通过宏观形貌观察、化学成分分析、扫描电镜及EDS能谱分析等手段,分析了某企业车间屋顶Q235彩钢板腐蚀失效的原因,并给出了改进措施。结果表明:屋顶彩钢板的严重腐蚀是高温气流及氧和硫腐蚀共同作用的结果,车间屋顶局部环境中超高浓度的S02是腐蚀速率增大的主要原因;建议在彩钢板表面喷涂防锈漆或聚脲材料,改进生产工艺和流程,做好定期检验和在线检查工作。 |
|
其他语种文摘
|
Through macro morphology observation, chemical composition analysis, scanning electron microscopy and energy dispersive spectroscopy, the reasons for corrosion of the colored plate of Q235 as an enterprise's workshop were analyzed, and the improved measures were also put forward. The results indicated that serious corrosion of the colored plate was due to a joint action of high temperature air, oxygen corrosion, and sulfur corrosion. The high concentration of sulfur dioxide in the of workshop roof was the main reason for the increased corrosion rate. It is suggested to spray antirust paint or polyurea material on the color steel surface, improve production process and do regular check and online inspection. |
|
来源
|
机械工程材料
,2012,36(12):101-104 【核心库】
|
|
关键词
|
彩钢板
;
高温气流
;
二氧化硫
;
腐蚀
;
失效分析
|
|
地址
|
1.
山东省科学院分析测试中心材料失效与安全评估工程技术中心, 济南, 250014
2.
中国科学院金属研究所, 沈阳, 110016
|
|
语种
|
中文 |
|
ISSN
|
1000-3738 |
|
学科
|
金属学与金属工艺 |
|
基金
|
山东省科学院科技发展基金项目
|
|
文献收藏号
|
CSCD:4730017
|
|
|
1.
龚嶷. 循环流化床锅炉返料阀门盖腐蚀失效分析.
金属热处理,2008,33(12):89-92
|
被引
2
次
|
|
|
|
|
2.
.
GB 3095-1996环境空气质量标准
|
被引
14
次
|
|
|
|
|
3.
丛树林. 延迟焦化装置中换热器管腐蚀失效分析.
机械工程材料,2008,32(9):79-81
|
被引
2
次
|
|
|
|
|
4.
贺红梅. 火电厂水冷壁管腐蚀失效常见形式简介.
理化检验-物理分册,2005,41(6):301-303
|
被引
3
次
|
|
|
|
|
5.
汪川. Q235钢在潮湿SO_2环境中的初期腐蚀锈层的表征.
科学通报,2008,53(23):2833-2838
|
被引
3
次
|
|
|
|
|
6.
黄微波. 喷涂聚脲技术在彩钢屋面快速修复中的应用.
施工技术,2011,40(7):93-94
|
被引
1
次
|
|
|
|
|
7.
陈兵. 水冷器腐蚀失效原因分析.
腐蚀科学与防护技术,2010,22(6):547-550
|
被引
4
次
|
|
|
了解气象卫星更多信息，请访问