Hot deformation behavior of Mg-7.22Gd-4.84Y-1.26Nd-0.58Zr magnesium alloy

查看参考文献20篇

文摘 The behavior evolvement of Mg-7.22Gd-4.84Y-1.26Nd-0.58Zr (GWN751K) magnesium alloy during the hot deformation process was discussed. The flow stress behavior of the magnesium alloy over the strain rate range of 0.002 to 2.000 s~(-1) and in the temperature range of 623 to 773 K was studied on a Gleeble-1500D hot simulator under the maximum deformation degree of 60%. The experimental results showed that the relationship between stress and strain was obviously affected by strain rate and deformation temperature. The flow stress of GWN751K magnesium alloy during high temperature deformation could be represented by the Zener-Hollomon parameter in the hyperbolic Arrhenius-type equation. The stress exponent n and deformation activation energy Q were evaluated by linear regression analysis. The stress exponent n was fitted to be 3.16. The hot deformation activation energy of the alloy during hot deformation was 230.03 kJ/mol. The microstructures of hot deformation were also influenced by strain rate and compression temperature strongly. It was found that the alloy could be extruded at 723 K with the mechanical properties of σ0.2 = 260 MPa, σb = 320 MPa, and δ = 18%
来源 Rare Metals ,2011,30(1):87-93 【核心库】
DOI 10.1007/s12598-011-0203-y
关键词 magnesium alloys ; rare earth elements ; microstructure ; activation energy ; deformation ; hot working
地址

1. General Research Institute for Nonferrous Metals, State Key Lab of Non-ferrous Metals and Processes, Beijing, 100088  

2. CNGC Shenyang Dong Ji Industries Group Corporation, Shenyang, 110045

语种 英文
文献类型 研究性论文
ISSN 1001-0521
学科 金属学与金属工艺
基金 国家973计划
文献收藏号 CSCD:4121547

参考文献 共 20 共1页

1.  Chang JW. Effect of heat treatment on corrosion and electrochemical behavior. Electrochim. Acta,2007,52:3160 被引 43    
2.  Xu H. Magnesium Alloy Fabrication and Processing Technology,2007:2 被引 1    
3.  Cahn RW. Materials Science and Technology: Structure and Properties of Nonferrous Alloys, Vol. 8,1999:109 被引 1    
4.  Roklin LL. Magnesium Alloy Containing Rare-Earth Metals: Structures and Properties,2002:3 被引 1    
5.  Pardo A. Corrosion behavior of magnesium/aluminum alloys in 3.5% NaCI. Corros. Sci,2008,50(3):823 被引 69    
6.  Zhang KF. Superplastic deformation behavior of hot-rolled AZ31 magnesium alloy sheet at elevated temperatures. J. Wuhan Univ. Technol. Mater. Sci. Ed,2006,21(3):1 被引 2    
7.  Zhang ZM. Corrosion and mechanical properties of hot-extruded AZ31 magnesium alloys, Trans. Nonferrous Met. Soc. China,2008,18(A01):s140 被引 4    
8.  Mordike BL. Magnesium properties applications potential. Materials Science and Engineering A,2001,302(1):37 被引 1179    
9.  Lin YC. Prediction of 42CrMo steel flow stress at high temperature and strain rate, Mech. Res. Commun,2008,35:142 被引 1    
10.  Gourdet S. An experimental study of the deformation of a 304 type austenitic stainless steel, Mate. Sci. Eng. A,1998,255:139 被引 1    
11.  Takuda H. Modeling on flow stress of Mg-AI-Zn alloys at elevated temperatures. Mater. Process. Technol,1998,80/81:513 被引 79    
12.  Semiatin SL. Formability and Workability of Metals-Plastic Instability Flow Localization,1984:121 被引 1    
13.  Sheppard T. Dynamic recrystallization in Al-7Mg. Met. Sci,1983,17(10):481 被引 38    
14.  Zener C. Effect of strain rate upon the plastic flow of steel. J. Appl. Phys,1944,15(1):22 被引 636    
15.  Duan YP. Flow behavior and microstructure evolution of TB8 alloy during hot deformation process. Nonferrous Met. Soc. China,2007,17:1199 被引 20    
16.  Abbasi SM. Prediction of hot deformation behaviour of 10Cr-10Ni-5Mo-2Cu steel. Mater. Lett,2007,61:2523 被引 13    
17.  Jonas JJ. Strength and structure under hot-working conditions. Int. Met. Rev,1969,3(1):1 被引 1    
18.  Yu K. Plastic deformation behaviors of a Mg-Ce-Zn-Zr alloy. Scripta Mater,2003,48:1319 被引 27    
19.  Wang X. Substructure of high temperature compressed titanium alloy IMI 834. Mater. Sci. Eng. A,2006,434(1/2):188 被引 7    
20.  Chen ZH. Heat-Resisting Magnesium Alloy,2007:173 被引 2    
引证文献 11

1 张迪 ZK60镁合金低挤压比棒材的热压缩变形行为 轻金属,2017(10):44-48
被引 0 次

2 张帆 Mg-Gd-Y与AZ31两种变形镁合金的冲击波响应 稀有金属,2012,36(2):201-206
被引 3

显示所有11篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号