普碳钢用陶瓷基高温防护涂层制备及其性能表征
Preparation and Characterization of High Temperature Protective Ceramic Coating for Plain Carbon Steel

查看参考文献16篇

文摘 采用机械混合法制各了一种针对碳钢的新型Al_2O_3-MgO-TiO_2-CaO体系陶瓷基高温防护涂料,1300℃下可在Q235B钢表面形成致密保护层,提高钢抗氧化烧损性能.结果表明,在涂料粒度48~75μm、涂层厚度0.5 mm的条件下,涂层防护性能优良.涂层的防护温度范围为900~1300℃,1300℃时比原样可降低氧化烧损59.36%,防护寿命长于8 h.涂层的应用将氧化层由经典的Fe_2O_3/Fe_3O_4/FeO三层结构转变为一层尖晶石结构,同时减薄了氧化层厚度,显著降低了Fe元素的高温扩散速率.
其他语种文摘 A new high temperature protective ceramic coating used on the surface of plain steel was prepared by mechanical mixing method. The coating was consisted of magnesia, titania, alumina and calcium oxide mixture. Such a coating, when it was applied superficially on Q235B plain steel surface, could form a compact scale and enhance oxidation resistance at 1300℃. The experimental result showed that the granularity between 48~75 μm and coating layer thickness of 0.5 mm were needed to observe the coating performance. The coating could work effectively in the temperature range of 900~1300℃. Metal loss was diminished by 59.36% compared with the uncoated sample at 1300℃. Duration of the coating could last over 8 h. The ceramic coating converted the scale structure from classic Fe_2O_3/Fe_3O_4/FeO three layers to one spinel layer, suppressed the growth of iron oxides and decreased Fe diffusion speed sharply at elevated temperature.
来源 过程工程学报 ,2010,10(1):167-172 【核心库】
关键词 陶瓷涂层 ; Q235B钢 ; 高温防护
地址

中国科学院过程工程研究所, 多相复杂系统国家重点实验室, 北京, 100190

语种 中文
文献类型 研究性论文
ISSN 1009-606X
学科 金属学与金属工艺
基金 国家科技部重大科技支撑项目基金 ;  国家自然科学基金 ;  中国科学院知识创新工程重要方向项目
文献收藏号 CSCD:3832982

参考文献 共 16 共1页

1.  陆索(译). 金属加热用保护涂层,1979:1-3 被引 2    
2.  魏连启. 动态过程钢坯高温防氧化技术. 电镀与涂饰,2007,27(3):53-55 被引 2    
3.  魏连启. 动态过程钢坯高温抗氧化涂料的研究. 涂料工业,2008,38(7):7-11 被引 5    
4.  宋超池. 加热炉,1981:185 被引 2    
5.  Zhan Z L. Aluminide Coatings Formed on Fe-13Cr Steel at Low Temperature and Its Oxidation Resistance. Oxidation of Metals,2007,68(1):243-251 被引 3    
6.  Kuiry S K. A Superficial Coating to Improve High Temperature Oxidation Resistance of Plain-carbon Steel under Nonisothermal Conditions. Oxidation of Metals,1994,41(2):65-78 被引 1    
7.  梁文. 玻璃基高温防氧化涂料的研究. 材料保护,2007,40(3):37-39 被引 6    
8.  李秋菊. 镍铬合金钢钢坯高温抗氧化涂料作用原理探讨. 鞍钢技术,2000(12):30-32 被引 1    
9.  欧阳德刚. 高温金属抗氧化无机涂层的作用机理与设计原则. 钢铁研究,1997(4):52-54 被引 2    
10.  张国才. 防止钢坯氧化用涂料的研究. 钢铁钒钛,1996,17(1):22-26 被引 4    
11.  王崇庆. 钢铁热处理保护涂料研究. 热加工工艺,2004(2):43-44 被引 4    
12.  Jaffee R. High-temperature Oxidation Resistant Coatings,1970:22-23 被引 1    
13.  Wagner C. Diffusion and High-temperature Oxidation of Metals in Atom Movements,1951:153-157 被引 1    
14.  Chen R Y. Review of the High-temperature Oxidation of Iron and Carbon Steels in Air or Oxygen. Oxidation of Metals,2003,59(5):460-461 被引 1    
15.  Neil B. Introduction to the High-temperature Oxidation of Metals,2006:8-9 被引 1    
16.  符长璞. 钢铁材料热处理防氧化涂层的研究. 金属热处理学报,1996,17(3):52-56 被引 6    
引证文献 4

1 王晓婧 钢坯热轧高温防护功能涂层研究及应用进展 过程工程学报,2010,10(5):1030-1040
被引 3

2 王书华 高温钢坯防氧化涂料用易熔玻璃粘结剂的制备及改性 过程工程学报,2011,11(5):863-868
被引 0 次

显示所有4篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号