Transient oxidation behavior of nanocrystalline CoCrAlY coating at 1 050 ℃
查看参考文献19篇
|
文摘
|
Nanocrystalline CoCrAlY overlay coating was prepared on M38G superalloy by magnetron sputtering deposition. To investigate the oxidation behavior and phase transformation of alumina during oxidation, the oxidation experiments were conducted at 1 050 ℃ for various time in the range of 5-180 min. The phase compositions of the oxide scales were investigated by using glancing angle X-ray diffraction(XRD). The microstructure analysis of oxide scales was carried out by means of scanning electron microscopy(SEM). The growth process of metastable alumina at the grain boundaries and transformation to stable alumina were discussed. The results show that at the initial oxidation stage the mixture of δ-Al_2O_3,γ-Al_2O_3 and α-Al_2O_3 is formed on the sample surface rapidly. Especially, δ-Al_2O_3 and γ-Al_2O_3 prefer growing at the grain boundaries of CoCrAlY coating. With increasing oxidation time, δ-Al_2O_3 and γ-Al_2O_3 transform to θ-Al_2O_3, afterwards θ-Al_2O_3 transforms to α-Al_2O_3 gradually. After 180 min oxidation, θ-Al_2O_3 transforms into α-Al_2O_3 completely. |
|
来源
|
Transactions of Nonferrous Metals Society of China
,2007,17(3):595-599 【核心库】
|
|
DOI
|
10.1016/s1003-6326(07)60140-x
|
|
关键词
|
CoCrAlY coating
;
oxidation
;
Al_2O_3
;
phase transformation
|
|
地址
|
1.
Institute of Metal Research, Chinese Academy of Sciences, Shenyang National Laboratory for Materials Science, Shenyang, 110016
2.
School of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology, Nanchang, 330034
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1003-6326 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:2827758
|
参考文献 共
19
共1页
|
|
1.
FRITSCHER K. Eutectic structures in the Ni-Co-Cr-Al system obtained by plasma spraying and by Bridgman growth.
Journal of Crystal Growth,2003,250:546-557
|
被引
1
次
|
|
|
|
|
2.
MOBARRA R. Hot corrosion behavior of MCrAlY coatings on IN738LC.
Surface and Coatings Technology,2006,216:2202-2207
|
被引
7
次
|
|
|
|
|
3.
BAUFELD B. Microstructural changes as postmortem temperature indicator in Ni-Co-Cr-Al-Y oxidation protection coatings.
Mater Sci Eng A,2004,384:162-171
|
被引
4
次
|
|
|
|
|
4.
GUO M H. The preparation and hot corrosion resistance of gradient NiCoCrAlYSiB coatings.
Surface and Coatings Technology,2006,200:3942-3949
|
被引
16
次
|
|
|
|
|
5.
WANG F. High temperature oxidation and corrosion resistant nanocrystalline coatings.
Surface Engineering,2003,19(1):32-36
|
被引
2
次
|
|
|
|
|
6.
NIJDAM T J. Promoting exclusiveα-Al2O3 growth upon high-temperature oxidation of NiCrAl alloys:Experiment versus model predictions.
Acta Materialia,2005,53:1643-1653
|
被引
4
次
|
|
|
|
|
7.
CHEN G. Transient alumina transformation on a sputtered K38G nanocrystalline coating.
Surface and Coatings Technology,2005,191:263-266
|
被引
1
次
|
|
|
|
|
8.
GRABKE H J. Oxidation of NiAl and FeAl.
Intermetallics,1999,7:1153-1158
|
被引
23
次
|
|
|
|
|
9.
BRUMM M W. The oxidation behaviour of NiAl-Ⅰphase transformations in the alumina scale during oxidation of NiAl and NiAl-Cr alloys.
Corr Sci,1992,33(11):1677-1690
|
被引
29
次
|
|
|
|
|
10.
PENG X. Transient alumina transformations during the oxidation of magnetron-sputtered CoCrAl nanocrystalline coatings.
Oxid Met,2003,60(4):225-240
|
被引
9
次
|
|
|
|
|
11.
AN T F. Effect of the Al2O3 transformation in scales on the oxidation behavior of a nickel-base superalloy with an aluminide diffusion coating.
Oxid Met,2000,54(4):301-316
|
被引
11
次
|
|
|
|
|
12.
RYBICKI G C. Effect of theθ→α-Al2O3 transformation on the oxidation behavior ofβ-NiAl+Zr.
Oxid Met,1989,31(4):275-304
|
被引
31
次
|
|
|
|
|
13.
WANG F. Oxidation behaviour and scale morphology of normal-grained CoCrAl alloy and its sputtered microcrystalline coating.
Mater Sci Eng A,1990,129(2):279-285
|
被引
11
次
|
|
|
|
|
14.
KOFSTAD P.
High Temperature Corrosion,1988
|
被引
26
次
|
|
|
|
|
15.
LI T F.
High Temperature Oxidation and Hot Corrosion of Metals,2003
|
被引
3
次
|
|
|
|
|
16.
ZHANG Z H. Effect of polymorphism of Al2O3 on the synthesis of magnesium aluminate.
Ceram Inter,2005,31:583-589
|
被引
4
次
|
|
|
|
|
17.
TURKDOGAN E T.
Physical Chemistry of High Temperature Technology,1980
|
被引
28
次
|
|
|
|
|
18.
PINT B A. Experimental observations in support of the dynamic-segregation theory to explain the reactive-element effect.
Oxid Met,1996,45(2):1-37
|
被引
89
次
|
|
|
|
|
19.
PINT B A. The oxidation mechanism ofθ-Al2O3 scales.
Solid State Ionics,1995,78:99-107
|
被引
14
次
|
|
|
|
|
了解气象卫星更多信息，请访问