铝稀土合金（Al-Nd）高能微弧火花合金化的研究
AI-Nd Surface Alloying by High Energy Microarc Spark Process
查看参考文献14篇
|
文摘
|
用高能微弧火花合金化设备将铝稀土（Al—Nd）电极合金熔化到AZ31镁合金上以提高其耐蚀性，用极化曲线测试和浸泡试验表征合金的耐蚀性，用金相显微镜和扫描电镜观察合金化层的显微结构，用x射线衍射进行物相分析。结果表明，使用高能微弧火花Al—Nd合金化后，由于晶粒细化、快速凝固和合金化层中富含Al和Nd，可显著提高AZ31镁合金的耐蚀性。 |
|
其他语种文摘
|
To improve the corrosion resistance of a magnesium-aluminum-zinc alloy, Al-Nd electrode alloy was melted on the surface of AZ31 magnesium alloy by high energy microarc spark alloying（HEMASA） equipment. The corrosion resistance was evaluated through polarization and immersion tests;the microstructure of the Al-Nd coating was examined by optical microscope（OM） and scanning electron microscope（ SEM ） ;the phases were analyzed by X-ray diffraction. The resuits show that the coating formed by HEMASA improves the corrosion resistance of the AZ31 alloy because of the fine microstructure, rapid solidification and rich content of Al and Nd in the coating. |
|
来源
|
金属热处理
,2007,32(1):36-39 【核心库】
|
|
关键词
|
镁合金
;
高能微弧火花合金化
;
铝-钕合金
;
腐蚀
|
|
地址
|
1.
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
2.
沈阳黎明航空发动机集团公司, 辽宁, 沈阳, 110043
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0254-6051 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金项目
|
|
文献收藏号
|
CSCD:2735248
|
参考文献 共
14
共1页
|
|
1.
陈长军. ZM5镁合金表面电火花合金化改性层的获得.
材料热处理学报,2004,25(4):42-44
|
被引
7
次
|
|
|
|
|
2.
陈长军. ZM5镁合金表面高能微弧沉积ZL301铝合金的研究.
金属热处理,2003,28(9):1-4
|
被引
9
次
|
|
|
|
|
3.
Parkansky N. Development and application of pulsed-air-arc deposition.
Surface and Coating Technology,1993(61):268-273
|
被引
1
次
|
|
|
|
|
4.
Johnson G N. Advances in the electrospark deposition coating process.
J Vac Sci Technol A,1986,4(6):2740-2746
|
被引
20
次
|
|
|
|
|
5.
Wang Ruijun. Interface behavior study of WC92-Co8 coating produced by electrospark deposition.
Applied Surface Science,2005,240:42-47
|
被引
18
次
|
|
|
|
|
6.
Parkansky N. Electrode erosion and coating properties in pulsed air arc deposition of WC-based hard alloys.
Surface and Coating Technology,1998,105:130-134
|
被引
10
次
|
|
|
|
|
7.
Lesnjak A. Process and properties of deposits in electrospark deposition.
Science and Technology of welding and Joining,2002,7(6):391-396
|
被引
22
次
|
|
|
|
|
8.
Parkansky N. Anode mass loss during pulsed air arc deposition.
Surface and Coating Technology,1998,108/109:253-256
|
被引
6
次
|
|
|
|
|
9.
Galinov L V. Mass transfer trends during electrospark alloying.
Surface and Coating Technology,1996(79):9-18
|
被引
1
次
|
|
|
|
|
10.
陈钟燮.
电火花表面强化工艺,1987:22-24
|
被引
3
次
|
|
|
|
|
11.
陈长军. 电火花表面强化研究进展.
航空维修与工程,2003(4):36-37
|
被引
2
次
|
|
|
|
|
12.
张诗昌. 主要合金元素对镁合金组织和性能的影响.
铸造,2001,50(6):310-315
|
被引
62
次
|
|
|
|
|
13.
范才河. 稀土在镁及镁合金中的作用.
材料导报,2005,19(7):61-63, 68
|
被引
27
次
|
|
|
|
|
14.
R Ambat. Evaluation of microstructure effects on corrosion behaviour of AZ91D magnesium alloy.
Corrosion Science,2000,42:1433-1455
|
被引
92
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问