TiC/NiCrMoAlTi金属陶瓷的微观结构与力学性能
Microstructures and mechanical properties of TiC/NiCrMoAlTi cermets
查看参考文献18篇
文摘
|
采用粉末冶金真空烧结方法制备了TiC/NiCrMoAlTi金属陶瓷.研究了Mo含量对TiC/NiCrAlTi金属陶瓷的微观结构与力学性能的影响.结果表明,在TiC/NiCrAlTi金属陶瓷中添加Mo后,在金属陶瓷的硬质相颗粒周围出现了典型的环形相,随着Mo含量的增加,环形相增多变厚,致使金属陶瓷的硬度线性增加,环形相的生成使金属陶瓷硬质相的颗粒细化、尖角钝化,从而提高了金属陶瓷的抗弯强度,当环形相过度发达时由于其本身较脆,金属陶瓷的抗弯强度降低,Mo含量为4%(质量分数)时抗弯强度达到最大值. |
其他语种文摘
|
TiC/NiCrMoAITi cermets were vacuum sintered by powder metallurgy technology. The effects of Mo additions on microstructures and mechanical properties of TiC/NiCrAITi cermets were investigated. Results show that the formation of surrounding phase around TiC particles refined the hard phase particles and blunted the sharp angles of TiC particles; With increasing Mo additions, both the amount and size of surrounding phase increased, thus the hardness increased linearly however the bonding strength increased to the maximum values at 4% Mo content and then decreased due to the brittle thick surrounding phase. |
来源
|
材料研究学报
,2005,19(4):354-360 【核心库】
|
关键词
|
复合材料
;
TiC/NiCrMoAlTi金属陶瓷
;
微观结构
;
力学性能
|
地址
|
1.
中国科学院金属研究所, 辽宁
2.
沈阳市工程质量监督站, 辽宁
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
1005-3093 |
学科
|
一般工业技术 |
文献收藏号
|
CSCD:2027148
|
参考文献 共
18
共1页
|
1.
P Ettmayer. Powder Metallurgy International.
Powder Metallurgy International,1989,21(2):37
|
被引
34
次
|
|
|
|
2.
P Ettmayer.
Metall,1989,43(8):742
|
被引
2
次
|
|
|
|
3.
P Ettmayer. Dreyer.
J. Refractory Metals & Hard Materials,1995,13:343
|
被引
75
次
|
|
|
|
4.
钱中良.
材料导报,1996,5:8
|
被引
1
次
|
|
|
|
5.
关德慧. 金属陶瓷复合塑料切粒刀的研制及应用.
粉末冶金技术,1998,16(1):36
|
被引
7
次
|
|
|
|
6.
Sam Zhang. Key Engineering Materials.
Key Engineering Materials,1998,521:138-140
|
被引
2
次
|
|
|
|
7.
朱丽娟.
材料工程,2001,6:10
|
被引
1
次
|
|
|
|
8.
LIU Yue. Journal of Materials Science Letters.
Journal of Materials Science Letters,2001,20:619
|
被引
3
次
|
|
|
|
9.
Iyori. Cermet Alloys and Composite Mechanical Parts Made by Employing Them.
Cermet Alloys and Composite Mechanical Parts Made by Employing Them,US Patent #4, 983, 212, Jan. 8,1991
|
被引
1
次
|
|
|
|
10.
张伟. 稀有金属与硬质合金.
稀有金属与硬质合金,1997,55:129
|
被引
2
次
|
|
|
|
11.
M Humenik. Amer.
J. Amer. Ceram. Soc,1956,39(2):60
|
被引
7
次
|
|
|
|
12.
N M Parikh. Amer.
J. Amer. Ceram. Soc,1957,40(9):315
|
被引
8
次
|
|
|
|
13.
D Moskowitz. in P/M.
Modern Dev. in P/M,1996:83
|
被引
1
次
|
|
|
|
14.
E Rudy. Less-Common Met.
J. Less-Common Met.,1973,33:43
|
被引
1
次
|
|
|
|
15.
H Suzuki. Jpn.
J. Jpn. Inst. Metals,1971,35:146
|
被引
2
次
|
|
|
|
16.
Jun-Kui Yang.
Materials Science and Engineering A,1996,213:209
|
被引
1
次
|
|
|
|
17.
刘宁.
硬质合金,1992,9(3):166
|
被引
3
次
|
|
|
|
18.
李晨辉. 复合材料学报.
复合材料学报,2003,1:20
|
被引
1
次
|
|
|
|
|