热处理对电沉积Ni-Fe合金箔微观结构和磁性能的影响
Effects of heat treatment on the microstructure and magnetic properties of electrodeposited Ni-Fe permalloy foils
查看参考文献13篇
|
文摘
|
对电沉积得到的Ni-Fe坡莫合金箔,在氢气气氛下进行退火处理,退火温度分别为850, 1000和1150℃,保温时间均为5h.在扫描电子显微镜(SEM)和光学显微镜下观察合金箔断面和表面的显微结构,利用XRD检测合金箔的晶体结构,利用软磁材料直流磁性测试仪装置测得合金箔的直流磁特性.实验结果表明:在850～1150℃温度下热处理时,退火温度越高,合金箔的直流磁性能越好;经过退火热处理后合金箔的晶粒明显长大,而且合金箔存在明显的择优取向. |
|
其他语种文摘
|
Electrodeposited Ni-Fe permalloy foils was annealed under hydrogen atmosphere at 850, 1000 and 1150℃ for 5 h, respectively. The microstructures of cross-sections and surfaces were observed by SEM and optical microscope, the crystal structure was studied by XRD, and the direct-current magnetic properties were measured by direct-current magnetic properties testing equipment. The results indicate that when the annealing temperature is between 850 and 1150℃, the direct-current magnetic properties improve with increasing temperature. After annealing, the crystals of the permalloy foils grow up rapidly and present obvious preferred orientation . |
|
来源
|
北京科技大学学报
,2009,31(3):357-361 【核心库】
|
|
关键词
|
坡莫合金
;
退火处理
;
电沉积
;
磁性能
;
择优取向
|
|
地址
|
1.
北京科技大学, 生态与循环冶金教育部重点实验室, 北京, 100083
2.
中国科学院,过程工程研究所, 北京, 100080
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-053X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:3528021
|
参考文献 共
13
共1页
|
|
1.
Leith S D. Characterization of NixFe1-x(0.01《x《0.95) electrodeposition from a family of sulfamate-chloride electrolytes.
Journal of the Electrochemical Society,1999,146(6):1431
|
被引
5
次
|
|
|
|
|
2.
郭占成. 电沉积Fe、Ni基合金箔的组织形貌及磁性能.
中国有色金属学报,2004,14(2):273
|
被引
12
次
|
|
|
|
|
3.
卢维昌.
电解成型制备纯铁箔的方法.中国专利,ZL91102934,1994
|
被引
1
次
|
|
|
|
|
4.
周绍民.
金属电沉积原理与研究方法,1987:243
|
被引
6
次
|
|
|
|
|
5.
宋维锡.
金属学,2004:203
|
被引
1
次
|
|
|
|
|
6.
Nakamura K. Electrodeposition of iron-rich Ni-Fe alloys from sulphate and chloride baths.
SURFACE TECHNOLOGY,1985,25:111
|
被引
3
次
|
|
|
|
|
7.
Egberts P. Mesoscale structure in electrodeposited nanocrystalline Ni-Fe alloys.
MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2006,441:336
|
被引
2
次
|
|
|
|
|
8.
El-Sharif M R. Microstructure of electrodeposited chromium and chromium alloys.
Eurocorrosion,1991(1):234
|
被引
1
次
|
|
|
|
|
9.
Banovic S W. Microstructural characterization and hardness of electrodeposited nickel coatings from a sulphamate bath.
Journal of Materials Science,1998,33:639
|
被引
2
次
|
|
|
|
|
10.
辜敏. 高择优取向铜镀层的电化学形成及其表面形貌.
物理化学学报,2002,18(11):973
|
被引
32
次
|
|
|
|
|
11.
黄令. 钕离子对镍电沉积层择优取向及其性能的影响.
厦门大学学报:自然科学版,1996,35(6):907
|
被引
6
次
|
|
|
|
|
12.
Bugaychuk S M. Effect of electron irradiation on texturing in electrodeposited nanocrystalline alloy Fe-78%Ni.
Scripta Mater,2007,57:1028
|
被引
1
次
|
|
|
|
|
13.
冯端.
金属物理学,第四卷:超导电性和磁性,1998:580
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问