基于埃洛石的载药凝胶小球的制备及性能研究
Preparation and properties of drug loaded hydrogel beads based on halloysite
查看参考文献15篇
|
文摘
|
采用离子凝胶法制备了一种新的壳聚糖-g-聚丙烯酸/埃洛石/海藻酸钠(CTS-g-PAA/HT /SA)凝胶小球. 研究了HT含量对载药凝胶小球的溶胀性、包封效率和释放性能等的影响;同时也讨论了凝胶小球的pH敏感性和双氯芬酸钠(DS)的释放行为. 结果表明:HT含量对载药凝胶小球的溶胀率、包封效率和累积释放率有明显的影响, 在HT含量为30%时, 溶胀率、包封效率和12h累积释放率分别达到32.84%、91.07%和 100%;另外, 载药凝胶小球具有较好的pH敏感性;在pH=2.1的释放介质中DS几乎不释放, 而在pH=6.8的释放介质中缓慢释放;DS释药机理为溶胀控释. |
|
其他语种文摘
|
A novel hydrogel bead, chitosan-g-poly (acrylic acid)/ halloysite /sodium alginate, was prepared by the ionic gelation method. Effects of halloysite content on swelling property, encapsulation efficiency and drug release for drug loaded in the composite hydrogel beads were investigated. A pH-sensitive and the release kinetics of diclofenac sodium from the hydrogel beads were also studied. The results indicated that the halloysite content obvious influenced the swelling ratio, encapsulation efficiency and diclofenac sodium cumulative release of the diclofenac sodium -loaded hydrogel beads. The biggest swelling ratio was 32. 84, the encapsulation efficiency was 91.07 % and the cumulative release after 12h was 100% when HT content was 30%. In addition, the hydrogel beads had good pH-sensitive. Diclofenac sodium( DS) in the hydrogel beads was hardly released in pH 2. 1 buffer solution, but slowly in pH 6. 8 phosphate buffer solution. The drug release behaviour of the composite hydrogel beads in pH 6. 8 PBS was swelling-controlled mode. |
|
来源
|
化学研究与应用
,2010,22(7):858-863 【核心库】
|
|
关键词
|
埃洛石
;
凝胶小球
;
pH敏感性
;
控制释放
;
双氯芬酸钠
|
|
地址
|
中国科学院兰州化学物理研究所, 甘肃, 兰州, 730000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-1656 |
|
学科
|
化学 |
|
基金
|
中国科学院“优秀博士学位论文、院长奖获得者科研启动专项资金”项目
|
|
文献收藏号
|
CSCD:3916118
|
参考文献 共
15
共1页
|
|
1.
何江川. 温敏水凝胶溶胀行为及其分离性能.
化学研究与应用,2004,16(2):187-190
|
被引
7
次
|
|
|
|
|
2.
向远清. 快速响应智能水凝胶的研究进展.
化学世界,2006(5):308-310
|
被引
2
次
|
|
|
|
|
3.
沈海蓉. 智能水凝胶在药物控释系统中的应用.
中国药学杂志,2004,39(7):490-493
|
被引
3
次
|
|
|
|
|
4.
Xiang Y Q. A new polymer/clay nano-composite hydrogel with improved response rate and tensile mechanical properties.
Eur. Polym. J,2006(42):2125-2132
|
被引
1
次
|
|
|
|
|
5.
郑海芳. 丙烯酸树脂/蒙脱土纳米复合材料的制备研究.
化学研究与应用,2008,20(10):1324-1326
|
被引
1
次
|
|
|
|
|
6.
Levis S R. Characterisation of halloysite for use as a microtubular drug delivery system.
Int. J. Pharm,2002(243):125-134
|
被引
1
次
|
|
|
|
|
7.
Levis S R. Use of coated microtubular halloysite for the sustained release of diltiazem hydrochloride and propranolol hydrochloride.
Int. J. Pharm,2003(253):145-157
|
被引
1
次
|
|
|
|
|
8.
Zheng Y A. Enhanced adsorption of ammonium using hydrogel composites based on chitosan and halloysite.
J. Macromol. Sci A,2010(47):33-38
|
被引
1
次
|
|
|
|
|
9.
Wang Q. Preparation and characterization of a novel pH sensitive chitosan-g-poly ( acrylic acid)/attapulgite/sodium alginate composite hydrogel bead for controlled release of diclofenac sodium.
Carbohyd. Polym,2009(78):731-737
|
被引
1
次
|
|
|
|
|
10.
Zhang J P. In situ generation of sodium alginate/hydroxyapatite nanocomposite beads as drug controlled release matrices.
Acta Biomaterialia,2010(6):445-454
|
被引
1
次
|
|
|
|
|
11.
Kulkari V H. Glutaraldehydecrosslinked chitosan beads for controlled release of diclofenac sodium.
J. Appl. Polym. Sci,2007,103:211-217
|
被引
1
次
|
|
|
|
|
12.
郑筱萸.
中华人民共和国药典. 二部附录,2005:73-74
|
被引
1
次
|
|
|
|
|
13.
Iliescu T. FT-Raman, surface-enhanced Raman spectroscopy and theoretical investigations of diclofenac sodium.
Chem Phys,2004,298:167-174
|
被引
1
次
|
|
|
|
|
14.
Ritger P L. A simple equation for description of solute release. I. Fickian and non-Fickian release from non-swellable devices in the form of slabs, spheres, cylinders or discs.
J. Control. Rel,1987(5):23-36
|
被引
4
次
|
|
|
|
|
15.
Siepmann J. Modeling of drug release from delivery systems based on hydroxypropyl methylcellulose (HPMC).
Adv. Drug. Deliv. Rev,2001(48):139-157
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问