三种热喷涂工艺制备NiCr/Cr_3C_2-BaF_2·CaF_2涂层的结构与性能
Microstructure and Properties of NiCr/Cr_3C_2-BaF_2·CaF_2 Coatings Prepared with Three Kinds of Thermal Sprayed Technologies
查看参考文献16篇
|
文摘
|
采用大气等离子喷涂、爆炸喷涂和超音速火焰喷涂三种热喷涂技术制备了NiCr/Cr_3C_2-BaF_2·CaF_2涂层,分析比较了涂层的显微组织、物相组成、孔隙率、硬度、结合强度及其摩擦学性能.结果表明,与大气等离子喷涂相比,超音速火焰喷涂和爆炸喷涂技术制备的涂层具有更高的致密度、硬度和结合强度.采用包覆法制备的粉末进行喷涂,碳化物失碳明显减少,涂层中氧化物含量低.三种NiCr/Cr_3C_2-BaF_2·CaF_2热喷涂涂层的摩擦系数都随着温度的升高而减小,爆炸喷涂和超音速火焰喷涂涂层的摩擦系数比等离子喷涂涂层的摩擦系数更低,耐磨性得到提高.高温下BaF2·CaF2润滑膜的形成均可有效降低三种涂层的摩擦系数,从而降低涂层和对磨球Si3N4的磨损率. |
|
其他语种文摘
|
Microstructures, composition, porosity, hardness, bonding strength and tribological properties of NiCr/Cr_3C_2-BaF_2·CaF_2 coatings prepared with plasma spraying (APS), detonation spraying (DS) and high velocity oxy-fuel spraying (HVOF) was systematically investigated. The results show that using coated spray powders, the decarburization of carbide, oxidation and ablation are reduced in thermal spray process. The NiCr/Cr_3C_2-BaF_2·CaF_2 coatings deposited by HVOF and detonation spraying have higher density, hardness and bond strength with comparison to plasma spraying. The friction coefficients of three kinds of NiCr/Cr_3C_2-BaF_2·CaF_2 coatings decrease with the increasing temperatures, and the high temperature friction coefficients are significantly lower than that at room temperature. The friction coefficients of HVOF and detonation spraying coatings are lower than plasma spraying coating, and HVOF and detonation spraying coatings show better wear-resistance. The friction coefficients and wear rates of three coatings as well as the wear rates of coupled Si3N4 balls are reduced due to the formation of BaF2·CaF2 lubrication layer at elevated temperatures. |
|
来源
|
航空材料学报
,2009,29(6):70-76 【扩展库】
|
|
DOI
|
10.3969/j.issn.1005-5053.2009.6.014
|
|
关键词
|
热喷涂
;
NiCr/Cr_3C_2-BaF_2·CaF_2
;
微观结构
;
力学性能
;
摩擦磨损
|
|
地址
|
1.
中国科学院过程工程研究所, 多相复杂系统国家重点实验室, 北京, 100190
2.
沈阳黎明航空发动机(集团)有限责任公司, 辽宁, 沈阳, 110043
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-5053 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:3763875
|
参考文献 共
16
共1页
|
|
1.
薛群基. 高温固体润滑研究的现状及发展趋势.
摩擦学学报,1999,19(1):91-96
|
被引
73
次
|
|
|
|
|
2.
李剑锋. 等离子喷涂Cr_3C_2-NiCr涂层的气孔率统计分析.
航空材料学报,2000,20(1):33-39
|
被引
9
次
|
|
|
|
|
3.
WIROJANUPATUMP S. The influence of HVOF powder feedstock characteristics on the abrasive wear behaviour of CrxCy-NiCr coatings.
WEAR,2001,249:829-837
|
被引
9
次
|
|
|
|
|
4.
MOHANTY M. Sliding wear behavior of thermally sprayed 75/25 Cr3C2/NiCr wear resistant coatings.
WEAR,1996,198:251-266
|
被引
12
次
|
|
|
|
|
5.
MATEOS J. Tribological properties of plasma sprayed and laser remelted 75/25 Cr3C2/NiCr coatings.
Tribology International,2001,34:345-351
|
被引
16
次
|
|
|
|
|
6.
GUILEMANY J M. Role of heat treatments in the improvement of the sliding wear properties of Cr3C2-NiCr coatings.
Surface and Coatings Technology,2002,157:207-213
|
被引
5
次
|
|
|
|
|
7.
李剑锋. 水润滑下等离子喷涂Cr_3C_2-NiCr涂层/增韧SiC陶瓷摩擦副的摩擦学特性.
摩擦学学报,2001,21(2):90-93
|
被引
8
次
|
|
|
|
|
8.
DONNET C. Historical developments and new trends in tribological and solid lubricant coatings.
Surface and Coatings Technology,2004,180/181:76-84
|
被引
51
次
|
|
|
|
|
9.
SLINEY H E. Solid lubricant materials for high temperature-a review.
Tribology International,1982,15:303-310
|
被引
39
次
|
|
|
|
|
10.
SHINYA SASAKI. Tribological evaluation of plasma sprayed coatings for high temperature sliding surface against cordierite.
Materials and Manufacturing Processes,1999,14:185-194
|
被引
1
次
|
|
|
|
|
11.
LIU G H. Improvement in tribological properties of chromium oxide coating at high temperature by solid lubricants.
WEAR,1993,160:181-189
|
被引
6
次
|
|
|
|
|
12.
MOORE G D. The friction and wear characteristics of plasma-sprayed NiO-CaF2 in rubbing contact with a ceramic matrix.
LUBRICATION ENGINEERING,1974,30:596-604
|
被引
1
次
|
|
|
|
|
13.
SLINEY H E. Fluoride solid lubricants for extreme temperatures and corrosive environments.
ASLE TRANSACTIONS,1965,8:309-322
|
被引
1
次
|
|
|
|
|
14.
DELLACORTE C. The effect of counterface on the tribological performance of a high temperature solid lubricant composite from 25 to 650℃.
Surface and Coatings Technology,1996,86/87:486-492
|
被引
12
次
|
|
|
|
|
15.
DELLACORTE C. Composition optimization of self-lubrication chromium-carbide based composite coatings for use to 760℃.
ASLE TRANSACTIONS,1987,30:77-83
|
被引
13
次
|
|
|
|
|
16.
WANG W C. Application of a high temperature self-lubricating composite coating on steam turbine components.
Surface and Coatings Technology,2004,177/178:12-17
|
被引
14
次
|
|
|
|
|
了解气象卫星更多信息，请访问