基于拉曼光谱的高密度聚乙烯质量检测
Detection of HDPE properties by Raman spectrum based on partial least square
查看参考文献47篇
文摘
|
密度和熔融指数是高密度聚乙烯(HDPE)产品最重要的质量指标.本文通过拉曼光谱,结合偏最小二乘法(PLS)分析,实现了对HDPE密度和熔融指数的同时检测.通过对2700~2970 cm~(-1)范围内HDPE的拉曼光谱进行PLS分析,发现了HDPE的密度与短支链数量的负相关,并建立了HDPE密度的PLS回归模型.模型所得密度预测值与真实值的相关系数(r)、平均相对误差(ARD)和预测标准误差(SEP)分别为0.950、0.09%和1.02,优于近红外光谱和基于凝聚态结构分析的拉曼光谱的检测结果.利用HDPE乙烯基含量与熔融指数的正相关,通过分析1288~1650 cm~(-1)范围内的拉曼光谱,建立了HDPE熔融指数的PLS回归模型,所得熔融指数的预测值与真实值的r、ARD和SEP分别为0.966、8.61%和0.99.与熔融指数的红外光谱检测结果相比,拉曼光谱的检测结果具有更高的精度. |
其他语种文摘
|
Density and melt index(MI)are the most important properties of high density polyethylene(HDPE)in industrial manufacturing.In this work,density and MI of commercial grade HDPE were detected by Raman spectrum,based on the partial least squares(PLS)method.The short-branch degree was found to be inversely proportional to the density,according to the PLS analysis of the characterization spectra in the range 2700—2970 cm~(-1).A regression model between short-branch degree and density was built up.The correlation coefficient(r),average relative deviation(ARD)and standard error of the prediction(SEP)for density prediction were 0.950,0.09% and 1.02,respectively.And the density regression model gave a better result than those obtained by near-infrared spectrum and Raman spectrum based on phase structure analysis.Furthermore,the vinyl content was found to be proportional to the MI value.A regression model between vinyl content and the MI of HDPE was established by analyzing the characterization spectra in the range from 1288 cm~(-1) to 1650 cm~(-1).And the values of r,ARD and SEP for MI prediction were 0.966,8.61% and 0.99,respectively.Comparing with the results measured by near-infrared spectrum,Raman spectrum showed higher precision for MI estimation. |
来源
|
化工学报
,2009,60(9):2365-2371 【核心库】
|
关键词
|
高密度聚乙烯
;
熔融指数
;
密度
;
拉曼光谱
;
偏最小二乘法
|
地址
|
浙江大学化学工程与生物工程学系, 化学工程国家重点实验室(浙江大学), 浙江, 杭州, 310027
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
0438-1157 |
学科
|
化学工业 |
基金
|
国家自然科学基金
;
国家863计划
|
文献收藏号
|
CSCD:3663722
|
参考文献 共
47
共3页
|
1.
赵众. 大型聚乙烯工业装置质量指标的次优强跟踪滤波估计.
化工学报,2008,59(7):1635-1638
|
被引
3
次
|
|
|
|
2.
朱印全. 先进过程控制技术在高密度聚乙烯装置上的应用.
石油化工,2006,35(5):469-474
|
被引
1
次
|
|
|
|
3.
McAuley K B. On-line inference of polymer properties in an industrial polyethylene reactor.
AICHE Journal,1991,37(6):825-835
|
被引
29
次
|
|
|
|
4.
McAuley K B. Nonlinear product property control in industrial gas-phase polyethylene reactor.
AICHE Journal,1993,39(5):855-866
|
被引
7
次
|
|
|
|
5.
Fernandes F A N. Reactor modeling and physicochemical properties characterization for a polyethylene fluidized bed reactor.
BRAZILIAN JOURNAL OF CHEMICAL ENGINEERING,1999,16(4):369-375
|
被引
4
次
|
|
|
|
6.
王靖岱. 工业流化床聚乙烯树脂性能模型的研究.
高校化学工程学报,2001,15(1):82-87
|
被引
12
次
|
|
|
|
7.
Alizadeh M. Modeling of fluidized bed reactor of ethylene polymerization.
CHEMICAL ENGINEERING JOURNAL,2004,97(1):27-35
|
被引
8
次
|
|
|
|
8.
刘恩滨. Application of non-linear controller to HDPE plant.
石油化工自动化,2004(3):13-17
|
被引
1
次
|
|
|
|
9.
John R F.
Introductory Raman Spectroscopy.2nd ed,2003:1-40
|
被引
2
次
|
|
|
|
10.
Richard L M.
Raman Spectroscopy for Chemical Analysis,2000:1-12
|
被引
2
次
|
|
|
|
11.
伍林. 拉曼光谱技术的应用及研究进展.
光散射学报,2005,17(2):180-186
|
被引
43
次
|
|
|
|
12.
Christopher C N. Raman spectroscopy employed for the determination of the intermediate phase in polyethylene.
MACROMOLECULES,1995,28(8):2969-2978
|
被引
2
次
|
|
|
|
13.
Norbert S. Study of the phase structure of linear polyethylene by means of small-angle X-ray scattering and Raman spectroscopy.
MACROMOLECULES,1995,28(14):5029-5036
|
被引
2
次
|
|
|
|
14.
Bryant G K. Raman spectroscopy combined with small angle X-ray scattering and wide angle X-ray scattering as a tool for the study of phase transitions in polymers.
Review of Scientific Instruments,1998,69(5):2114-2117
|
被引
1
次
|
|
|
|
15.
Rodriguez-Cabello. Determination of the content of extended chain segments in isotropic and uniaxially stretched polyethylenes by Raman spectroscopy.
Macromolecular Chemistry and Physics,1998,199(12):2767-2776
|
被引
1
次
|
|
|
|
16.
Paradkar R P. Estimating crystallinity in high density polyethylene fibers using online Raman spectroscopy.
Journal of Applied Polymer Science,2003,88(2):545-549
|
被引
6
次
|
|
|
|
17.
Lin W. The application of Raman spectroscopy to three-phase characterization of polyethylene crystallinity.
Polymer Test,2007,26(6):814-821
|
被引
5
次
|
|
|
|
18.
Sano K. Fourier transform Raman spectra of linear low-density polyethylene and prediction of their density by multivariate data analysis.
Applied Spectroscopy,1999,53(5):551-556
|
被引
2
次
|
|
|
|
19.
Harumi S. Raman spectra of high-density,low-density,and linear low-density polyethylene pellets and prediction of their physical properties by multivariate data analysis.
Journal of Applied Polymer Science,2002,86(2):443-448
|
被引
2
次
|
|
|
|
20.
陈德钊.
多元数据处理,1998:190-200
|
被引
4
次
|
|
|
|
|