可膨胀石墨阻燃水发泡聚氨酯泡沫塑料的制备
Preparation of Flame-Retardant of Water Blown Polyurethane Foams Filled with Expandable Graphite

查看参考文献6篇

文摘 采用四溴醇合成了适合水发泡的阻燃聚醚多元醇,并通过可膨胀石墨与其它阻燃剂的复配使用,制得了可膨胀石墨阻燃的水发泡聚氨酯泡沫塑料.讨论了溴代醇种类、发泡剂种类及用量、可膨胀石墨粒径及用量和复合阻燃剂配比等因素对泡沫阻燃性能的影响.结果表明,该阻燃聚醚多元醇与含有可膨胀石墨的复合阻燃剂复配使用,制得的可膨胀石墨阻燃水发泡聚氨酯泡沫塑料氧指数可达33%,压缩强度为280 KPa,达到了国家标准GB/T 8624-1997中B_1级氧指数的要求,并且阻燃剂用量少,阻燃效果稳定.
其他语种文摘 Flame-retardant polyether polyol, which was mainly made of bromhydrin, was compounded with expandable graphite and other flame retardants to prepare a flame-retardant of water-blown polyurethane foam filled with expandable graphite. Effects of different kinds of bromal, blowing agent level, diameter and level of expandable graphite and proportion of synergistic flame retardants on flame-retardant performance of the rigid polyurethane (PU) foams were discussed. The results show that the flame-retardant effect of the PU foams is improved with oxygen index 33% , compressive strength 280 KPa, which reaches the Chinese national standard of flame-retardant B_1 grade. The level of the flame retardants is low and the effect is steady.
来源 高分子材料科学与工程 ,2009,25(6):128-131 【核心库】
关键词 可膨胀石墨 ; 阻燃 ; 聚氨酯泡沫塑料 ; 水发泡
地址

中国科学院过程工程研究所, 北京, 100080

语种 中文
文献类型 研究性论文
ISSN 1000-7555
学科 化学工业
文献收藏号 CSCD:3583117

参考文献 共 6 共1页

1.  闫格. 建筑用高阻燃型硬质聚氮酯泡沫塑料的研制. 聚氨酯工业,2003,18(2):31-33 被引 8    
2.  秦桑路. 添加型阻燃剂对聚氨酯硬泡阻燃性能的影响. 高分子材料科学与工程,2007,23(4):167-169 被引 9    
3.  DUQUESNE S. Thermal degradation of polyurethane and polyurethane/expandable graphite coatings. Polymer Degradation and Stability,2001,74:493-499 被引 45    
4.  KRASSOWSKI D W. Expandable graphite flake as an Intumaescent flame retardant additive. Proceedings of Fire & Materials,1998,2:293 被引 3    
5.  MODESTI M. Expandable graphite as an intumescent flame retardant in polyisocyanurate polyurethane foams. Polymer Degradation and Stability,2002,77:195-202 被引 41    
6.  CELZARD A. Modelling of exfoliated graphite. Process in Materials Science,2005,50:93-179 被引 22    
引证文献 8

1 赵义平 复配无卤阻燃聚氨酯泡沫塑料的制备与表征 功能材料,2013,44(5):697-699
被引 13

2 李卫亮 可膨胀石墨对聚氨酯半硬质泡沫性能的影响 工程塑料应用,2015,43(8):1-5
被引 0 次

显示所有8篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号