文摘
|
采用热膨胀仪、金相显微镜与维氏硬度计测定了不同Mo含量下R5系泊链钢的过冷奥氏体在不同冷却速度下的连续冷却转变曲线(CCT),并观察了试验钢在不同冷却条件下的显微组织. 结果表明,在R5系泊链钢中钼含量每增加0. 15%, Bs点平均下降28℃左右,当Mo含量分别为0. 3%、0. 45%、0. 6%时, Bs点温度依次为632℃、601℃和576℃,钼对Ms点影响较小,降幅不足10℃ |
|
其他语种文摘
|
Based on dilatometry, metallography and Vickers hardness determination, the continuous cooling transformation curves (CCT) of the under-cooled austenite were determined for R5 offshore mooring chain steels with varied contents of Mo. And the microstructure of these steels under different cooling conditions was observed. The results show that when Mo content increases by 0. 15%, the start temperature of bainite transformation decreases by about 28 ℃, when Mo contents are 0. 30%,0. 45% and 0. 60%, Bs point temperatures are 632 ℃,601 ℃ and 576 ℃, respectively. And Mo has little effect on Ms point, which decreases by less than 10 ℃ |
|
来源
|
金属热处理
,2010,35(5):6-10 【核心库】
|
|
关键词
|
Mo
;
R5系泊链钢
;
贝氏体转变
;
连续冷却转变曲线
|
|
地址
|
1.
北京科技大学冶金与生态工程学院, 北京, 100083
2.
北京科技大学材料科学与工程学院, 北京, 100083
3.
河北工业大学体育部, 天津, 300130
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0254-6051 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:3934145
|
|
|
1.
张文基. 高强度高韧性海洋四级系泊链钢的试制及应用.
特殊钢,2000,21(4):43-45
|
被引
4
次
|
|
|
|
|
2.
宛农. 22CrMnNMi o 4级系泊链钢回火参数模拟与优化.
江苏船舶,2004,21(4):26-27
|
被引
4
次
|
|
|
|
|
3.
钱刚. R4级海洋系泊链140 mm圆棒的开发.
特殊钢,2006,27(5):43-45
|
被引
2
次
|
|
|
|
|
4.
琚艳军. 马氏体双相钢生产工艺探讨.
河南冶金,2008,16(4):24-25
|
被引
3
次
|
|
|
|
|
5.
林慧国.
钢的奥氏体转变曲线-原理、测试与应用,1988
|
被引
19
次
|
|
|
|
|
6.
肖国华. 含钒高强度船体结构钢的连续冷却转变.
北京科技大学学报,2006,28(9):830-834
|
被引
3
次
|
|
|
了解气象卫星更多信息，请访问