Si掺杂对Mn-Co-Ni系NTC热敏电阻电性能的影响
Eeffect of Si dopng on the electric properties of Mn-Co-Ni type NTC thermistors
查看参考文献10篇
文摘
|
采用传统陶瓷工艺制备了Mn_(1.05-x)Co_(0.92)Ni_(0.03)Si_x0_4(0≤x≤0.05)系列NTC热敏电阻样品, 借用XRD、 SEM和电性能测试等手段, 研究了Si掺杂量对样品相结构和电性能的影响. 结果表明: 当0≤x≤0.03时, 样品为尖晶石立方相和四方相的固溶体, 室温电阻率P25和B_(25/50)值均随着Si掺杂量的增加而增加; 当0.03
|
其他语种文摘
|
Mn_(1.05-x)Co_(0.92)Ni_(0.03)SiO_4 (0≤x≤0.05) series NTC thermistor samples were prepared using the conventional ceramic technique. The effects of Si-doping amount on the phase structure and electric properties of the samples were studied using XRD, SEM and electric property measurements. The results show.that in the range of 0≤x≤0.03, the spinel cubic phase and tetragonal phase co-existed as solid solution in the samples, and the resistivity at room temperature P25 and B_(25/50) value of the sample increased with increasing Si-doping amount. When 0.03<x≤<0.05, the tetragonal phase was absence and only spinel cubic phase existed in the samples, and the B25/50 value and P25 of the sample decreased with increasing Si-doping amount. The obtained sample with x = 0.03 sintered at 1 373 K show optimal electric properties with P25 of 79 501 Ω · cm and B_(25/50) value of 4 142 K |
来源
|
电子元件与材料
,2011,30(3):36-39 【扩展库】
|
关键词
|
NTC
;
热敏电阻
;
Si掺杂
;
尖晶石
;
电性能
|
地址
|
中国科学院新疆理化技术研究所, 新疆电子信息与材料重点实验室, 新疆, 乌鲁木齐, 830011
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
1001-2028 |
学科
|
化学工业 |
基金
|
国家工业和信息化部电子信息产业发展基金
|
文献收藏号
|
CSCD:4145646
|
参考文献 共
10
共1页
|
1.
王恩信. NTC热敏电阻器的现状与发展趋势.
电子元件和材料,1997,16(4):1-8
|
被引
24
次
|
|
|
|
2.
翟继卫. 抑制涌浪电流用NTC热敏电阻器.
电子元件和材料,1996,15(2):33-35
|
被引
7
次
|
|
|
|
3.
李言荣.
电子材料导论,2001:384-388
|
被引
6
次
|
|
|
|
4.
王卫民. NTC热敏电阻材料组成及制备工艺研究进展.
材料科学与工程学报,2005,23(2):286-289
|
被引
11
次
|
|
|
|
5.
PARK K. Effect of SiO2 addition on the electrical stability of (Mn2.1-xNi0.9Si_x)04 (0≤x≤0.18) NTC thermistors.
Mater Lett,2004,58:933-937
|
被引
7
次
|
|
|
|
6.
PARK K. Influence of the composition on the electrical stability of (Mn2.1-xNi0.9Si_x)O4 (0≤x≤0.18) negative temperature coefficient thermistors.
J Mater Sci,2004,15:359-362
|
被引
3
次
|
|
|
|
7.
MEGURO T. Prepapation of Mn-Co-Ni monophase spinel oxide by oxidation of rock salt-type oxide.
J Mater Sci,1992,27:5529-5530
|
被引
1
次
|
|
|
|
8.
王卫民.
Mn--Co-Ni-O基NTC热敏半导体陶瓷的低温烧结和电性能研究,2006
|
被引
1
次
|
|
|
|
9.
PARK K. Electrical properties of Ni-Mn-Co-(Fe) oxide thick-film NTC thermistors prepared by screen printing.
J Mater Sci,2003,14(2):81-87
|
被引
6
次
|
|
|
|
10.
莫以豪.
半导体陶瓷及其敏感元件,1983:177-220
|
被引
10
次
|
|
|
|
|
|