Effect of DH treatment on microstructure and mechanical properties of an LM28-0.3wt.%Nd hypereutectic aluminum silicon alloy
查看参考文献10篇
文摘
|
In this article, a novel heat treatment method, deformation heat (DH) treatment (extrusion + aging), was employed on a hypereutectic aluminum silicon alloy (LM28-0.3wt.%Nd), and its effect on microstructure and mechanical properties of this alloy was investigated. It can be concluded that the eutectic microstructure disappears after the DH treatment, in the meantime the morphology of α(Al) solid solution was transformed from fir-tree and cellular to equiaxed, Si was refined with grain sizes of about 1-10 μm and distributed dispersedly, even some of them became globular shape, which can reduce stress accumulation effectively. Mechanical properties test indicated that the DH treatment could significantly improve the room-temperature strength and have little effect on the high-temperature strength of LM28-0.3wt.%Nd alloy. The fracture mechanism is ductile fracture by fracture morphology analysis. |
来源
|
Rare Metals
,2007,26(6):578-583 【核心库】
|
DOI
|
10.1016/s1001-0521(08)60010-8
|
关键词
|
Al-Si alloys
;
Nd
;
deformation heat treatment
;
mechanical properties
|
地址
|
School of Materials and Metallurgy, Northeastern University, Shenyang, 110004
|
语种
|
英文 |
文献类型
|
研究性论文 |
ISSN
|
1001-0521 |
学科
|
金属学与金属工艺 |
文献收藏号
|
CSCD:3115311
|
参考文献 共
10
共1页
|
1.
Bentz H W. Pistons for the 90's.
Automat. Eng,1992,100:13
|
被引
1
次
|
|
|
|
2.
Ho C R. Heterogeneous nucleation of solidification of Si in Al-Si and Al-Si-P alloys.
Acta Metall. Mater,1995,43(8):3231
|
被引
22
次
|
|
|
|
3.
Knuutinen A. Porosity formation in aluminium alloy A356 modified with Ba, Ca, Y and Yb.
J Light Met,2001,1:241
|
被引
6
次
|
|
|
|
4.
Nogita K. Mechanisms of eutectic solidification in Al-Si alloys modified with Ba, Ca, Y and Yb.
J. Light Met.,2001,1:219
|
被引
11
次
|
|
|
|
5.
Wu S S. Modification mechanism of hypereutectic Al-Si alloy with P-Na addition.
Trans. Nonferrous Met. Soc. China,2003,13:1285
|
被引
16
次
|
|
|
|
6.
Nafisi S. Boutorabi S. M. A, Ghomashchi R. , Factors influencing the modification and refinement of hypereutectic Al-Si alloys for production of automotive pistons.
TMS Light Met,2004,851
|
被引
1
次
|
|
|
|
7.
Takahashi T. Mechanism of Al-Si alloy castings modified with sodium, strontium and antimony.
J. Jpn. Inst. Light Met,1982,32(10):511
|
被引
1
次
|
|
|
|
8.
Liu Q Y. Effect of antimony on the growth kinetics of high purity Al-Si alloy.
Scripta Mater,1998,38(7):1083
|
被引
3
次
|
|
|
|
9.
Knuutinen A. Modification of Al-Si alloys with Ba,.
J. Light Met.,2001,1:229
|
被引
34
次
|
|
|
|
10.
Pei Y T. Five-fold branched Si particles in laser clad Al-Si functionally graded materials.
Acta Mater,2001,49:561
|
被引
7
次
|
|
|
|
|