Structure and mechanical properties of aluminum alloy/Ag interlayer/steel non-centered electron beam welded joints
铝合金/Ag中间层/钢的电子束偏束焊接头组织与性能
查看参考文献15篇
|
文摘
|
Electron beam welding was carried out between aluminum alloy and steel with Ag interlayer. Seam morphology, structure and mechanical properties of the joints were investigated with different action positions of the electron beam spot. The results show that with the increment of the beam offset to the silver side from the interface between silver and steel, the seam morphology was improved, and the porosity in the Ag interlayer vanished. A transition layer mainly composed of Ag_2Al and Al eutectic was formed at the interface between silver and aluminum, and became thin and spiccato as the beam offset increased. When the beam offset was too large, two IMC layers composed of FeAl and FeAl_3 respectively were formed at the interface between steel and Ag interlayer. The optimal beam offset was 0.2 mm, and the maximum tensile strength of the joint was 193 MPa, 88.9% that of the aluminum alloy, and the fracture occurred at the interface between steel and Ag interlayer. |
|
其他语种文摘
|
在铝合金与钢之间添加Ag中间层后进行电子束焊接实验。其他参数固定的情况下,对电子束作用位置不同时的焊缝成形、接头组织和力学性能进行分析。结果表明:随着电子束斑点从银-钢对接面向银侧偏移距离的增大,焊缝成形明显得到改善,接头中的气孔缺陷消失。在银-铝对接面形成由Ag_2Al和Al共晶组成的过渡层,过渡层随着偏束距离的增大而变窄且不连续。当偏束距离过大时,在银-钢界面上形成FeAl和FeAl_3两种化合物层。当电子束最佳偏束距离为0.2mm时,接头强度最高达193MPa,为铝母材的88.9%,此时断裂发生在银-钢界面上。 |
|
来源
|
Transactions of Nonferrous Metals Society of China
,2011,21(12):2592-2596 【核心库】
|
|
DOI
|
10.1016/s1003-6326(11)61096-0
|
|
关键词
|
aluminum alloy
;
steel
;
Ag interlayer
;
non-centered electron beam welding
;
joint
|
|
地址
|
1.
Harbin Institute of Technology, State Key Laboratory of Advanced Welding and Joining, Harbin, 150001
2.
AVIC Shenyang Aircraft Corporation, Shenyang, 110034
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1003-6326 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
;
国家自然科学基金
|
|
文献收藏号
|
CSCD:4426212
|
参考文献 共
15
共1页
|
|
1.
Haraga K. Strength properties of aluminum/aluminum and aluminum/steel joints for light weighing of automotive body.
Welding in the World,2000,44(4):23-27
|
被引
15
次
|
|
|
|
|
2.
Schubert E. Light weight structures produced by laser beam joining for future applications in automobile and aerospace industry.
Journal of Materials Processing Technology,2001,115(1):2-8
|
被引
78
次
|
|
|
|
|
3.
Li H. Interlayer design and its effect on the liquid diffusion of steel-Al honeycomb sandwich panels.
Journal of University of Science and Technology Beijing,2006,28(2):138-143
|
被引
1
次
|
|
|
|
|
4.
Geiger M. Friction stir knead welding of steel aluminum butt joints.
International Journal of Machine Tools and Manufacture,2008,48(5):515-521
|
被引
1
次
|
|
|
|
|
5.
Watanabe T. Joining of aluminum alloy to steel by friction stir welding.
Journal of Materials Processing Technology,2006,178:342-349
|
被引
21
次
|
|
|
|
|
6.
Uzun H. Friction stir welding of dissimilar Al 6013-T4 to X5CrNi18-10 stainless steel.
Materials and Design,2005,26(1):41-46
|
被引
30
次
|
|
|
|
|
7.
Yokoyama T. Impact tensile properties of 6061 aluminum alloy to SUS 304 stainless steel friction-welded butt joints.
Welding International,2003,17(7):514-523
|
被引
4
次
|
|
|
|
|
8.
Liu P. Vacuum brazing technology and microstructure near the interface of Al/18-8 stainless steel.
Materials Research Bulletion,2003,38(9/10):1493-1499
|
被引
6
次
|
|
|
|
|
9.
Mathieu A. Laser brazing of a steel/aluminum assembly with hot filler wire (88% Al, 12% Si).
Materials Science and Engineering A,2006,435/436:19-28
|
被引
25
次
|
|
|
|
|
10.
He P. Resolve of fragile and reaction defect problem for a new contact reaction brazing aluminum to stainless steel.
Materials Science & Technology,2005,13(1):82-85
|
被引
1
次
|
|
|
|
|
11.
Lu X Q. The process and principle analysis of Ni/Cu transitional layer brazing of Al (Al alloys) and stainless steel.
Materials for Mechanical Engineering,2004,28(1):23-25
|
被引
1
次
|
|
|
|
|
12.
Zhang H T. Interfacial microstructure and mechanical properties of aluminum-zinc-coated steel joints made by a modified metal inert gas welding-brazing process.
Materials Characterization,2007,58(7):588-592
|
被引
22
次
|
|
|
|
|
13.
Song J L. Spreading behavior and microstructure characteristics of dissimilar metals TIG welding-brazing of aluminum alloy to stainless steel.
Materials Science and Engineering A,2009,509(1/2):31-40
|
被引
22
次
|
|
|
|
|
14.
Lei Z. Fusion-brazing welding for dissimilar metals between aluminum and steel by Nd:YAG laser-MIG hybrid welding.
Welding,2006,6:36-37
|
被引
1
次
|
|
|
|
|
15.
Lei Z. Fusion-brazing joining for dissimilar metals between 5A02 aluminum alloy and zinc-coated steel based on laser-MIG hybrid welding.
Journal of Mechanical Engineering,2009,45(3):94-98
|
被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问