质子注入聚酰亚胺的摩擦学特性
Tribological Properties of Proton Implanted Polyimide
查看参考文献10篇
|
文摘
|
用能量为110 keV剂量分则为1×10~(14)ions/cm~2、5×10~(14)ions/cm~2、2.5×10~(15)ions/cm~2和1.25×10~(16)ions/cm~2的质子对聚酰亚胺进行注入改性.摩擦磨损试验表明,质子注入能够提高其耐磨性.但在不同载荷下,其摩擦磨损行为随着注入剂量的变化有所不同.未注入样品的磨痕内存在明显的粘着和划痕,而注入之后,粘着和划痕受到抑制,磨痕变得光滑. |
|
其他语种文摘
|
The polyimide was implanted with 110 keV protons in four doses of 1*10~(14) ions/ cm~2, 5*10~(14) ions/cm~2, 2.5*10~(15) ions/cm~2 and 1.25*10~(16)ions/cm~2. Friction and wear experiments showed the improvement of their wear-resistance after proton implantation. But under different loads, the variety of their friction and wear behavior with implantation doses showed some differences. There were obvious adhesiveness and scuffing in the wear scar of polyimide before implantation, whereas the wear scar became smoother after implantation, with the adhesiveness and scuffing abated. |
|
来源
|
高分子材料科学与工程
,2006,22(6):153-156 【核心库】
|
|
关键词
|
聚酰亚胺
;
质子注入
;
摩擦磨损
|
|
地址
|
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 甘肃, 兰州, 730000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1000-7555 |
|
学科
|
化学工业 |
|
基金
|
国家自然科学基金
;
国家自然科学基金资助
|
|
文献收藏号
|
CSCD:2613223
|
参考文献 共
10
共1页
|
|
1.
贾均红. 聚酰亚胺复合材料的摩擦性能及其机理研究.
摩擦学学报,2002,22(4):273-276
|
被引
29
次
|
|
|
|
|
2.
贾均红. 聚四氟乙烯/碳纤维增强聚酰亚胺复合体系的摩擦学性能.
材料科学与工程学报,2003,21(2):183-186
|
被引
11
次
|
|
|
|
|
3.
Cai H.
Polymer Testing,2003,22(8):875-882
|
被引
32
次
|
|
|
|
|
4.
Liu W M.
Wear,1996,194:103-106
|
被引
7
次
|
|
|
|
|
5.
杨生荣. 离子注入聚酰亚胺的摩擦磨损性能研究.
摩擦学学报,1996,16(2):180-183
|
被引
7
次
|
|
|
|
|
6.
Cai H.
Materials Science and Engineering A,2004,364:94-100
|
被引
19
次
|
|
|
|
|
7.
Cai H.
Polymer Testing,2003,22:875-882
|
被引
32
次
|
|
|
|
|
8.
Mishra R.
Radiation Mesurements,2003,36:719-722
|
被引
1
次
|
|
|
|
|
9.
Guenther M.
Surface and Coatings Technology,2002:108-113
|
被引
9
次
|
|
|
|
|
10.
Sabre K.
Surface and Coatings Technology,2001,139:257-264
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问