表面修饰In纳米微粒的声化学法制备及结构表征
Preparation and Characteration of Surface Modified Indium Nanoparticles by Sonochemistry
查看参考文献18篇
|
文摘
|
金属纳米微粒由于具有不同于普通材料的光、电、磁、热力学和化学反应等性能,在催化、信息存储、光电、微电子以及润滑等领域中有着广阔的应用前景.金属纳米微粒这些特殊的物理化学性能主要取决于制备工艺和具体的反应条件,因此研究具有特定性能的金属纳米微粒一直是纳米技术领域中的一个研究热点[1,2].目前制备金属纳米微粒的方法主要有化学还原法[3,4]、金属气相沉积法[5]、电化学合成法[6]、热分解法[7]和微波法[8]等.…… |
|
其他语种文摘
|
Surface modified indium nanoparticles were prepared by a simple and rapid process from bulk indium via ultrasound dispersion. The morphology and structure of synthesized nanoparticles were characterized by TEM, XRD, XPS and FTIR. The results show that the morphology of indium nanoparticles is spherical and the structure of indium nanoparticles is the tetragonal phase. The surface of indium nanoparticles was coated by 2 ethyl hexanoic acid, which could almost hold back oxidation of the indium nanoparticles. In addition, the tribological property of indium nanoparticles as additives in oil was evaluated on a four-ball tester and the results show that indium nanoparticles exhibit good performance in wear. |
|
来源
|
无机化学学报
,2005,21(8):1261-1264 【核心库】
|
|
关键词
|
In纳米微粒
;
声化学
;
制备
;
摩擦学
|
|
地址
|
1.
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 甘肃, 兰州
2.
河南大学, 河南省特种功能材料重点实验室, 河南, 开封, 475001
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4861 |
|
学科
|
化学 |
|
基金
|
国家863计划
;
河南省科技攻关项目
|
|
文献收藏号
|
CSCD:2104978
|
参考文献 共
18
共1页
|
|
1.
Sun Y G. Science.
Science,2002,298:2176-2179
|
被引
151
次
|
|
|
|
|
2.
Puntes V F. Science.
Science,2001,291:2115-2117
|
被引
101
次
|
|
|
|
|
3.
Tan Y. Mater.
Mater. Chem,2003,13:1069-1075
|
被引
1
次
|
|
|
|
|
4.
Turkevich J. Science.
Science,1970,169:873-879
|
被引
11
次
|
|
|
|
|
5.
Klabunde K J. Chem.
Chem. Mater,1991,3:30-39
|
被引
1
次
|
|
|
|
|
6.
Reetz M T. Am.
Am. Chem. Soc,1994,116:7401-7402
|
被引
25
次
|
|
|
|
|
7.
Tano T. Colloid Interface Sci.
Colloid Interface Sci,1989,133:530-534
|
被引
5
次
|
|
|
|
|
8.
Chem W X. Chem.
Chem. Commun,2002:2588-2589
|
被引
1
次
|
|
|
|
|
9.
Su C H. J.
J. Phys. Chem. B,2003,107:14240-14243
|
被引
4
次
|
|
|
|
|
10.
Fujimoto T. Chem.
Chem. Mater,2001,13:1057-1060
|
被引
4
次
|
|
|
|
|
11.
Chen W. Ultrason.
Ultrason. Sonochem,2001,8:335-339
|
被引
2
次
|
|
|
|
|
12.
Suslick K S. J.
J. Phys. Chem,1993,97:3098-3099
|
被引
1
次
|
|
|
|
|
13.
Koltypin Y. Chem.
Chem. Mater,1999,11:1331-1335
|
被引
4
次
|
|
|
|
|
14.
Li Q L. New J.
New J. Chem,2003,27:1194-1199
|
被引
3
次
|
|
|
|
|
15.
Zhao Y B. J.
J. Am. Chem. Soc,2004,126:6854-6855
|
被引
5
次
|
|
|
|
|
16.
Zhao Y B. J.
J. Phys. Chem. B,2003,107:7574-7576
|
被引
9
次
|
|
|
|
|
17.
Zhao Y B. Mater.
Mater. Lett,2004,58:790-793
|
被引
4
次
|
|
|
|
|
18.
Zhao Y B. Mater.
Mater. Science Engineering A,2003,359:405-407
|
被引
5
次
|
|
|
|
|
了解气象卫星更多信息，请访问