微量磷(P)对等原子比NiAl的微观组织与力学性能的影响
Effect of Trace Element P on Microstructure and Mechanical Properties for Stoichiometric NiAl
查看参考文献18篇
|
文摘
|
研究了微量P对挤压态等原子比NiAl的微观组织与高温力学性能的影响.结果表明:微量P的添加对NiAl的晶格常数有一定的影响,P偏聚于NiAl晶界处;并对其高温延伸率有重要影响.P偏聚于晶界阻碍了合金变形过程中的动态回复和再结晶,加剧了晶界处孔洞的形成,造成了NiAl-P合金与二元NiAl合金高温力学性能的显著差异,主要表现在:应力-应变曲线经历了较长的加工硬化阶段;最大延伸率明显下降;变形激活能升高,应变速率敏感指数下降.NiAl-P合金的高温变形机制为变形过程中位错的滑移与攀移共同作用. |
|
其他语种文摘
|
The effect of trace element P on the microstructure and mechanical properties at high temperature for stoichiometric NiAl as extruded were investigated. The results showed that the little doping P mainly segregated at the grain boundaries and influenced the lattice parameter of NiAl and the elongation at high temperature. The segregation of P at the grain boundaries impeded the process of dynamic recovery or recrystallization during deformation at high temperature, which aggravated to the formation of cavities at the grain boundaries and this made the different mechanical properties between pure stoichiometric NiAl with and without phosphorus. The difference mainly revealed as follow: (1) the alloy doping little P experienced long time hardening in the true-stress vs true strain curves; (2) the largest elongation was decreasing during the deforming process; (3) the deformation activation energy and the strain rate sensitivity index were increasing and decreasing, respectively. The deforming mechanism was the comprehensive role between dislocation gliding and climbing behavior at high temperature. |
|
来源
|
材料工程
,2007(4):7-11 【核心库】
|
|
关键词
|
金属间化合物
;
NiAl
;
微观组织
;
力学性能
|
|
地址
|
1.
湖南科技大学, 湖南省机械设备健康维护重点实验室, 湖南, 湘潭, 411201
2.
中国科学院金属研究所, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
国家863计划
|
|
文献收藏号
|
CSCD:2730103
|
参考文献 共
18
共1页
|
|
1.
SIKKA V K.
Superplastic behavior in Fe-Si-Al alloy,1987:417-429
|
被引
1
次
|
|
|
|
|
2.
JOHNSON D R. Processing and mechanical properties of in-situ composites from the NiAl-Cr and the NiAl-(Cr Mo)eutectic systems.
Intermetallics,1995,3:99-106
|
被引
59
次
|
|
|
|
|
3.
GALE W F. Formation and microstructural stability of multiphase intermetallic based on NiAl.
Materials Sciences and Engineering,1995,192/193:868-878
|
被引
1
次
|
|
|
|
|
4.
CUI C Y. Preliminary investigation of directionally solidified NiAl-28Cr-5.
Mater Letters,2000,43:203-210
|
被引
5
次
|
|
|
|
|
5.
陈荣石. NiAl基多相金属间化合物的显微组织、超塑性研究.
金属学报,1998,34:1121-1125
|
被引
14
次
|
|
|
|
|
6.
COTTON J D. Chromium-bearing NiAl inter-metallic alloys.
Intermetallics,1993,1:117-130
|
被引
4
次
|
|
|
|
|
7.
郭建亭. 稀土元素在金属间化合物（铝化物）中的作用.
材料工程,2002(1):36-41
|
被引
15
次
|
|
|
|
|
8.
DAROLIA R. The effect of Fe Ga and Mo on the room temperature tensile ductility of NiAl.
Scritpa Metall Mater,1992,26:1007-1013
|
被引
24
次
|
|
|
|
|
9.
NOEBE R D. Physical and mechanical properties of the B2 compound NiAl.
International Materials Reviews,1993,38(4):193-233
|
被引
57
次
|
|
|
|
|
10.
TUNER F. Effect of trace elements on forgeability of superalloys.
Met Technol,1984,11:446-452
|
被引
1
次
|
|
|
|
|
11.
SUN W R. Effect of minor elements on the microstructure and mechanical properties.
Metr Trans.A,1997,27:649-654
|
被引
1
次
|
|
|
|
|
12.
MEETHAM G D. Trace elements in superalloys an overview.
Met Technol,1984,11:414-418
|
被引
1
次
|
|
|
|
|
13.
WHITE C L. Effect of Sb Sn As and P additions on the high temperatures ductility of Ni.
Scripta Metall.A,1982,23:3343-3359
|
被引
1
次
|
|
|
|
|
14.
HOLT R T. Impurities and trace elements in Ni-base superalloys.
Inter Met Rev,1976,21:1-24
|
被引
33
次
|
|
|
|
|
15.
CAO W D. The effect of P on mechanical properties of alloy 718.
Superalloy 718,625,706 and Various Derivatives,1994:463-477
|
被引
2
次
|
|
|
|
|
16.
GUO S.
Superalloy 718,625,706 and Various Derivatives,1997:521-530
|
被引
1
次
|
|
|
|
|
17.
MCFADDEN S X. Superplasticity in nanocrystalline Ni3Al.
Materials Science and Engineering A,2001(319/321):849-856
|
被引
1
次
|
|
|
|
|
18.
DU X H. The superplastic deformation of NiAl with large grain.
Scripta Materilia,2001,45(1):89-95
|
被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问