钢基身管内镀铬层下的激光淬火基体界面腐蚀与铬层剥落
INTERFACIAL CORROSION AND SPALLSTION OF Cr-PLATED COATING ON A GUN BARREL STEEL SUBSTRATE PRE-TRATED BY LASER SPIRALY QUECHING
查看参考文献25篇
|
文摘
|
钢基身管镀铬层在高温腐蚀性气体中服役,采用YAG激光器对身管内表面作螺旋线状离散淬火预处理后再电镀铬的复合工艺,形成了基体界面呈激光淬火区/激光未处理区周期性变化的铬层/基体结构.对该身管进行高温腐蚀介质为火药气体的靶场实验.对实验后的基体界面腐蚀形貌与铬层剥落的关系研究表明:次界面裂纹的形成是基体界面高温气体腐蚀的根本原因,基体界面腐蚀的结果是形成基体烧蚀坑,烧蚀坑上的铬层以断裂形式剥落.激光淬火预处理钢基体通过抑制次界面裂纹的形成避免了基体界面高温气体腐蚀损伤,提高了铬层的抗剥落能力. |
|
其他语种文摘
|
To meet the technical requirement for service in hot corrosive gases environment of Chromium-plated coatings of gun barrel, a complex technology was developed to improve the performance of the coatings that YAG laser was used to pre-quench the inner surface of gun barrel in mode of helix and then chromium-coating was plated to fabricated the Cr-coating/substrate structure with periodically dispersed substrate interface with laser quenched zones and original ones. Thereafter, the treated gan barrels were experienced for field firing test. The hot gasous environment is real firing gases. The analysis of corrosion morphology at interface of coating/substrate shows that the main reason of hot gases corrosion of substrate at the interface is the sub-interfacial crack formation in the substrate, which may induce erosion hole at the initial cracks of substrate. Thereby Cr-coatings on the erosion hole would spall in mode of fracture. Laser pre-quenched substrate may surpress the interface corrosion damage by suppressing the sub-interfacial crack forming, for this reason, the spallation resistance of Cr-coatings is enhanced. |
|
来源
|
腐蚀科学与防护技术
,2006,18(6):418-421 【核心库】
|
|
关键词
|
腐蚀
;
铬层
;
激光淬火
;
基体界面
;
剥落
|
|
地址
|
中国科学院力学研究所, 北京, 100080
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金资助项目
|
|
文献收藏号
|
CSCD:2631853
|
参考文献 共
25
共2页
|
|
1.
S Sopok. Thermal-chemical-mechanical gun bore erosion of an advanced artillery system part one:theories and mechanisms.
Wear,2005,258:659
|
被引
36
次
|
|
|
|
|
2.
S Sopok. Thermal-chemical-mechanical gun bore erosion of an advanced artillery system part two:modeling and predictions.
Wear,2005,258:671
|
被引
23
次
|
|
|
|
|
3.
P J Cote. Gas-met al reaction products in the erosion of chromium-plated gun bores.
Wear,2000,241:17
|
被引
26
次
|
|
|
|
|
4.
P J Cote. Laser pulse heating of gun bore coatings.
Surface and Coatings Technology,2001,146/147:65
|
被引
7
次
|
|
|
|
|
5.
P J Cote. Application of Laser Pulse Heating to Simulate Thermomechanical Damage at Gun Bore Surfaces.
Journal of Pressure Vessel Technology,2003,125:335
|
被引
6
次
|
|
|
|
|
6.
PJ Cote. Gun bore erosion mechanisms revisited with laser pulse heating.
Surface and Coatings Technology,2003,163/164:478
|
被引
18
次
|
|
|
|
|
7.
J H Underwood. Thermomechanical modeling of transient thermal damage in cannon bore materials.
Wear,2004,257:992
|
被引
13
次
|
|
|
|
|
8.
J H Underwood. Critical Fracture Processes in Army Cannons:A Review.
Journal of Pressure Vessel Technology,2003,125:291
|
被引
1
次
|
|
|
|
|
9.
J H Underwood. Thermal Damage,Crackingand Rapid Erosion of Cannon Bore Coatings.
Journal of Pressure Vessel Technology,2003,125:299
|
被引
29
次
|
|
|
|
|
10.
B Lawton. Thermo-chemical erosion in gun barrels.
Wear,2001,251:827
|
被引
48
次
|
|
|
|
|
11.
张喜发.
火炮烧蚀内弹道学,2001:6
|
被引
2
次
|
|
|
|
|
12.
EO CObo. Corrosion of chromium plated rotor in drilling fluid.
Surface and Coatings Technology,1999,122:39
|
被引
3
次
|
|
|
|
|
13.
徐永祥. 表面状态和处理对涂层下A3钢腐蚀和涂层失效的影响.
腐蚀科学与防护技术,2003,15(4):208
|
被引
2
次
|
|
|
|
|
14.
徐永祥. 可溶盐污染对涂层下A3钢腐蚀和涂层失效的影响.
腐蚀科学与防护技术,2003,15(3):137
|
被引
1
次
|
|
|
|
|
15.
林海潮. 涂层下金属的腐蚀过程.
腐蚀科学与防护技术,2002,14(3):180
|
被引
13
次
|
|
|
|
|
16.
陈光南. 提高镀铬身管寿命的激光强化新方法.
兵工学报,2003,12(增刊):6
|
被引
16
次
|
|
|
|
|
17.
Huaixue Li. Characteristics of the interface of a laser-quenched steel substrate and chromium electroplate.
Surface&Coatings Technology,2006,201(3/4):902
|
被引
9
次
|
|
|
|
|
18.
徐向阳. 激光硬化基体对镀铬层组织和结合的影响.
中国激光,2006,33(3):413
|
被引
9
次
|
|
|
|
|
19.
陈光南.
管状工件内表面激光强化方法与装置.中国.ZL99116728.7
|
被引
2
次
|
|
|
|
|
20.
曾志银.
火炮身管强度设计理论,2001:46
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问