耐候钢在含MgCl2介质的干湿环境下的腐蚀行为
CORROSION BEHAVIOR OF WEATHERING STEEL IN A WET/DRY ENVIRONMENT CONTAINING MgCl2
查看参考文献11篇
文摘
|
通过以0.3%MgCl2溶液为介质的浸渍干湿循环加速腐蚀试验,研究了Corten—A耐候钢在干/湿环境下的腐蚀行为.扫描电镜(SEM)和能量色散X射线谱(EDX)观察分析了各腐蚀循环下的腐蚀形貌及C1、Mg元素含量的变化.结果表明Corten—A钢的腐蚀失重与循环次数呈线性关系.腐蚀产物中的晶体相初期主要是β-FeOOH,后期主要是γ—FeOOH和少量的ε-Fe2O3.电化学测试表明铁锈的还原反应加速了阴极反应;锈层的电容值比较大,说明锈层的结构比较疏松,不具保护性. |
其他语种文摘
|
The corrosion behavior of Corten - A weathering steel was investigated by immersion - dry - wet accelerated corrosion test in 0.3 % magnesium chloride solution. By using SEM and EDAX technology, the corrosion images as well as the contents of the chloride ion and magnesium under different cycles were provided. It ap- peared linear relationship between the weight loss and corrosion test cycles. In early stage the main crystal product is/β - FeOOH, in late period it is γ- FeOOH with few ε - Fe2O3. The result of the electrochemical tests showed that the cathodic reaction was accelerated due to the reduction of the rust; the large amount of the rust indicated that structure of the rust was loose and the rust did not have protection ability. |
来源
|
中国腐蚀与防护学报
,2006,26(3):136-140 【核心库】
|
关键词
|
耐候钢
;
MgCl2
;
干湿环境
;
加速腐蚀
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
1005-4537 |
学科
|
金属学与金属工艺 |
基金
|
国家自然科学基金资助项目
|
文献收藏号
|
CSCD:2447481
|
参考文献 共
11
共1页
|
1.
翁永基. 盐沉积量对埕岛海域大气腐蚀性分级的影响.
油气储运,2001,20(7):36-40
|
被引
6
次
|
|
|
|
2.
Takemura M. Protectiveness of rust formed on weathering steel in atmosphere rich in air-born chloride particles.
Material and Environment,2000,49(2):72-77
|
被引
2
次
|
|
|
|
3.
Masuda H. Effect of magnesium chloride liquid thickness on atmospheric corrosion of pure iron.
Corrosion,2001,57(2):99-109
|
被引
7
次
|
|
|
|
4.
胡东生. 近代察尔汗盐湖的变迁.
科学通报,1990,35(24):1888-1891
|
被引
8
次
|
|
|
|
5.
Ogundele G I. The effect of cation on the corrosion of carbon and stainless steels in differing chloride environments.
Corrosion,1989,45(12):981-984
|
被引
1
次
|
|
|
|
6.
Yamashita M. The long term growth of the protective rust layer formed on weathering steel by atmospheric corrosion during a quarter of a century.
Corros Sci,1994,36(2):283-299
|
被引
137
次
|
|
|
|
7.
Misawa T. The mechanism of formation of iron oxide and oxyhydroxides in aqueous solutions at room temperature.
Corros Sci,1974,14(2):131-149
|
被引
38
次
|
|
|
|
8.
Evans U R. Mechanism of atmospheric rusting.
Corros Sci,1972,12(3):227-246
|
被引
67
次
|
|
|
|
9.
Evans U R. Mechanism of rust.
Corros Sci,1969,9(11):813-821
|
被引
23
次
|
|
|
|
10.
曹楚南.
电化学阻抗谱导论,2002,26:153
|
被引
5
次
|
|
|
|
11.
Wang J H. Modeling of atmospheric corrosion behavior of weathering steel in sulfur dioxide-polluted atmospheres.
Corrosion,1996,52(12):900-909
|
被引
8
次
|
|
|
|
|
|