高温长期时效对镍基单晶高温合金γ′相形貌的影响
The Effect of Long Aging Time at High Temperature on the Structure Evolution of γ′ Phase for a Nickel Base Single Crystalline Superalloy
查看参考文献9篇
|
文摘
|
研究了长期时效对一种镍基单晶高温合金γ′相形貌的影响.结果表明:合金在950℃时效100h后,γ′相正方度略有下降,500h后γ′相开始沿不同的[100]方向长大.合金在1 050℃时效100h后,γ′相开始沿不同的[100]方向长大,长大速度明显高于950℃时效.γ/γ′相界面能和弹性应变能的降低是γ′相长大的驱动力,γ′相按 Ostwald熟化方式长大,即大的γ′相长大,小的γ′相溶解,高温长期时效过程中无有害相析出,表明合金的组织是稳定的. |
|
其他语种文摘
|
The effect of long time aging treatment on the structural evolution of f' phase was investigated. The results showed that the squareness of y' phase is slightly reduced when aged at 950°Cfor 100 hours, then l' began to grow in the direction of [100] after aging for 500 hours. Whereas the V began to grow in the direction of [100] at 1 050°C for only 100 hours. The growth rate is faster for the latter case. The interfacial energy of ill' phases and the reduction of elastic strain energy is the driven force for l' phase's growth. The 7' phase grows according to Ostwald ripe mode, i. e. the larger l' phase continuously grows while the smaller l' phase dissolved into the larger one. No deleterious phase was detected during long time aging at high temperature, which indicated the stability of the micros tructure of the alloy. |
|
来源
|
机械工程材料
,2004,28(3):10-12,15 【核心库】
|
|
关键词
|
单晶合金
;
时效
;
γ′相
|
|
地址
|
中国科学院金属研究所, 辽宁, 沈阳, 110015
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1000-3738 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:1857587
|
参考文献 共
9
共1页
|
|
1.
Tawancy H M. The Microstructure thermal stability of a nickel-base superalloy[J].
J Maer Sci,1983,18:2976
|
被引
5
次
|
|
|
|
|
2.
Lai G Y. An investigation of the thermal stability of a cummercial Ni-Cr-Fe-Mo alloy (Hastelloy alloyx)[J].
Metall Trans A,1978,9:827
|
被引
5
次
|
|
|
|
|
3.
王淑荷. GH903高温合金650℃长期时效后的组织与性能.
金属学报,1990,26(6):A432
|
被引
4
次
|
|
|
|
|
4.
姜文辉. DZ40M钴基高温合金950℃长期时效后的组织与性能.
金属学报,1998,35(12):1289
|
被引
9
次
|
|
|
|
|
5.
Khachzturyan A G. SciTheoretical analysis of strain-induced shape changes in cubic precipitates during coarsening[J].
Acat Metal,1988,36:1563
|
被引
2
次
|
|
|
|
|
6.
Mulier L. Modelling thermal misfit stresses in nickel-base superalloys containing high volume fraction[J].
Actarmetall Mater,1992,40(6):1321
|
被引
6
次
|
|
|
|
|
7.
Glatzedl U. Calculations of internal stresses in the γ/γ′ microstructure of a nickel-base superalloy with high fraction of γ′ phase[J].
Scripta Metallurgica,1989,23:1839
|
被引
14
次
|
|
|
|
|
8.
任英磊. 热处理制度对一种单晶镍基高温合金γ′相形貌演化的影响.
机械工程材料,2001,25(4):7
|
被引
11
次
|
|
|
|
|
9.
田素贵.
单晶镍基合金组织演化与蠕变行为及微观特征的研究,1998:24
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问