异氰酸酯/环氧树脂的固化机理
Curing mechanism of isocyanate/epoxy resin
查看参考文献22篇
|
文摘
|
详细研究了异氰酸酯/环氧树脂体系的固化反应和固化机理。采用差示扫描量热法(DSC)和红外光谱法(FTIR)跟踪了异氰酸酯/环氧树脂固化反应过程,定量分析了异氰酸酯、环氧基团和新生成的异氰脲酸酯和唑烷酮的变化。DSC分析结果表明,DSC曲线上出现3个放热峰,说明固化过程中存在至少3种反应;FTIR分析结果表明,在140℃以下固化体系主要发生异氰酸酯的三聚反应生成三嗪环(异氰脲酸酯);在200℃下,异氰酸酯—NCO基团与环氧基团开环反应生成唑烷酮;在230℃下,三嗪环(异氰脲酸酯)进一步与环氧基团开环反应生成唑烷酮。研究了不同温度下环氧基团、异氰酸酯基团、异氰脲酸酯基团、唑烷酮基团随反应时间的变化规律。 |
|
其他语种文摘
|
The curing reaction of bisphenol A epoxy resin and isocyanate was carried out and the curing mechanism was investigated.Differential scanning calorimetry(DSC)and Fourier transform infrared spectroscopy(FTIR)were used to monitor and analyze quantitatively the decrease of the groups of isocyanate,epoxy group and generation of new groups of isocyanurate and oxazolidone.The DSC results showed that three reactions mainly occurred during the curing process of epoxy/isocyanate system corresponding to three exothermic peaks.The FTIR results indicated that when reaction temperature was below 140℃ trimerization of isocyanate groups into isocyanurate was observed;when temperature was up to 200℃ the formation of oxazolidone ring by the reaction between epoxy and isocyanate occurred;when temperature was above 230℃ the transformation reaction of isocyanurate with epoxide group to oxazolidone occurred.The curing reaction time dependence of the conversions of epoxide,isocyanate,isocyanurate,oxazolidone groups at different temperature were studied. |
|
来源
|
化工学报
,2012,63(8):2629-2634 【核心库】
|
|
DOI
|
10.3969/j.issn.0438-1157.2012.08.041
|
|
关键词
|
异氰酸酯
;
环氧树脂
;
异氰脲酸酯
;
唑烷酮
;
固化机理
|
|
地址
|
1.
北京化工大学, 碳纤维及功能高分子教育部重点实验室, 北京, 100029
2.
北京化工大学常州先进材料研究院, 江苏, 常州, 213164
|
|
语种
|
中文 |
|
ISSN
|
0438-1157 |
|
学科
|
化学工业 |
|
基金
|
常州微电子化学材料公共工业技术平台项目
;
江苏省科技支撑项目
;
国家863计划
;
国家自然科学基金项目
|
|
文献收藏号
|
CSCD:4594061
|
参考文献 共
22
共2页
|
|
1.
陈平.
环氧树脂,1999:1-10
|
被引
10
次
|
|
|
|
|
2.
黄丽. 环氧树脂/氰酸酯共固化体系热性能的研究.
北京化工大学学报:自然科学版,2007,34(2):164-168
|
被引
4
次
|
|
|
|
|
3.
林秀英. Study on poly (isocyanurate oxazolidone) adhesive.
热固性树脂,1992,4:11
|
被引
1
次
|
|
|
|
|
4.
Kordomenos P I. Thermal stability of isocyanate-based polymers (1): Kinetics of the thermal dissociation of urethane, oxazolidone, and isocyanurate groups.
Macromolecules,1981,14:1434-1437
|
被引
1
次
|
|
|
|
|
5.
Sendijarevic V. Novel isocyanate-based matrix resins for high temperature composite applications.
Polymer Composites,1996,17(2):180
|
被引
1
次
|
|
|
|
|
6.
Yeganeneh H. Synthesis, characterization and properties of novel thermally stable poly (urethane-oxazolidone) elastomers.
European Polymer Journal,2006,42:1743-1754
|
被引
9
次
|
|
|
|
|
7.
Chattopadhyay D K. Thermal stability and flame retardancy of polyurethanes.
Progress in Polymer Science,2009,34:1068-1133
|
被引
104
次
|
|
|
|
|
8.
Speranza G. Preparation of substituted 2-oxazolidones from 1, 2-epoxides and isocyanates.
Journal of Organic Chemistry,1958,23:1922
|
被引
3
次
|
|
|
|
|
9.
Sandler S R. Ploy-2-oxazolidones.
Journal of Applied Polymer Science,1965,9:1994
|
被引
3
次
|
|
|
|
|
10.
Marline J D. Ploy (urethane-oxazolidone): synthesis, characterization and shape memory properties.
European Polymer Journal,2007,43:3629-3637
|
被引
1
次
|
|
|
|
|
11.
Chian K S. Synthesis and characterization of an isocyanurate-oxazolidone polymer:effect of stoichimetry.
Journal of Applied Polymer Science,2001,82:879-888
|
被引
6
次
|
|
|
|
|
12.
赵宝宗. 聚（异氰脲酸酯-恶唑烷酮）合成反应的研究.
高分子学报,1993(1):66-74
|
被引
2
次
|
|
|
|
|
13.
赵宝宗. Studies on the syntheses, properties and application of polyisocyanurate-oxazolidones.
热固性树脂,1990(4):14
|
被引
1
次
|
|
|
|
|
14.
孙以实. Study on toughening of ploy (isocyanuric ester-oxazolidone).
热固性树脂,1992(2):5
|
被引
6
次
|
|
|
|
|
15.
赵宝宗. Study on structures and properties of polyisocyanurate-oxazolidones.
热固性树脂,1992(1):11
|
被引
1
次
|
|
|
|
|
16.
包建文. Study on copolymerization of epoxy/isocyanate resin.
热固性树脂,1999(3):6-9
|
被引
1
次
|
|
|
|
|
17.
亢茂青. Lewis酸／碱络合催化剂对恶唑烷酮合成的研究.
高分子材料科学与工程,1999,15(3):64
|
被引
4
次
|
|
|
|
|
18.
Kordomenos P I. Thermal stability of isocyanate-based polymers (2): Kinetics of the thermal dissociation of model urethane, oxazolidone, and isocyanurate block copolymers.
Macromolecules,1987,20:2077-2083
|
被引
7
次
|
|
|
|
|
19.
Okumoto S. A computational study of base-catalyzed reactions between isocyanates and epoxides affording 2-oxazolidones and isocyanurates.
Journal of Computational Chemistry,2001,22:316-326
|
被引
1
次
|
|
|
|
|
20.
李文峰. Study on novolac cyanate ester co-cured with epoxy E-51.
高分子学报,2006,6:804-809
|
被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问