Zn对铸态Mg—Mn合金力学性能和腐蚀性能的影响
Effect of Zn on mechanical properties and corrosion properties of as-cast Mg-Mn alloy
查看参考文献17篇
|
文摘
|
研究Zn对Mg-Mn合金微观组织、力学性能和在Hank’s溶液中腐蚀性能的影响。结果表明：Zn可以明显细化Mg—Mn合金的铸态组织，当合金中Zn含量（质量分数）为3％时，合金的晶粒尺寸由700-900μm减小到50-80μm。合金的力学性能也随Zn含量的增加而显著提高；Zn含量为3％时，拉伸强度提高128．8MPa，屈服强度提高42．6MPa，伸长率提高1倍多。在Mg-Mn合金中加入1％-2％的Zn，能够增强Mg-Mn合金钝化膜的稳定性，使Mg-Mn合金腐蚀速度显著降低。但是，当Zn含量增至3％时，钝化膜变得不稳定，腐蚀速度增加，耐蚀性能降低。 |
|
其他语种文摘
|
The effect of Zn on the microstructure, mechanical properties and corrosion properties in Hank＇s solute on of as-cast Mg-Mn alloy was studied. The results indicate that the addition of Zn element can significantly refine the grain size of cast Mg-Mn alloy. When Zn content is increased up to 3% （mass fraction）, the grain size of the cast alloy decreases from 700-900 gm to 50-80 Ixm. Meanwhile, the mechanical properties of the alloy also increase with increasing Zn content. When Zn content is 3%, the ultimate tensile strength and the yield strength are increased by 128.8 and 42.6 MPa, respectively, while the elongation is increased twice. Addition of Zn element to Mg-Mn alloy can stabilize the passivation film, which mainly contributes to the low corrosion rate of Mn-Mn-Zn alloy. However, when the Zn content is over 3%, the passivation film becomes unstable, which results in a relatively high corrosion rate. |
|
来源
|
中国有色金属学报
,2008,18(3):388-393 【核心库】
|
|
关键词
|
镁合金
;
锌
;
微观组织
;
力学性能
;
腐蚀
|
|
地址
|
1.
哈尔滨工业大学材料科学与工程学院, 黑龙江, 哈尔滨, 150001
2.
中国科学院金属研究所, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-0609 |
|
学科
|
金属学与金属工艺 |
|
基金
|
中国科学院“百人计划”项目
;
沈阳市创新平台建设计划资助项目
|
|
文献收藏号
|
CSCD:3257994
|
参考文献 共
17
共1页
|
|
1.
CAHN R W.
Materials science and technology,1996:18-20
|
被引
1
次
|
|
|
|
|
2.
WITTE F. In vitro and in vivo corrosion measurements of magnesium alloys.
Biomaterials,2006,27(7):1013-1018
|
被引
179
次
|
|
|
|
|
3.
WITTE F. In vivo corrosion of four magnesium alloys and the associated bone response.
Biomaterials,2005,26(17):3557-3563
|
被引
269
次
|
|
|
|
|
4.
STAIGERA M P. Magnesium and its alloys as orthopedic biomaterials:A review.
Biomaterials,2006,27(9):1728-1734
|
被引
424
次
|
|
|
|
|
5.
ZHANG Er-lin. Formation by ion plating of Ti-coating on pure Mg for biomedical applications.
Scripta Materialia,2005,53(5):523-527
|
被引
2
次
|
|
|
|
|
6.
王登峰. 镁锰合金的晶粒细化及其耐蚀性的研究.
铸造设备研究,2005,1:12-14
|
被引
2
次
|
|
|
|
|
7.
关学丰. 改善变形Mg-Mn系合金性能的研究.
湖南冶金,1993,1:7-9
|
被引
1
次
|
|
|
|
|
8.
范靖亚. Mg-Y-Mn合金高性能板材研究.
轻合金加工技术,1994,22(8):45-47
|
被引
2
次
|
|
|
|
|
9.
翁康荣. Si、Ca对Mg-2Mn变形镁合金组织和性能的影响.
热加工工艺:铸锻版,2006,35(1):1-3
|
被引
4
次
|
|
|
|
|
10.
BALLERINI G. About some corrosion mechanisms of AZ91D magnesium alloy.
Corrosion Science,2005,47(9):2173-2184
|
被引
32
次
|
|
|
|
|
11.
张忠林. 镁合金燃点和耐蚀性及力学性能的研究.
轻合金加工技术,2003,31(7):31-33
|
被引
5
次
|
|
|
|
|
12.
李冠群. 主要合金元素对镁合金组织及耐蚀性能的影响.
铸造技术,2006,27(1):81-82
|
被引
4
次
|
|
|
|
|
13.
谢苗. 甘纯?海带膳食纤维的制备条件与营养评价.
河南科技大学学报:农学版,2004,24(4):56-59
|
被引
2
次
|
|
|
|
|
14.
胡汉起.
金属凝固原理,2000:126-130
|
被引
1
次
|
|
|
|
|
15.
QIU D. A novel approach to the mechanism for the grain refining effect of melt superheating of Mg-Al alloys.
Acta Materialia,2007,55(6):1863-1871
|
被引
14
次
|
|
|
|
|
16.
MA Yan-long. Effects of heat-treatment on microstructure of wrought magnesium alloy ZK60.
Transactions of Nonferrous Metals Society of China,2006,16(3):1889-1990
|
被引
1
次
|
|
|
|
|
17.
BARIL G. The corrosion of pure magnesium in aerated and deaerated sodium sulphate solutions.
Corrosion Science,2001,43(3):471-484
|
被引
87
次
|
|
|
|
|
了解气象卫星更多信息，请访问