Ag对β-NiAl高温氧化膜Al2O3形貌的影响
EFFECT OF SILVER ADDITION ON SURFACE MORPHOLOGY OF Al2O3 SCALES DURING OXIDATION OF β-NiAl
查看参考文献21篇
|
文摘
|
利用TGA,SEM/EDS研究了Ag含量对β-NiAl合金高温氧化时生成Al2O3膜表面形貌的影响及添加1%Ag(原子分数)对1000℃氧化动力学的影响.结果表明,β-NiAl合金的氧化动力学由两段抛物线组成,分别受亚稳Al2O3和稳态α-Al2O3的生长控制.NiAl-1Ag合金的氧化动力学由三段抛物线组成,分别受γ-Al2O3,θ-Al2O3和α-Al2O3的生长控制.1000℃时,向β-NiAl中添加少量的Ag(＜1%)可以促进亚稳Al2O3向稳态α-Al2O3的转变.当添加量超过5%时,促进作用不明显.1100℃时,添加0.5%Ag对Al2O3的相变无明显的促进作用. |
|
其他语种文摘
|
The effect of adding small amounts of Ag (0.5%, 1%, 5% and 10%, atomic fraction) to /3-NiAl on surface morphology of alumina scale during the oxidation at 1000-1100 'C and the oxidation kinetics of /3-NiAl and NiAl-lAg were investigated by TGA and SEM/EDS. The kinetics of /3-NiAl presents two parabolic stages controlled by the growth of metastable alumina and stable a-Al2O3, respectively, while the kinetics of NiAl-lAg is composed of three different parabolic stages controlled by the growth of 7-AI2O3, 0-Al2O3 and a-Al2O3) respectively. The addition of small amounts of Ag (<1%) to /3-NiAl favors the phase transformation from metastable alumina to a-Al2O3, while this effect disappears for an Ag content above 5% at 1000 "C oxidation. Finally, the addition of 0.5% Ag to /3-NiAl does not affect the surface morphology of AI2O3 at 1100 'C. |
|
来源
|
金属学报
,2005,41(4):369-374 【核心库】
|
|
关键词
|
β-NiAl
;
Ag
;
高温氧化
;
Al2O3相变
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金资助项目
|
|
文献收藏号
|
CSCD:2024334
|
参考文献 共
21
共2页
|
|
1.
Zhou J. Mater Sci Eng.
Mater Sci Eng. A,2003,339:166
|
被引
3
次
|
|
|
|
|
2.
Rybicki G C. Oxid Met.
Oxid Met,1989,31:275
|
被引
31
次
|
|
|
|
|
3.
Doychak J. Metall Trans.
Metall Trans. A,1989,20:499
|
被引
16
次
|
|
|
|
|
4.
Mosely P T. Corros Sci.
Corros Sci,1984,24:547
|
被引
2
次
|
|
|
|
|
5.
Doychak J. Oxid Met.
Oxid Met,1989,31:431
|
被引
10
次
|
|
|
|
|
6.
Hagel W C. Corrosion.
Corrosion,1965,21:316
|
被引
5
次
|
|
|
|
|
7.
Wood G C. Corros Sci.
Corros Sci,1970,10:471
|
被引
1
次
|
|
|
|
|
8.
Wood G C. Oxid Met.
Oxid Met,1970,2:373
|
被引
1
次
|
|
|
|
|
9.
Smialek J L. Metall Trans.
Metall Trans. A,1983,10:2143
|
被引
1
次
|
|
|
|
|
10.
Brumm M W. Corros Sci.
Corros Sci,1992,33:1677
|
被引
29
次
|
|
|
|
|
11.
Brumm M W. Corros Sci.
Corros Sci,1993,34:547
|
被引
10
次
|
|
|
|
|
12.
Brumm M W. Corros Sci.
Corros Sci,1994,36:37
|
被引
2
次
|
|
|
|
|
13.
Grabke H J. Oxid Met.
Oxid Met,1995,44:147
|
被引
4
次
|
|
|
|
|
14.
Grabke H J. Appl Surf Sci.
Appl Surf Sci,1997,47:243
|
被引
1
次
|
|
|
|
|
15.
Grabke H J. Mater Corros.
Mater Corros,1996,47:675
|
被引
5
次
|
|
|
|
|
16.
Pint B A. Oxid Met.
Oxid Met,1997,47:1
|
被引
25
次
|
|
|
|
|
17.
Yang S L. Mater Sci Forum.
Mater Sci Forum,2001,369/372:361
|
被引
1
次
|
|
|
|
|
18.
Li M J. Oxid Met.
Oxid Met,2003,59:483
|
被引
2
次
|
|
|
|
|
19.
李猛进. Pd-Ni-Al涂层的高温长期氧化行为.
金属学报,2003,39:755
|
被引
4
次
|
|
|
|
|
20.
Zhang X J. High Temp Mater Proc.
High Temp Mater Proc（in press）
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问