有机-无机复合CdS纳米晶的制备及表征
Preparation and Characterization of CdS Nanocrystals
查看参考文献14篇
|
文摘
|
本文采用液液两相法，在甲苯、甲醇和水两相体系中制备了烷基硫醇和芳杂环硫醇修饰的有机-无机复合的CdS半导体纳米晶。通过紫外可见吸收光谱、X-射线光电子能谱、X-射线粉末衍射、透射电子显微镜、元素分析和热重分析检测手段对样品的结构和组成进行了表征。结果表明：该方法所制备的硫化镉纳米晶是由无机纳米核及通过化学键吸附在其表面的硫醇分子所组成。纳米晶的平均粒径约为5nm，尺寸均匀，稳定性高，在空气中可长时间保存。 |
|
其他语种文摘
|
Inorganic-organic composite CdS nanocrystals covered with thiols were chemically synthesized in a two-phase system including toluene, methanol and distilled water by a new liquid-liquid two-phase method. The structure and composition were investigated with UV-Vis absorption spectra, XPS, XRD, TEM, EA and TGA. The results show these as-prepared samples consist of a nano-CdS core and a layer of thiols chemically absorbed on the surface, and they can be stored for a long time in air atmosphere. The average diameter of CdS nanocrystals was about 5nm and the size distribution was narrow. |
|
来源
|
材料科学与工程学报
,2005,23(6):891-894,901 【核心库】
|
|
关键词
|
液液两相法
;
有机-无机复合结构
;
硫化镉纳米晶
|
|
地址
|
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 甘肃, 兰州, 730000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1673-2812 |
|
学科
|
一般工业技术 |
|
基金
|
中国科学院“百人计划”项目
|
|
文献收藏号
|
CSCD:2180487
|
参考文献 共
14
共1页
|
|
1.
Zhang Li-De. Nanomaterials[M].
Nanomaterials,2000:11
|
被引
1
次
|
|
|
|
|
2.
Henglein A. physicochemical properties of extremely small colloidal metal and semiconductor particles [J].
Chem. Rev,1989,89:1861-1873
|
被引
100
次
|
|
|
|
|
3.
V.I. Klimov. I.
Science,2000,290:314-317
|
被引
129
次
|
|
|
|
|
4.
Warren C. W.
Science,1998,281:2016-2018
|
被引
128
次
|
|
|
|
|
5.
A. Rogach. Rogach.
Adv. Mater,2000,12:333-337
|
被引
22
次
|
|
|
|
|
6.
Frank Caruso. Caruso.
Science,1998,282:1111-1114
|
被引
226
次
|
|
|
|
|
7.
R.J. Bandaranayake. J.
Appl. Phys. Lett,1995,67:831-833
|
被引
7
次
|
|
|
|
|
8.
Wang L W. W.
J. Phys. Chem. B,1998,102:6449-6454
|
被引
4
次
|
|
|
|
|
9.
姚建曦. 聚乙烯吡咯烷酮硫脲修饰CdS纳米粒子制备.
无机材料学报,2003,18(2):445-450
|
被引
6
次
|
|
|
|
|
10.
吴伟平. 气-液反应反胶束法制备CdS纳米颗粒[J].
无机材料学报,2003,18(4):937-941
|
被引
1
次
|
|
|
|
|
11.
Yan Li. Preparation of Cadmium Sulfide Nanowire Arrays in Anodic Aluminum Oxide Templates [J].
Chem. Mater,1999,11:3433-3435
|
被引
2
次
|
|
|
|
|
12.
Edward J D. D.
Materials Research Bulletin,1998,33(2):323-329
|
被引
1
次
|
|
|
|
|
13.
Murray C B. B.
J. Am. Chem. Soc,1993,115:8706-8715
|
被引
351
次
|
|
|
|
|
14.
Ying Wang. materials synthesis.
J. Phys .Chem,1997,95(2):525-532
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问