文摘
|
采用MHK-500型摩擦磨损试验机和日本协和株式会社产CA-A型接触角仪分别研究了聚四氟蜡、聚四氟乙烯（PTFE）／聚氨酯粘接固体润滑涂层的摩擦磨损性能和疏水性能；采用扫描电子五微镜、光学五微镜分析了涂层磨损表面、对偶表面的磨损情况．结果表明，聚四氟蜡和PTFE都能提高聚氨酯涂层的疏水性和耐磨性能，降低涂层的摩擦系数。聚四氟蜡／聚氨酯粘接润滑涂层的耐磨性明显优于PTFE／聚氨酯粘接润滑涂层的耐磨性。同时，速度与负荷对聚四氟蜡／聚氨酯粘接涂层的摩擦磨损性能有很大影响。在低负荷、中高速试验条件下，它具有良好的减摩耐磨性能。 |
|
其他语种文摘
|
The tribological and hydrophobical properties of polyurethane coating with additive of POLYFLUO-150 WAX （PFW） and PTFE were discussed. The effect of PFW and PTFE volume content on the friction and wear properties of multiplayer coatings was investigated through MHK-500 friction and wear tester in sliding against stainless steel ring under dry friction condition. As the result, the polyurethane coating with PFW has much better friction and wear behaviors than the coating with PTFE. The friction and wear behavior of the PU coating with PFW is depended on the applied load and sliding speed. With the increase of load and sliding speed , the friction coefficient and the wear life of PU coatings with PFW is reduced, the wear life of the coatings is best at 1.97 m/s. |
|
来源
|
高分子材料科学与工程
,2006,22(2):149-152 【核心库】
|
|
关键词
|
聚四氟蜡
;
聚氨酯
;
聚四氟乙烯
;
复合涂层
;
摩擦磨损性能
|
|
地址
|
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 甘肃, 兰州, 730000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1000-7555 |
|
学科
|
化学 |
|
文献收藏号
|
CSCD:2461050
|
|
|
1.
薛群基. 摩擦学研究的发展概况与趋势.
摩擦学学报,1993,13(1):73-81
|
被引
24
次
|
|
|
|
|
2.
田军. 聚氨酯/聚四氟乙烯耐磨防腐涂层表面结构的研究.
腐蚀科学与防护技术,1997,9(3):182-186
|
被引
12
次
|
|
|
|
|
3.
Gong D.
Wear,1991,147(1):9-24
|
被引
6
次
|
|
|
|
|
4.
张招柱. 陶瓷颗粒填充PTFE复合材料的摩擦磨损性能研究.
高分子材料科学与工程,2001,17(2):121-124
|
被引
18
次
|
|
|
|
|
5.
Yoichiro M.
Progress in Organic Coatings,2000,40:119-120
|
被引
5
次
|
|
|
|
|
6.
Tian J.
Journal of Applied Polymer Science,2002,86:3454-3459
|
被引
3
次
|
|
|
|
|
7.
Vink P.
Progress in Organic Coating,1996,28:173-181
|
被引
8
次
|
|
|
了解气象卫星更多信息，请访问