Cu/Sn63-Pb37偶对在模拟湿热大气环境中的电化学腐蚀
ELECTROCHEMICAL CORROSION BEHAVIORS OF THE GALVANIC COUPLE Cu/Sn63-Pb37 IN SIMULATED ATMOSPHERE

查看参考文献15篇

文摘 针对电子装备中Cu/Sn63-Pb37偶对在模拟湿热大气环境中(40℃,95%RH)的腐蚀特性,用薄液膜下原位零阻安培表腐蚀电化学测试技术结合SEN、Fr-IR及XRD等表面分析手段,获得了电偶对的阳极电偶电流密度和电偶电位随时间的变化规律及腐蚀试样表面形貌和腐蚀产物组成的信息,阐述了Cu与sn63-Pb37之间的电偶腐蚀特征和电化学机制,并揭示了金属表面腐蚀产物膜的形成进程及其对电偶腐蚀行为的影响。结果表明,Cu作为偶对中的阳极发生腐蚀而Sn63-Pb37作为阴极受到保护,腐蚀产物对Cu表面腐蚀进程具有阻滞作用,实验后期Sn63-Pb37表面的阴极活化作用加强,并破坏其表面的稳态氧化膜促使其发生腐蚀。
其他语种文摘 The Cu/Sn63-Pb37 galvanic couple appeared in most electronic devices.This paper was to investigate the corrosion characteristics and mechanisms of this couple,which was exposed in the typically simulated air condition at 40 ℃ with 95% RH.The in-situ electrochemical information of the couple have been performed with related zero resistance ampere techniques under thin moisture film.According to the time dependent features of galvanic potential and anodic galvanic current density results,the Cu acted as anode and the Sn63-Pb37 acted as cathode during exposure.The gradually formed corrosion products,which were detected by FT-IR and XRD,restrained the anodic polarization behavior occurring on Cu surface.The hydrolyzed CO_2 on the Sn63-Pb37 surface induced the breakdown of Pb oxides formed in air naturally,which was confirmed from the SEM surface morphologies.Despite of the exact corrosion rates not obtained from the galvanic current density data,the changing trend was valuable for estimating the atmospheric corrosion behavior of the Cu/Sn63-Pb37 couple.
来源 中国腐蚀与防护学报 ,2007,27(6):329-333 【核心库】
关键词 电偶腐蚀Cu ; Sn63-Pb37焊料
地址

中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016

语种 中文
文献类型 研究性论文
ISSN 1005-4537
学科 金属学与金属工艺
基金 国家自然科学基金
文献收藏号 CSCD:3042579

参考文献 共 15 共1页

1.  Guttenplan J D. Corrosion control for electrical contacts in submarine based electronic equipment. Mater Perform,1978,18(12):49-55 被引 1    
2.  Sinclair J D. Corrosion of electronics. J Electrochem Soc,1988,135(3):89 被引 1    
3.  李青. 电子材料的腐蚀. 电子元件与材料,1996,15(6):48-50 被引 3    
4.  Aastrup T. Experimental in situ studies of copper exposed to humidified air. Corros Sci,2000,42:957-967 被引 11    
5.  Shin B L. Electrochemical migration characteristics of eutectic SnPb solder alloy in printed circuit board. Thin Solid Films,2006,504:294-297 被引 1    
6.  Manning M I. Atmospheric corrosion issues today. Industrial Corros,1989,7(8):5-9 被引 1    
7.  Mattsson E. Corrosion:an electrochemical problem. Chem Technol,1985,4:234-243 被引 2    
8.  曹楚南. 腐蚀电化学原理,2004 被引 79    
9.  徐俊丽. 大气腐蚀电化学监测的研究. 中国腐蚀与防护学报,1987,7(1):60-65 被引 10    
10.  Zakipour S. Evaluation of laboratory tests to simulate indoor corrosion of electrical contact materials. J Electrochem Soc,1986,133(1):21-30 被引 1    
11.  Debiemme C. X-Ray photoemission investigation of the corrosion film formed on a polished Cu-13Sn alloy in aerated NaCl solution. Appl Surf Sci,2001,174:55-61 被引 1    
12.  Ryck I D. Study of tin corrosion:the influence of alloying elements. J Cultural Heritage,2004,5:189-195 被引 2    
13.  Mansfeld F. Galvanic corrosion of Al alloysⅢ The effect of area ratio. Corros Sci,1975,15:239-250 被引 3    
14.  Chen Z Y. The effects of sodium chloride particles on the atmospheric corrosion of pure copper. Corrosion,2004,60(5):479-491 被引 4    
15.  鲁永奎. 固态铅,锡及其合金表面腐蚀热力学. 北京科技大学学报,1989,11(2):167-172 被引 4    
引证文献 3

1 方强 塑封功率器件在湿热老化试验中分层导致的电化学腐蚀的分析 复旦学报. 自然科学版,2009,48(5):539-544
被引 1

2 姚小飞 热浸镀速率对铜导线表面Pb40Sn60合金镀层组织和力学性能的影响 稀有金属材料与工程,2019,48(11):3651-3656
被引 1

显示所有3篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号