藏药南寒水石热制炮制工艺研究
Study on processing technics of Tibetan medicine Nanhanshuishi
查看参考文献8篇
文摘
|
目的:探讨藏药南寒水石的热制最佳炮制工艺. 方法:通过文献、典籍记载的查阅及实地走访各藏医院调查了解, 对南寒水石热制炮制方法进行归纳总结. 据此确定各单因素实验条件并进行正交试验, 对不同炮制条件下所得南寒石炮制品中钙(Ca), 铁(Fe), 锰(Mn), 锌(Zn), 铜(Cu)元素含量进行测定. 结果:粒径10~20 mm, 生草乌与火硝比例1:2, 煮沸3 h为南寒水石最佳炮制条件. 结论:本实验为研究南寒水石热制炮制机制及制定最佳炮制工艺奠定基础 |
其他语种文摘
|
Objective: To study the heat processing technics of Nanhanshuishi. Method: To find the best processing technic, the single factor experiments and orthogonal experiments were designed basing on the processing technics summarized by consulting documents, scriptures and investigating some Tibetan hospitals, meanwhile, the content of Ca, Fe, Mn, Zn, and Cu in the processed Nanhanshuishi in single factor experiments and orthogonal experiments were detected. Result: The best processing technic of Nanhanshuishi was as follows: Nanhanshuishi was crashed to 10-20 mm in diameter, the ratio of the weight of Aconiti Kusnezoffii Radix and potassium nitrate was 1:2, and the boiling time was 3 h. Conclusion: The work in this article provided a basic processing technic data for clarifying the mechanism of processing and establishing the perfect processing technics of Nanhanshuishi |
来源
|
中国中药杂志
,2011,36(6):683-686 【核心库】
|
DOI
|
10.4268/cjcmm20110605
|
关键词
|
南寒水石
;
炮制
;
微量元素
;
正交试验
|
地址
|
中国科学院西北高原生物研究所藏药现代化研究中心, 青海省藏药药理学与安全性评价研究重点实验室, 青海, 西宁, 810008
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
1001-5302 |
学科
|
中国医学 |
基金
|
国家重大科技专项
;
国家“十一五”科技支撑计划项目
|
文献收藏号
|
CSCD:4185830
|
参考文献 共
8
共1页
|
1.
罗达尚.
中华藏本草,1997:8
|
被引
1
次
|
|
|
|
2.
国家中医药管理局中华本草编委会.
中华本草.藏药卷,2002:32
|
被引
1
次
|
|
|
|
3.
青海省药品检验所.
中国藏药.第3卷,1996:191
|
被引
1
次
|
|
|
|
4.
罗达尚.
新修晶珠本草,2004:78
|
被引
2
次
|
|
|
|
5.
王琰. 微量元素与胃癌关系的研究.
北华大学学报,2005,6(1):53
|
被引
3
次
|
|
|
|
6.
门子荣. 不同胃病患者血清、胃液、胃粘膜锌含量的测定.
基础医学与临床,1997,17(23):204
|
被引
1
次
|
|
|
|
7.
杨平. 胃癌及胃炎患者血清中微量元素变化的探讨.
现代医药卫生,2007,1(23):26
|
被引
1
次
|
|
|
|
8.
何雪芬. 慢性胃病胃粘膜cAMP, SOD与上皮细胞线粒体超微结构及其微量元素的量变.
江苏医药,1997,23(2):85
|
被引
2
次
|
|
|
|
|