高孔率网状Cu+CeO_2/Cu抗菌材料的制备及其抗菌性能
Preparation and antibacterial properties of Cu+CeO_2/Cu porous materials
查看参考文献12篇
|
文摘
|
以泡沫海绵为基体材料,通过电镀的方法制备了高孔率网状Cu+CeO_2/Cu抗菌材料,研究了制备条件并测定了其孔隙率和比表面积,评价了其抗菌性能.结果表明,网状Cu+CeO_2/Cu抗菌材料的孔隙率高达95%以上,其比表面积约为31.4m~2/cm~3,对于大肠埃希氏菌、金黄色葡萄球菌和白色念珠菌3种菌种均具有良好的抗菌性能. |
|
其他语种文摘
|
The porous materials of Cu+CeO_2/Cu were prepared by the electro-deposition on a precursor of conventional polyamide foam.Their porosity and specific surface area were measured.Antibacterial properties of Cu+CeO_2/Cu porous materials were investigated.The results show that their porosity may reach above 95% and specific surface area is about 31.4m~2/cm~3.The porous materials of Cu+CeO_2/Cu exhibited excellent antibacterial properties against E.coli,S.aureus and C.albicans. |
|
来源
|
功能材料
,2009,40(2):265-267 【核心库】
|
|
关键词
|
高孔率
;
网状Cu+CeO_2/Cu
;
抗菌性能
|
|
地址
|
1.
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
2.
辽宁省微生物科学研究院, 辽宁, 朝阳, 122000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-9731 |
|
学科
|
化学工业 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:3586935
|
参考文献 共
12
共1页
|
|
1.
Jeon H J.
BIOMATERIALS,2003,24:4921-4928
|
被引
34
次
|
|
|
|
|
2.
孙剑. 无机抗菌剂的研究进展.
材料导报,2007,21(Ⅷ):344-348
|
被引
20
次
|
|
|
|
|
3.
Dan Z G.
THIN SOLID FILMS,2005,492:93-100
|
被引
28
次
|
|
|
|
|
4.
周新文. 光化学还原法制备Ag—TiO2抗菌材料的制备及性能研究.
化工新型材料,2006,34(11):68-70
|
被引
2
次
|
|
|
|
|
5.
袁鹏.
化工矿物与加工,2002,10:5-9
|
被引
4
次
|
|
|
|
|
6.
Kim T N.
Journal of Materials Science:Materials in Medicine,1998,9:129-134
|
被引
32
次
|
|
|
|
|
7.
张彬. 铜、银双组分无机抗菌材料的制备和性能研究.
化工新材料,2007,35(2):73-75
|
被引
8
次
|
|
|
|
|
8.
许应.
河北理工学院学报,2001,23(4):77-82
|
被引
1
次
|
|
|
|
|
9.
慕康国. 稀士元素防治植物病害的研究进展.
中国稀土学报,2003,21(1):1-5
|
被引
14
次
|
|
|
|
|
10.
敬和民.
新型抗菌材料的研究,2006:106
|
被引
1
次
|
|
|
|
|
11.
陆春华.
南京工业大学学报,2003,25(1):1107-110
|
被引
1
次
|
|
|
|
|
12.
谷俊改. Cu^2＋、Zn^2＋复合无机抗菌剂的制备及性能研究.
功能材料,2006,37(8):1310-1311
|
被引
3
次
|
|
|
|
|
了解气象卫星更多信息，请访问