-413 被引 19 次    
15.  Zhang L. Effect of applied potentials on stress corrosion cracking of X70 pipeline steel in alkali solution. Materials and Design,2009,30(6):2259-2263 被引 11 次    
16.  Liu Z Y. Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment. Journal of University of Science and Technology Beijing, Mineral,Metallurgy, Material,2008,15(6):707-713 被引 9 次    
17.  Liang P. Stress corrosion cracking of X80 pipeline steel in simulated alkaline soil solution. Materials and Design,2009,30(5):1712-1717 被引 38 次    
18.  张亮. 应变速率对管线钢在碱性溶液中应力腐蚀行为的影响. 钢铁研究学报,2009,21(10):55-59 被引 3 次    
19.  孙齐磊. 应变速率对X70管线钢应力腐蚀行为的影响. 钢铁研究学报,2009,21(9):51-55 被引 4 次    
引证文献 15 篇

1 黄本生 热处理对X80管线钢在模拟海水中应力腐蚀的影响 金属热处理,2014,39(8):109-112
被引 4 次

2 周峰 超快冷工艺对高铌X80管线钢抗腐蚀性能的影响 材料工程,2015,43(2):67-72
被引 0 次

显示所有15篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号