煤拔头中低温快速热解烟煤半焦的孔隙结构
Pore Structure of Low Temperature and Fast Pyrolysis Bituminous Semi-char from Coal Topping Process
查看参考文献31篇
|
文摘
|
利用喷动载流床模拟煤拔头工艺, 在550, 650, 750和850℃热解温度下对大同烟煤进行热解得到拔头半焦.采用氮吸附法对该烟煤及其半焦的孔隙结构进行了研究.结果表明, 拔头半焦的孔隙发达度都弱于原煤; 由低到高4个热解温度下挥发分析出率(Y)依次为7.89%, 21.79%, 22.12%, 39.33%, 中孔尺寸随Y增加而减小, 微孔和大孔尺寸及总孔体积和总孔比表面积基本随Y增加而增加; 550℃时挥发分的析出对孔隙结构的发展无明显有利影响.从原煤到半焦(热解温度由低到高), 样品满足BET吸附等温式的相对压力范围依次为0.101~0.351, 0.093~0.201, 0.072~0.152, 0.032~0.053, 0.058~0.108, BET比表面积与NLDFT总孔比表面积变化趋势一致. |
|
其他语种文摘
|
The pore structure of char derived from Datong bituminous coal after mild pyrolysis at 550, 650, 750 and 850 ℃in a spout entrained reactor was studied using N_2 adsorption. The results show that pore structure of all char samples is inferior to that of the parent coal. Yield of volatiles(Y)at four pyrolysis temperatures, 550, 650, 750 and 850℃, are 7.89%, 21.79%, 22.12%and 39.33%respectively. With increasing of Y, mesopore size decreases, micropore and macropore size, as well as total pore volume(V_(total))and total pore specific area(S_(total)), basically increase.At 550℃, volatile release has little contribution to pore structure evolution of char. Relative pressure ranges obtained are used to calculate BET specific surface area(S_(BET))for parent coal and four chars(derived at 550, 650, 750 and 850℃), are 0.101~0.351, 0.093~0.201, 0.072~0.152, 0.032~0.053, 0.058~0.108 respectively. The change of S_(BET) with pyrolysis temperature is the same as that of S_(total). |
|
来源
|
过程工程学报
,2010,10(3):522-529 【核心库】
|
|
关键词
|
孔隙结构
;
煤拔头半焦
;
氮吸附
;
热解
|
|
地址
|
1.
哈尔滨工业大学能源科学与工程学院, 多相复杂系统国家重点实验室, 黑龙江, 哈尔滨, 015001
2.
哈尔滨工业大学能源科学与工程学院, 黑龙江, 哈尔滨, 015001
3.
中国科学院过程工程研究所, 多相复杂系统国家重点实验室, 北京, 100190
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1009-606X |
|
学科
|
能源与动力工程 |
|
基金
|
国家863计划
;
多相复杂系统国家重点实验室开放课题资助项目
|
|
文献收藏号
|
CSCD:3912432
|
参考文献 共
31
共2页
|
|
1.
许红星. 我国能源利用现状与对策.
中外能源,2010,15(1):3-14
|
被引
16
次
|
|
|
|
|
2.
骆仲泱.
煤的热电气多联产技术及工程应用实例,2004:8, 34-48
|
被引
1
次
|
|
|
|
|
3.
中国工程院. 煤拔头工艺.
中国科学院第九次院士大会报告汇编,1998:202-204
|
被引
1
次
|
|
|
|
|
4.
Wang J G. Experimental Study of Coal Topping Process in a Downer Reactor.
Ind. Eng.Chem. Res,2005,44(3):463-470
|
被引
13
次
|
|
|
|
|
5.
Wang J G. Coal Topping Process and Its Prelimiminary Experiments.
Proceedings of the 7th China-Japan Symposium on Coal and C1 Chemistry,2001:185-188
|
被引
1
次
|
|
|
|
|
6.
Ceiling D W. Coal Topping in a Fluidized Bed System.
Proceedings of the 16th International Conference on Fluidized Bed Combustion,2001:10-14
|
被引
1
次
|
|
|
|
|
7.
Lorenz H. Role of Char Surface Structure Development in Pulverized Fuel Combustion.
Fuel,2000,79(10):1161-1172
|
被引
21
次
|
|
|
|
|
8.
黄瀛华. 煤焦孔隙结构与气化反应性的研究.
煤气与热力,1991,11(5):14-22
|
被引
1
次
|
|
|
|
|
9.
陈彩霞. 煤的结构与煤焦反应性关系的研究及其发展.
煤气与热力,1994,14(2):9-11
|
被引
1
次
|
|
|
|
|
10.
张占涛. 煤的孔隙结构与反应性关系的研究进展.
煤炭转化,2005,28(4):62-68
|
被引
9
次
|
|
|
|
|
11.
Shen C M. Experimental Study of Combustion Characteristics of Bituminous Char Derived under Mild Pyrolysis Conditions.
Energy Fuels,2009,23(11):5322-5330
|
被引
3
次
|
|
|
|
|
12.
Liua G. The Porous Structure of Bituminous Coal Chars and Its Influence on Combustion and Gasification under Chemically Controlled Conditions.
Fuel,2000,79(1):617-626
|
被引
3
次
|
|
|
|
|
13.
刘辉. 快速热解褐煤焦的比表面积及孔隙结构.
中国电机工程学报,2005,25(12):86-90
|
被引
47
次
|
|
|
|
|
14.
丘纪华. 煤粉在热分解过程中比表面积和孔隙结构的变化.
燃料化学学报,1994,22(3):316-320
|
被引
33
次
|
|
|
|
|
15.
Ruiz B. Study of Porous Development in Pyrolysis Chars Obtained from a Low-volatile Coal.
J.Anal. Appl. Pyrolysis,2001,58/59:873-886
|
被引
2
次
|
|
|
|
|
16.
周军. 高温下热解温度对煤焦孔隙结构的影响.
燃料化学学报,2007,35(2):155-159
|
被引
23
次
|
|
|
|
|
17.
王明敏. 热解条件对煤焦比表面积及孔隙分布的影响.
煤炭学报,2008,33(1):76-79
|
被引
20
次
|
|
|
|
|
18.
王明敏. 热解条件对煤焦结构及气化反应活性的影响.
煤炭转化,2007,30(3):21-24
|
被引
18
次
|
|
|
|
|
19.
王俊琪. 热解半焦孔隙特性研究.
热力发电,2008,37(7):6-14
|
被引
7
次
|
|
|
|
|
20.
刘辉. 快速热解褐煤焦的低温氮吸附等温线形态分析.
煤炭学报,2005,30(4):507-510
|
被引
31
次
|
|
|
|
|
了解气象卫星更多信息，请访问