不同Al2O3含量ZrO2（3Y）／Al2O3纳米复合粉体的制备与表征
Preparation and Characterization of ZrO2 （3Y）/Al2O3 Nano-sized Powders with Various Al2O3 Contents
查看参考文献15篇
|
文摘
|
采用化学共沉淀法制备了Al2O3数量分数为0％～30％的ZrO2（3Y）／Al2O3纳米复合粉体，研究了Al2O3含量和煅烧温度对粉体相结构、晶粒尺寸和晶格畸变的影响。结果表明：800℃×2h煅烧的复合粉体只出现t-ZrO2相，不出现Al2O3的任何晶相；Al2O3的添加抑制了ZrO2（3Y）晶粒的增长和四方相向单斜相的结构相变，使相变温度显著提高，晶格畸变增大。 |
|
其他语种文摘
|
ZrO2 （3Y） nano-sized powders containing 0% - 30mass% Al2O3 were prepared by coprecipitation method. The effects of Al2O3 content and calcining temperature on phase structure, grain size and lattice distortion were studied. Only t-ZrO2 phase was found when powders were calcined at 800 ℃ for 2 h. The dopants of Al2O3 greatly inhibited the increase of crystallite size and the phase transformation from tetragonal to monoclinic, also made the phase transformation temperature and crystal lattice distortion increase. |
|
来源
|
机械工程材料
,2006,30(7):75-78 【核心库】
|
|
关键词
|
ZrO2（3Y）／Al2O3纳米复合粉体
;
相变
;
晶格畸变
|
|
地址
|
1.
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 甘肃, 兰州, 730000
2.
兰州理工大学材料科学与工程学院, 甘肃, 兰州, 730050
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1000-3738 |
|
学科
|
冶金工业 |
|
基金
|
国家自然科学基金创新研究群体项目
;
国家自然科学基金资助项目
|
|
文献收藏号
|
CSCD:2477993
|
参考文献 共
15
共1页
|
|
1.
Mayo M J. Processing nanocrystalline ceramics for applications in superplasticity.
Mater Sci Eng A,1993,166:145-159
|
被引
8
次
|
|
|
|
|
2.
Mayo M J. Synthesis and applications of nanocrystalline ceramics.
Mater Design,1993,16(6):323-329
|
被引
7
次
|
|
|
|
|
3.
靳喜海. 纳米复相陶瓷.
化工进展,2003,22(6):553-558
|
被引
2
次
|
|
|
|
|
4.
Seong-Min Choi. Nanocomposites-a new material design concept.
Science and Technology of Advanced Materials,2005,6(1):2-10
|
被引
1
次
|
|
|
|
|
5.
Tsubakino H. Effect of alumina addition on the tetragonal-to-monoclinic phase transformation in zirconia-3mol%yttria.
J AmCeram Soc,1991,74(2):440-443
|
被引
5
次
|
|
|
|
|
6.
Vladimir V Srdic. Sintering behavior of nanocrystalline zirconia doped with alumina prepared by chemical vapor synthesis.
J Am Ceram Soc,2000,83(8):1853-1860
|
被引
14
次
|
|
|
|
|
7.
杨刚. Ce-TZP/Al2O3纳米复合粉的制备.
机械工程材料,2002,26(12):27-29
|
被引
1
次
|
|
|
|
|
8.
Sonia L. Obtaining CeO2-ZrO2 mixed oxides by coprecipitation:role of preparation conditions.
Applied Catalysis B:Environmental,2005,58:3-4
|
被引
1
次
|
|
|
|
|
9.
克鲁格 H P.
X射线衍射技术,1986
|
被引
2
次
|
|
|
|
|
10.
Yamakata K. Formation of alumina/zirconia(3 mol%yt tria)composite powders prepared by the hydrazine method.
J Am Ceram Soc,1994,77:2207-2208
|
被引
4
次
|
|
|
|
|
11.
Yoshimura M. Crystallization and microstructural characterization of ZrO2(3 mol%Y2O3)nano-sized powders with various Al2O3 contents.
Journal of Alloys and Compounds,1999,290:284-289
|
被引
2
次
|
|
|
|
|
12.
尹邦跃. 3Y-TZP/Al_2O_3复合粉末的相变研究.
硅酸盐学报,2001,29(1):1-7
|
被引
6
次
|
|
|
|
|
13.
张立德.
纳米材料和纳米结构,2001
|
被引
489
次
|
|
|
|
|
14.
尹荔松. 纳米TiO_2粉晶的XRD研究.
功能材料,1999,30(5):498-500
|
被引
41
次
|
|
|
|
|
15.
方国家. CuO-SnO2纳米晶粉料的SolGel制备及表征.
无机材料学报,1996,11(3):537-541
|
被引
9
次
|
|
|
|
|
了解气象卫星更多信息，请访问