具有倍频效应的硼酸盐Pb_2 [B_5O_9]Br化合物的合成、晶体生长及其性质研究
Study on Synthesis, Crystal Growth and Properties of Second-order Nonlinear Optical Material Pb_2 [B_5O_9]Br
查看参考文献13篇
文摘
|
利用高温固相反应法合成出Pb_2 [B_5O_9]Br硼酸盐粉末.采用PbO-NaF做复合助熔剂,利用顶部籽晶法获得了3 mm ×3 mm ×1.5 mm的透明单晶,X射线粉末衍射数据显示,该晶体属正交晶系,Pnn2空间群,晶胞参数为a=1.1524(1) nm, b=1.1431(1) nm, c=0.65399(3) nm. 红外光谱测量证实晶体结构中含有BO_3~(3-)和BO_4~(5-)基团.反射光谱表明Pb_2 [B_5O_9]Br的紫外吸收边在250 nm左右.Pb_2 [B_5O_9]Br粉末倍频效应(SHG)测试表明该化合物具有非线性光学效应,信号强度约等同于β-BaB_2O_4. |
其他语种文摘
|
Pb_2[B_5O_9]Br borate powder was synthesized by the high-temperature solid-state method. The transparent single crystal of Pb_2[B_5O_9]Br was grown by top-seeded solution growth method using the powder as raw material. The typical crystal size was about 3 mm × 3 mm ×1.5 mm. X-ray diffraction analysis show that it is same as the one reported in the literature. It belongs to the orthorhombic system, space group Pnn 2, and lattice parameters a =1.1524(1) nm, b =1.1431(1) nm, c =0.65399(3) nm. The measurement of the infrared spectrum indicate that the basic anionic group is the BO_3~(3-) and BO_4~(5-). The reflection spectrum show that the cut-off wavelength of Pb_2[B_5O_9]Br is about 250 nm. Pb_2[B_5O_9]Br exhibits a powder second harmonic generation (SHG) effect similar to that of β-BaB_2O_4. |
来源
|
人工晶体学报
,2009,38(4):898-901 【核心库】
|
关键词
|
硼酸盐
;
Pb_2[B_5O_9]Br
;
倍频
;
高温固相法
|
地址
|
中国科学院新疆理化技术研究所, 新疆电子信息材料与器件重点实验室, 新疆, 乌鲁木齐, 830011
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
1000-985X |
学科
|
晶体学 |
基金
|
新疆自然科学基金
;
中国科学院“百人计划”项目
;
中国科学院西部之光人才培养计划
;
新疆维吾尔自治区高技术研究与发展计划
;
国家自然科学基金
|
文献收藏号
|
CSCD:3753421
|
参考文献 共
13
共1页
|
1.
Chen C T. A New Ultraviolet SHG Crystal β-BaB2O4.
Science in China. Series B, Chemistry(in English),1985,B28:235-243
|
被引
57
次
|
|
|
|
2.
Chen C. New Nonlinear-optical Crystal:LiB3O3.
Journal of the Optical Society of America,1989,B6:616-621
|
被引
42
次
|
|
|
|
3.
陈创天. 紫外、深紫外非线性光学晶体探索十年回顾.
人工晶体学报,2001,30:36-42
|
被引
9
次
|
|
|
|
4.
Wu Y. CsB3O5:A New Nonlinear Optical Crystal.
Applied Physics Letters,1993,62(21):2614-2615
|
被引
19
次
|
|
|
|
5.
Ye N. New Nonlinear Optical Crystal K2Al2B2O7.
JOURNAL OF THE OPTICAL SOCIETY OF AMERICA B-OPTICAL PHYSICS,2000,17(5):764-768
|
被引
17
次
|
|
|
|
6.
吴以成. B3O7基团型硼酸盐非线性光学晶体研究进展.
人工晶体学报,2001,30:30,44-48
|
被引
1
次
|
|
|
|
7.
Wu Y. A New Lanthanum and Calcium Borate La2CaB10O19.
Chemistry of Materials,2001,13(3):753-755
|
被引
4
次
|
|
|
|
8.
张承乾. 深紫外激光倍频新晶体KBe_2BO_3F_2.
功能材料,2001,32(6):595-597
|
被引
3
次
|
|
|
|
9.
Wang J. Growth of Characterization of PbxSr1-xB4O7 Solid Solution Crystals.
Journal of Crystal Growth,1993,132(1/2):329-330
|
被引
1
次
|
|
|
|
10.
Belokoneva E L. New Hilgardite-group Polyborate Pb2[B5O9]Br with High Optical Nonlinearity.
Crystallography Reports,2003,48(1):44-48
|
被引
1
次
|
|
|
|
11.
Machida K I. Crystal Structure of Europium(II)Bromoborate.
Inorganic Chemistry,1980,19:3807-3811
|
被引
3
次
|
|
|
|
12.
张国春. 一种新的非线性光学材料?Na_3Sm_2(BO_3)_3.
人工晶体学报,2001,30(3):227-231
|
被引
3
次
|
|
|
|
13.
Kurtz S K. A Powder Technique for the Evaluation of Nonlinear Optical Materials.
J.Appl.Phys,1968,39(8):3798-3812
|
被引
98
次
|
|
|
|
|