碳钢在90℃、H_2S-HCl-H_2O环境下的腐蚀行为 Ⅰ-H_2S浓度对碳钢腐蚀行为的影响
CORROSION BEHAVIOR OF CARBON STEEL IN H_2S-HCl-H_2O AT 90℃ Ⅰ-The Effect of H_2S Concentration on the Corrosion Behavior of Carbon Steel
查看参考文献28篇
|
文摘
|
在实验室模拟炼油厂常减压塔顶冷凝水系统环境,用腐蚀失重法和电化学测试方法并结合扫描电镜(SEM)和X射线衍射(XRD)分析手段,研究90℃条件下低碳钢在含有不同浓度H_2S的模拟溶液中的腐蚀电化学行为. 结果表明,H_2S强烈地促进碳钢的阴极过程,H_2S浓度升高,阴极过程加剧,腐蚀速率加快;H_2S存在时,电极表面发生严重的局部腐蚀而形成大量腐蚀坑,同时形成一层主要成分为四方硫铁矿的腐蚀产物,硫化物沉积层随H_2S浓度升高而变得疏松、易于破裂和脱落 |
|
其他语种文摘
|
The electrochemical behavior of low carbon steel in acidic simulation solutions containing different concentrations of H_2S at 90℃was investigated by mass loss method, electrochemical measurements and observations of scanning electron microscope(SEM) and X-ray radiation diffaction(XRD).The results showed that the cathodic depolarization was enhanced greatly and the corrosion rate of carbon steel increased remarkably with the increase of H_2S concentration. The severe corrosion holes were observed on the carbon steel surface in the H_2S-containing solutions. The corrosion products layer deposited on carbon steel were mainly composed of mackinawite, which became loose, easily cracked and sloughed off with increasing concentration of H_2S |
|
来源
|
中国腐蚀与防护学报
,2011,31(1):28-33 【核心库】
|
|
关键词
|
碳钢
;
H_2S
;
腐蚀
;
四方硫铁矿
|
|
地址
|
1.
哈尔滨工程大学材料科学与化学工程学院腐蚀与防护实验室, 哈尔滨, 150001
2.
中国石油兰州石油化工公司, 兰州, 730060
3.
哈尔滨工程大学材料科学与化学工程学院腐蚀与防护实验室, 金属腐蚀与防护国家重点实验室, 哈尔滨, 150001
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-4537 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:4136030
|
参考文献 共
28
共2页
|
|
1.
顾望平. 加工进口高硫原油腐蚀环境分析与防护.
石油化工腐蚀与防护,1994,11(2):56-60
|
被引
7
次
|
|
|
|
|
2.
Veloz M A. Electrochemical study of carbon steel corrosion in buffered acetic acid solutions with chlorides and H2S.
Electrochim. Acta,2002,48:135-144
|
被引
28
次
|
|
|
|
|
3.
Aezola S. The effect of H2S concentration on the corrosion behavior of API 5L X-70 steel.
J. Solid State Electrochem,2005,8(4):197-200
|
被引
4
次
|
|
|
|
|
4.
Ma H Y. Theoretical interpretation on impedance spectra for anodic iron dissolution in acidic solutions containing hydrogen sulfide.
Corrosion,1998,54:634-640
|
被引
6
次
|
|
|
|
|
5.
Ma H Y. An ac impedance study of the anodic dissolution of iron in sulfuric acid solutions containing hydrogen sulfide.
J. Electroanal. Chem,1998,451:11-17
|
被引
4
次
|
|
|
|
|
6.
Ma H Y. The influence of hydrogen sulfide on corrosion of iron under different conditions.
Corros. Sci,2000,42:1669-1683
|
被引
36
次
|
|
|
|
|
7.
Cheng X L. Corrosion of iron in acid solutions with hydrogen sulfide.
Corrosion,1998,54:369-376
|
被引
9
次
|
|
|
|
|
8.
Cheng X L. Electrochemical behavior of chromium in acid solutions with H2S.
Corros. Sci,1999,41:773-788
|
被引
2
次
|
|
|
|
|
9.
Cheng X L. Corrosion of nickel in acid solutions with hydrogen sulphide.
Corros. Sci,2000,42:299-311
|
被引
3
次
|
|
|
|
|
10.
Choi Y S. Aqueous corrosion behavior of weathering steel and carbon steel in acid-chloride environments.
Corrosion,2000,56:1202-1210
|
被引
7
次
|
|
|
|
|
11.
Huang H H. Cracking characteristics of A516 steel weldment in H2S containing environments.
Mater. Sci. Eng.A,1994,188(1/2):219-227
|
被引
2
次
|
|
|
|
|
12.
Huang H H. Effect of H2S on the electrochemical behavior of steel weld in acidic chloride solutions.
Mater. Chem. Phys,1999,58(2):177-181
|
被引
6
次
|
|
|
|
|
13.
Huang H H. Electrochemical behavior of the simulated heat-affected zone of A516 carbon steel in H2S solution.
Electrochim. Acta,1996,41(7/8):1191-1199
|
被引
10
次
|
|
|
|
|
14.
Vedage H. Electrochemical growth of iron sulfide films in H2S-saturated chloride media.
Corrosion,1993,49(2):114-121
|
被引
17
次
|
|
|
|
|
15.
Rehan H H. Effect of sulfide ions on the corrosion behavior of mild steel in acetate buffer.
Collect. Czech. Chem. Commun,1993,58:547-554
|
被引
2
次
|
|
|
|
|
16.
Liu J. Study of cavitation corrosion behaviors and mechanism of carbon steel in neutral sodium chloride aqueous solution.
Corrosion,2005,61(11):1061-1069
|
被引
2
次
|
|
|
|
|
17.
Doche M L. Influence of ultrasound power and frequency upon corrosion kinetics of zinc in saline media.
Ultrason. Sonochem,2003,10:357-362
|
被引
2
次
|
|
|
|
|
18.
曹楚南.
腐蚀电化学,1994:104
|
被引
4
次
|
|
|
|
|
19.
Shoesmith D W. The formation of ferrous monosulfide polymorphs during the corrosion of iron by aqueous hydrogen sulfide at 21 ℃.
J. Electrochem. Soc,1980,127:1007-1015
|
被引
14
次
|
|
|
|
|
20.
Uhlig H H.
Corrosion and Corrosion Control(3rd),1991:120
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问