文摘
|
针对大飞机壁板用的铝合金板料AA6056进行激光弯曲过程的试验研究.试验选用厚度为1.0 mm和2.5 mm的薄板,采用多组不同的工艺参数进行对比分析.采用直径0.1 mm的镍铬.镍硅热电偶作为温度传感器,YOKOGAWA MV200型便携式记录仪测量板料表面的温度;使用MV.1300UM CCD拍摄板料激光弯曲变形的过程,通过自行开发的实时采集软件记录并进行图像处理,最终得到了板料激光弯曲变形过程的实测曲线.试验结果为该过程的数值模拟提供了更为精确的验证依据,为深入研究板料激光弯曲过程奠定了试验基础. |
|
其他语种文摘
|
The process of laser bending for aluminium alloy AA6056 used to produce large airplane panel was studied through experiment. The thickness of specimens was selected 1. 0 mm and 2. 5 mm separately. The different groups of the technological parameters were used to analyze contrastively in the process of laser bending. The specimen was clamped at one end as a cantilever plate and was irradiated by the laser beam in the width direction. 0.1 mm diameter NiCr/NiSi thermocouple was adopted as temperature sensor in the ex-periment, and the temperature on the specimen surface was measured by YOKOGAWA MV200 measuring de-vice. A free end point was chosen as a measuring point and a CCD-camera recordsed its displacement during the laser bending process. The video was processed by the measuring software, which was developed by Beijing University of Aeronautics and Astronautics, and the displacement value can be obtained. Experiment result supplies more accurate data for numerical simulation of laser bending process and provides the experimental foundation for research on laser bending process deeply. |
|
来源
|
北京航空航天大学学报
,2009,35(2):154-157 【核心库】
|
|
关键词
|
激光弯曲
;
实时测量
;
温度场
;
位移场
|
|
地址
|
1.
北京航空航天大学,机械工程及自动化学院, 北京, 100191
2.
中国科学院力学研究所, 北京, 100080
3.
欧洲宇航防务创新集团, 德国, 慕尼黑, 81663
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-5965 |
|
学科
|
金属学与金属工艺;电子技术、通信技术 |
|
基金
|
欧洲宇航防务创新集团(德国EADS Innovation Works)资助项目
|
|
文献收藏号
|
CSCD:3574661
|
|
|
1.
程丽芳.
铝合金板激光弯曲成形的实验研究,2005
|
被引
2
次
|
|
|
|
|
2.
Geiger M. Synergy of laser material processing and metal forming.
Annals of CIRP,1994,43(2):563-570
|
被引
28
次
|
|
|
|
|
3.
Vollertsen F. Mechanisms and models for laser forming.
Laser Assisted Net Shape Engineering 1,1994:345-359
|
被引
2
次
|
|
|
|
|
4.
周益军. 基于水冷却的不锈钢板料激光热应力成形试验.
农业机械学报,2007,38(4):172-176
|
被引
2
次
|
|
|
|
|
5.
裴继斌. 船舶钢板激光弯曲成形的试验研究.
锻压技术,2005,5:64-66
|
被引
3
次
|
|
|
|
|
6.
管延锦. 扫描路径规划对激光弯曲成形影响的实验研究.
锻压技术,2005,1:36-39
|
被引
2
次
|
|
|
|
|
7.
Wang X F. Research on the themo-physical process of laser bending.
Journal of Materials Processing Technology,2002,127:388-391
|
被引
6
次
|
|
|
|
|
8.
王秀凤. 薄板激光弯曲温度场的数值模拟与校验.
北京航空航天大学学报,2003,29(5):377-381
|
被引
3
次
|
|
|
了解气象卫星更多信息，请访问