稀土处理炭纤维填充聚四氟乙烯复合材料在干摩擦条件下的摩擦磨损性能研究
Tribological Behavior of Polytetrafluroethylene Composites Filled with Rare Earths Treated Carbon Fiber under Dry Friction Condition
查看参考文献13篇
|
文摘
|
研究了稀土元素（RE）处理炭纤维表面的最佳添加量和不同炭纤维表面处理对聚四氟乙烯（PTFE）复合材料在干摩擦条件下摩擦磨损性能的影响，并利用扫描电子显微镜对其磨损表面进行观察和分析．结果表明：当稀土元素在表面改性剂中的含量为0．3％时，炭纤维填充聚四氟乙烯复合材料的摩擦磨损性能最佳；在干摩擦条件下。表面处理炭纤维填充聚四氟乙烯复合材料的摩擦系数比未经处理炭纤维填充聚四氟乙烯复合材料的低，且其耐磨性较好；稀土处理使得复合材料的界面强韧性得到明显改善，从而提高了其摩擦磨损性能． |
|
其他语种文摘
|
Optimum amount of rare earths （RE） for treating carbon fiber surface and effects of different surface treatments of carbon fiber on tribological behavior of Polytetrafluoroethylene （PTFE） composites under dry friction condition were investigated. Worn surfaces were observed and analyzed by scanning electron microscope （SEM）. Experimental results showed that the best tribological behavior of the CF/PTFE composites was obtained when the content of rare earth elements was 0.3wt%. Under dry friction condition, PTFE composites filled with surface treated carbon fibers exhibited better tribological performance than those of the PTFE composite filled with untreated carbon fibers did. Rare earth elements acting as surface modifier of the carbon fibers can increase interfacial adhesion and toughness between carbon fibers and PTFE matrix, and it improved tribological performance of the composites. |
|
来源
|
摩擦学学报
,2006,26(2):135-139 【核心库】
|
|
关键词
|
聚四氟乙烯复合材料
;
炭纤维
;
稀土
;
表面处理
;
摩擦磨损性能
|
|
地址
|
上海交通大学机械与动力工程学院, 上海, 200030
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-0595 |
|
学科
|
金属学与金属工艺;机械、仪表工业 |
|
基金
|
国家自然科学基金资助项目
|
|
文献收藏号
|
CSCD:2346845
|
参考文献 共
13
共1页
|
|
1.
Zhang Z Z. Tribological properties of metal-plastic multilayer composites under oil lubricated conditions[J].
Wear,1997,210(122):195-203
|
被引
9
次
|
|
|
|
|
2.
阎逢元. 铜包石墨填充PTFE基复合材料摩擦学特性的研究.
摩擦学学报,1999,19(1):7-11
|
被引
12
次
|
|
|
|
|
3.
Li F. The tribological behaviors of copper-coated graphite filled PTFE composites[J].
Wear,2000,237(1):33-38
|
被引
17
次
|
|
|
|
|
4.
唐炜. 液晶微纤原位增强PTFE复合材料抗磨性能与磨损机理.
摩擦学学报,2000,20(1):10-13
|
被引
15
次
|
|
|
|
|
5.
施凯. 短切炭纤维表面改性及其增强聚四氟乙烯复合材料性能的研究.
新型炭材料,1999,14(1):26-31
|
被引
10
次
|
|
|
|
|
6.
贾均红. 炭纤维增强聚四氟乙烯复合材料在干摩擦和水润滑条件下的摩擦学行为对比研究.
摩擦学学报,2004,24(1):16-20
|
被引
14
次
|
|
|
|
|
7.
Lee J S. Changes in physico-chemical and morphological properties of carbon fiber by surface treatment[J].
Carbon,1997,35(2):209-216
|
被引
7
次
|
|
|
|
|
8.
Ko K R. Effect of ozone treatment on Cr(VI) and Cu(II) adsorption behaviors of activated carbon fibers[J].
Carbon,2004,42(8/9):1864-1867
|
被引
1
次
|
|
|
|
|
9.
Park S J. Effect of silane surface treatment on interfacial adhesion of silica/rubber composites[J].
Polymer-Korea,2002,26(4):445-451
|
被引
1
次
|
|
|
|
|
10.
Xue Y J. Tensile properties of glass fiber reinforced PTFE using a rare-earth surface modifier[J].
Journal of Materials Science Letters,2001,20(18):1729-1731
|
被引
5
次
|
|
|
|
|
11.
薛玉君. 稀土处理玻璃纤维填充聚四氯乙烯复合材料在油润滑下的磨擦学性能.
摩擦学学报,2002,22(2):107-111
|
被引
7
次
|
|
|
|
|
12.
程先华. 稀土改性玻璃纤维对PTFE复合材料摩擦摩损性能的影响.
无机材料学报,2002,17(6):1321-1326
|
被引
9
次
|
|
|
|
|
13.
王荣国. 复合材料概论[M].
复合材料概论,1999
|
被引
28
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问